Disertación de Maestría
DOI
10.11606/D.25.2000.tde-14032005-150441
Documento
Autor
Nombre completo
Daniela Castilio
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2000
Director
Tribunal
Bonachela, Wellington Cardoso (Presidente)
Araujo, Carlos dos Reis Pereira de
Pinto, Joao Henrique Nogueira
Título en portugués
Avaliação da Adaptação da Interface Intermediários/Cilindros de Plástico Fundidos em Titânio e Cobalto-Cromo, Antes e Após Soldagem a Laser.
Palabras clave en portugués
Laser
Soldagem odontológica
Titanio
Resumen en portugués
A condição passiva da adaptação das próteses implanto-suportadas é um requisito básico para o sucesso do tratamento. O objetivo deste estudo foi avaliar a adaptação da interface intermediário/componentes protéticos (cilindros), fundidos, em titânio e cobalto-cromo, em monobloco e após a realização da soldagem a laser. Foram utilizados 30 cilindros torneados em plástico e 15 barras cilíndricas para a interligação dos componentes protéticos (cilindros). Cada corpo de prova apresentava três componentes protéticos unidos entre si. Um total de 10 corpos de prova foram realizados, sendo que destes, 5 foram fundidos em titânio e os outros 5 fundidos em liga de cobalto-cromo. As análises e mensurações das interfaces foram feitas antes e após a soldagem a laser, com a utilização de um microscópio comparador. Os resultados mostraram que as estruturas fundidas em monobloco (peça única) apresentaram uma maior interface (desajuste médio de 26,164µm) que as mesmas após a soldagem a laser (desajuste médio de 19,943µm). Foram encontradas diferenças estatisticamente significantes também entre os dois materiais utilizados, sendo que o titânio (desajuste médio de 21,262µm) apresentou melhores resultados que o cobalto-cromo (desajuste médio de 24,845µm).
Resumen en inglés
The passivity of adaptation for prostheses supported by osseointegrated implants is basic requirement for the long-term sucess of the treatment. The purpose of this study was to evaluate the adaptation of the abutment to titanium or cobalt-chromium one-piece castings before and after laser welding. A total of 30 cylinders machined plastic and 15 cylinders bars were inserted to joint the prosthetics componentes. Each specimen, had three prosthetics components joined. A total of 10 specimens wewr obtained 5 casted with titanium and 5 with cobalt-chromium alloy. The measurements of interfaces were made after and before laser welding with a comparative microscope. The results showed the greatest interface (26,164µm) of the one-piece castings compared to the laser welding specimens (19,943µm). Titanium castings showed best results statistically significant when compared to the cobalt-chromium specimens.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
danielacastilio.pdf (8.33 Mbytes)
Fecha de Publicación
2005-04-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.