Master's Dissertation
DOI
10.11606/D.25.2010.tde-17082010-154424
Document
Author
Full name
Cintia Lumi Nishida
Institute/School/College
Knowledge Area
Date of Defense
Published
Bauru, 2010
Supervisor
Committee
Rubo, Jose Henrique (President)
Oliveira, Pedro Cesar Garcia de
Silva, Renato Oliveira Ferreira da
Title in Portuguese
Análise da rugosidade superficial de diferentes marcas comerciais de resina acrílica para coroas provisórias
Keywords in Portuguese
Coroas provisórias
Polimento de superfície
Resinas acrílicas
Rugosidade de superfície
Abstract in Portuguese
As coroas provisórias apresentam algumas características que podem comprometer a estética e facilitar aderência de microorganismos e formação de placa. Estudos prévios demonstraram que a forma de processamento influi na rugosidade e porosidade de uma marca comercial de resina acrílica comumente utilizada para a confecção de provisórias. Como diferentes marcas comerciais apresentam diferenças de qualidade, o presente estudo teve como objetivo principal avaliar a rugosidade superficial de quatro marcas comerciais de resina acrílica utilizadas na confecção de coroas provisórias (Dencor, Vipi, Duralay e Alike) de acordo com quatro técnicas de manipulação, diretas e indiretas. Os processamentos avaliados foram: GRUPO I autopolimerização sob pressão em matriz de silicona; GRUPO II - autopolimerização térmica em mufla; GRUPO III autopolimerização utilizando a técnica do pincel; GRUPO IV autopolimerização pela mistura em pote dappen. Para cada tipo de processamento foram confeccionados 12 corpos-deprova de cada material, totalizando 48 corpos-de-prova para cada grupo e 192 espécimes ao total. Logo após a confecção dos espécimes foi realizado o teste de rugosidade de superfície (Ra) através de um rugosímetro/perfilômetro. Posteriormente, a superfície dos mesmos foi uniformizada e polida com a utilização de politriz, realizando-se novamente os mesmos testes de rugosidade. Antes do acabamento e polimento de superfície, os resultados encontrados apontaram a maior rugosidade para resina Vipi (4,074 ± 0,541) e técnica da mistura em dappen gupo IV (3,538 ± 0,509), enquanto que a menor rugosidade foi encontrada para resina Alike (2,671 ± 0,512) e técnica da prensagem em mufla grupo II (2,733 ± 0,470). Após acabamento e polimento, a maior rugosidade foi encontrada para resina Vipi (0,207 ± 0,032) e técnica da pressão grupo I (0,172 ± 0,037), enquanto que a menor rugosidade para resina Alike (0,113 ± 0,036) e técnica da prensagem em mufla grupo II (0,138 ± 0,027). Com os resultados obtidos, foi possível concluir que a melhor combinação para confecção de coroas provisórias em resina acrílica foi a técnica da prensagem em mufla associada à resina Alike.
Title in English
Surface roughness analysis of acrylic resin for provisional crowns under different commercial brands
Keywords in English
Acrylic resins
Provisional crowns
Surface polishing
Surface roughness
Abstract in English
Provisional crowns have some features that may compromise aesthetics and favors adherence of microorganisms and dental plaque formation. Previous studies have shown that processing may influence roughness and porosity of acrylic resins commonly used make provisional crowns. Because the several commercial resins available present differences in their quality the aim of this study was to evaluate the surface roughness of four commercial brands of acrylic resins (Dencor, Vipi, Duralay and Alike) according to four manipulation techniques (two direct and two indirect): GROUP I - autopolimerization under pressure in a silicone matrix; GROUP II autppolimerization in flask; GROUP III - autopolimerization using the bead brush technique; GROUP IV - autopolimerization after mixing in dappen dish. For each type of processing 12 specimens were made of each material, being 48 specimens for each group and 192 specimens in total. After specimens preparation, surface roughness tests (Ra) was performed using a rugosimeter / profilometer. Posteriorly, all surfaces were polished for standardization and same roughness tests were performed again. Before finishing and polishing, the results pointed out that Vipi resin presented the highest roughness (4.074 ± 0.541). Mixing the resin in dappen dish group IV (3.538 ± 0.509) also presented the highest roughness values regarding the technique. The lowest roughness values were found with Alike resin (2.671 ± 0.512) and flask technique group II (2.733 ± 0.470). After finishing and polishing techniques, the highest roughness was found with Vipi resin (0.207 ± 0.032) and the autopolimetization under pressure in silicone matrix technique - group I (0.172 ± 0.037). The lowest roughness values were found with Alike resin (0.113 ± 0.036) and flask technique group II (0.138 ± 0.027). With these results, it was possible to conclude that the best combination for making provisional crowns was the flask technique associated with Alike resin.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
CintiaLumiNishida.pdf (2.07 Mbytes)
Publishing Date
2010-08-19
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.