Master's Dissertation
DOI
10.11606/D.25.2009.tde-29052009-094511
Document
Author
Full name
Juan Carlos Pontons Melo
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Bauru, 2009
Supervisor
Committee
Freitas, Cesar Antunes de (President)
Francisconi, Paulo Afonso Silveira
Sábio, Sérgio
Title in Portuguese
Avaliação do desgaste por escovação, in vitro, de uma resina composta, fotopolimerizada por lâmpada halógena, em dois diferentes tempos
Keywords in Portuguese
Abrasão
Desgaste
Escovação
Resina composta
Abstract in Portuguese
Um dos principais problemas dos materiais restauradores (incluindo a resina composta) é o desgaste por abrasão. Portanto, o objetivo neste trabalho foi avaliar in vitro o desgaste abrasivo por escovação da resina composta 4Seasons, de duas cores diferentes (A3 e C4) e com fotopolimerização por dois diferentes tempos (20 e 40 s), utilizando escova Sorriso, da Colgate, e creme dentifrício Colgate Tripla Ação; também foi usado, como material de referência, o polimetil metacrilato. Assim, foram confeccionados dez corpos-de-prova, para cada um dos cinco grupos formados (PMMA, A3 20s, A3 40s, C4 20s, C4 40s). Cada espécime consistia basicamente num cilindro de cerca de 1,8 mm de altura e 8 mm de diâmetro. Cada espécime, após sua confecção, era imerso em água deionizada, a 37 ± 2 ºC, por 24 horas, quando então eram regularizados com lixa (granulação # 600 e # 1.000); após lavagem com ultrassom, voltavam a ser armazenados nas mesmas condições, até completar-se um período de uma semana. A escovação foi então efetuada numa máquina própria, que comportava dez espécimes simultaneamente, sendo de 3 N a carga de cada escova sobre o respectivo espécime; a velocidade de cada escova era de 18 cm/s, com a freqüência (ida e volta, num percurso total de 4 cm) de 4,5 ciclos/s; o período de escovação de um espécime compreendia 150. 000 ciclos. Foram efetuados cinco períodos (ou lotes) de escovação, de modo que um espécime do material de cada grupo tivesse sido submetido à ação de cada uma das posições ocupadas pelas dez escovas. A quantidade de massa perdida, para cada espécime, foi calculada por meio de pesagem (pré e pós escovação), numa balança com acuidade de milionésimo de grama. O trabalho foi também ilustrado com gráficos de rugosidade e com fotomicrografias tomadas ao MEV. A taxa média de desgaste foi de 2,8 mg para o PMMA, de 5,5 mg para o A3-20s, 4,7 mg para o A3-40 s, 5,4 para o C4-20s e 4,2 mg para o C4-40s; a respectiva análise de variância mostrou não existir diferença significante entre os grupos, para p=0,166; o coeficiente de variação entre os grupos foi bastante semelhante. Foi possível concluir que não existiu diferença da resistência ao desgaste abrasivo entre os grupos estudados.
Title in English
In vitro toothbrushing wear evaluation of a resin composite cured by QTH curing unit in two different times
Keywords in English
Abrasion
Resin composite
Toothbrushing
Wear
Wear resistance
Abstract in English
One of the main problems of dental restorative materials (including the resin composites) is the abrasion wear. Therefore, the aim of this work was to evaluate in vitro the abrasive wear by toothbrushing of the resin composite 4Seasons, of two different colors (A3 and C4), cured by two different times (20 and 40 s), using a toothbrush (Sorriso - Colgate), and a dentifrice (Tripla Ação Colgate). Polimetil meth-acrylate was used as reference material. Ten cylindric samples (approximately 1.8 mm height and 8 mm diameter) had been prepared for each one of the five evaluated groups (PMMA, A3 20s, A3 40s, C4 20s, C4 40s). After confection, samples were immersed in deionized water, at 37 ± 2ºC, for 24 h, and then regularized by abrasive gritting with sandpaper (from #600 to # 1 000); after that, were cleaned in ultrasound bath, and restored to the same described conditions, until completing the period of one week. The toothbrushing was then conducted in a proper machine that holds 10 specimens simultaneously, with a 3 N load of each toothbrush on the respective sample. The speed of each toothbrush was of 18 cm/s, at a frequency of 4.5 cycles/s (each cycle consisting of 2 cm forward and 2 cm backward). 150. 000 cycles were applied per sample. Five periods (or lots) of toothbrushing had been performed, in a way that one sample of each group had been submitted to the brushing action at one position in the machine. The amount of weight loss for each sample was calculated by means of weighting (before and after toothbrushing), in an analytical balance with accuracy of millionth of gram. Roughness and MEV photomicrographies were also evaluated. The average rate of wear was of 2.8 mg for PMMA, 5.5 mg for A3-20s, 4.7 mg for A3-40 s, 5.4 for C4-20s, and 4,2 mg for C4-40s. One-way ANOVA showed no significant difference between groups (p = 0.166). The coefficient of variation between the groups was sufficiently similar. It was possible to conclude that difference of the resistance to the abrasive wear between the studied groups did not exist.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2009-06-02
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.