Thèse de Doctorat
DOI
10.11606/T.25.2007.tde-09112007-111953
Document
Auteur
Nom complet
Paulo Fukashi Yamaguti
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2007
Directeur
Jury
Rubo, José Henrique (Président)
Ferreira, Paulo Martins
Francisconi, Paulo Afonso Silveira
Gennari Filho, Humberto
Silva, Eulália Maria Martins da
Titre en portugais
Análise da técnica de fundição rápida segundo a adaptação cervical de infra-estrutura de liga à base de Ni-Cr e expansões de presa e térmica de quatro revestimentos
Mots-clés en portugais
Adaptação marginal
Revestimento para fundição odontológica
Técnica de fundição odontológica
Resumé en portugais
Estudos recentes têm demonstrado que o aprimoramento dos revestimentos odontológicos para o uso da técnica de fundição rápida pode ser considerado uma realidade no seu uso diário no laboratório de prótese. Desta forma, obtêm-se peças metálicas fundidas em menor tempo, produz-se mais em pouco tempo e, diminuem-se os custos sem perda da qualidade. Mesmo assim, ainda há incógnitas sobre como estes revestimentos se expandem. Imagina-se que para obter a melhor adaptação cervical é necessária a maior expansão total do revestimento, mas alguns estudos têm demonstrado que outros fatores podem ser determinantes para obter a melhor adaptação cervical. O objetivo deste trabalho foi averiguar a adaptação cervical de infra-estruturas metálicas à base de Ni-Cr obtidas com quatro revestimentos odontológicos para a técnica de fundição rápida e analisar as expansões de presa e térmica dos mesmos. De cada revestimento foram obtidos 10 corpos de prova. Na análise da expansão de presa e térmica utilizou-se 3 corpos de prova de cada revestimento. Para a análise estatística, utilizou-se o ANOVA e o Teste de Tukey. Estas análises demonstraram que o uso do revestimento Heat Shock resultou na melhor adaptação cervical, seguido do Flash, Bellavest SH e Micro-Fine 1700. Na expansão de presa, no período de 15 minutos após a inclusão, nenhum dos revestimentos havia completado a sua total expansão. Na expansão térmica, dentro do forno no período de 20 minutos, todos os revestimentos apresentaram a expansão completada dentro de 15 minutos. Conclui-se que todos os revestimentos têm o potencial a oferecer peças fundidas com adaptação cervical adequada e que a obtenção da mesma não depende apenas da maior expansão total, mas também do comportamento da expansão de presa e da expansão térmica. Há também indícios de que a resistência à compressão do revestimento desempenha importância considerável.
Titre en anglais
Analysis of accelerated casting technique in accordance with marginal adaptation of Ni-Cr crown and curing expansion and thermal expansion of four investments
Mots-clés en anglais
Dental casting investments
Dental casting technique
Marginal Adaptation
Resumé en anglais
With the improvement of dental investments for accelerated casting technique, recent studies have demonstrated that the procedure can be considered safe for daily use in the dental laboratory. Thus, cast pieces can be obtained in less time, the prosthetic work as a whole can be speed up and costs are cut with no quality compromise. Even though, there are still unanswered questions on how investments expand. It is thought that to reach the best cervical adaptation the greatest investment total expansion is needed, but some studies have demonstrated that other factors can be determining. The aim of this study was to verify the cervical adaptation of nickelchromium crowns cast using four dental investments for the accelerated casting technique and to analyze the curing and thermal expansion of such investments. For each investment, ten samples were obtained. For thermal expansion analysis three samples of each investment were used. For statistical purposes ANOVA and Tukey tests were used. The use of Heat Shock yielded the best results of cervical adaptation, followed by Flash, Bellavest SH and Micro-Fine 1700. For thermal expansion, 15 minutes after investment, none of the investments had reached their complete expansion. After 20 minutes inside the oven all investments had completed their expansion. It was concluded that all investments tested are suitable to offer cast pieces with adequate cervical adaptation. Adaptation depends not only of the greatest total expansion, but also of the curing and thermal expansion. There are indications that investment compression strength plays an important role on the technique.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2007-11-09
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.