Disertación de Maestría
DOI
10.11606/D.25.2003.tde-06122004-100505
Documento
Autor
Nombre completo
Jefferson Ricardo Pereira
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2003
Director
Tribunal
Valle, Accacio Lins do (Presidente)
Bonachela, Wellington Cardoso
Silva Filho, Cicero Eleuterio da
Título en portugués
Influência do remanescente dentário coronal na avaliação de dentes tratados endodonticamente restaurados com pinos pré-fabricados e resina composta
Palabras clave en portugués
núcleos
pinos dentários
resinas compostas
resistência estrutural
Resumen en portugués
O objetivo deste trabalho foi analisar a influência da quantidade de remanescente dentário coronal sobre a resistência de dentes tratados endodonticamente. Para isto foram selecionados 60 caninos superiores humanos anatomicamente semelhantes, divididos em seis grupos de dez espécimes cada, sendo que o grupo I não recebeu pino intra-radicular, o grupo II foi restaurado com núcleos metálicos fundidos e os grupos 3, 4, 5 e 6 foram restaurados com pinos pré-fabricados intra-radiculares e resina composta com diferentes quantidades de remanescentes dentários coronais de 0, 1, 2 e 3mm, respectivamente. Após serem restaurados os dentes foram levados a Máquina de Ensaios Universal para os testes de compressão a 45º. A análise dos resultados (ANOVA, p>0,05) mostrou haver diferença statisticamente significativa entre os grupos. O teste de Tukey encontrou valores de resistência à fratura significativamente mais elevados para os núcleos fundidos, seguido dos pinos pré-fabricados sem remanescente coronal. Os outros grupos se apresentaram com valores inferiores muito próximos entre si, mostrando, desta forma que o remanescente dentário coronal influencia de maneira pouco significativa a resistência dos dentes tratados endodonticamente.
Palabras clave en inglés
composite
core
post
resistence
Resumen en inglés
The aim of this study was to analysed the influence the influence of coronal remainders amounts on the resistence of teeth endodontically treated. For that purpose, sixty anatomically similar upper human canines were selected and divided into six groups with ten specimens each, with the element of group 1 did not receive any post, group 2 restored with cast post and core, and groups 3, 4, 5, 6 with pre-fabricated post and composite core with different amount of coronal dental remainders of 0, 1, 2, 3mm, respectivally. After restoration the teeth were subjected to compression tests at 45º in the Universal Test Machine. The assessment of results (ANOVA) showed significant statistical difference amoung the groups. The Tukey test reveiled resistence to fracture values significantilly higher for the cast post and core, followed by the pre-fabricated post with no coronal remainders. The other groups presented lower values much closed amoung each other, thus, showing that the coronal remainders exerts little influence on the resistence of teeth endodontically treated.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2004-12-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.