Mémoire de Maîtrise
DOI
10.11606/D.25.2000.tde-14032005-150441
Document
Auteur
Nom complet
Daniela Castilio
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2000
Directeur
Jury
Bonachela, Wellington Cardoso (Président)
Araujo, Carlos dos Reis Pereira de
Pinto, Joao Henrique Nogueira
Titre en portugais
Avaliação da Adaptação da Interface Intermediários/Cilindros de Plástico Fundidos em Titânio e Cobalto-Cromo, Antes e Após Soldagem a Laser.
Mots-clés en portugais
Laser
Soldagem odontológica
Titanio
Resumé en portugais
A condição passiva da adaptação das próteses implanto-suportadas é um requisito básico para o sucesso do tratamento. O objetivo deste estudo foi avaliar a adaptação da interface intermediário/componentes protéticos (cilindros), fundidos, em titânio e cobalto-cromo, em monobloco e após a realização da soldagem a laser. Foram utilizados 30 cilindros torneados em plástico e 15 barras cilíndricas para a interligação dos componentes protéticos (cilindros). Cada corpo de prova apresentava três componentes protéticos unidos entre si. Um total de 10 corpos de prova foram realizados, sendo que destes, 5 foram fundidos em titânio e os outros 5 fundidos em liga de cobalto-cromo. As análises e mensurações das interfaces foram feitas antes e após a soldagem a laser, com a utilização de um microscópio comparador. Os resultados mostraram que as estruturas fundidas em monobloco (peça única) apresentaram uma maior interface (desajuste médio de 26,164µm) que as mesmas após a soldagem a laser (desajuste médio de 19,943µm). Foram encontradas diferenças estatisticamente significantes também entre os dois materiais utilizados, sendo que o titânio (desajuste médio de 21,262µm) apresentou melhores resultados que o cobalto-cromo (desajuste médio de 24,845µm).
Resumé en anglais
The passivity of adaptation for prostheses supported by osseointegrated implants is basic requirement for the long-term sucess of the treatment. The purpose of this study was to evaluate the adaptation of the abutment to titanium or cobalt-chromium one-piece castings before and after laser welding. A total of 30 cylinders machined plastic and 15 cylinders bars were inserted to joint the prosthetics componentes. Each specimen, had three prosthetics components joined. A total of 10 specimens wewr obtained 5 casted with titanium and 5 with cobalt-chromium alloy. The measurements of interfaces were made after and before laser welding with a comparative microscope. The results showed the greatest interface (26,164µm) of the one-piece castings compared to the laser welding specimens (19,943µm). Titanium castings showed best results statistically significant when compared to the cobalt-chromium specimens.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
danielacastilio.pdf (8.33 Mbytes)
Date de Publication
2005-04-04
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.