• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tesis Doctoral
DOI
10.11606/T.25.2007.tde-11102007-093822
Documento
Autor
Nombre completo
Anuradha Prakki
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2007
Director
Tribunal
Mondelli, Rafael Francisco Lia (Presidente)
Braga, Roberto Ruggiero
Francci, Carlos Eduardo
Goes, Mario Fernando de
Kalachandra, Sid
Título en portugués
Influência de aditivos nas propriedades de comonômeros, copolímeros e compósitos a base de Bis-GMA, diluído com TEGDMA ou análogos sintetizados do Bis-GMA (CH3Bis-GMA e CF3Bis-GMA)
Palabras clave en portugués
Aditivos
Análogos do Bis-GMA
Monômeros diluentes
Propriedades mecânicas
Resinas compostas
Resumen en portugués
O objetivo deste estudo foi avaliar a influência de dois aditivos, propionaldehyde (propanal aldeído) e 2,3-butanedione (diquetona diacetil), nas propriedades de comonômeros, copolímeros e resinas compostas à base de Bis-GMA, quando diluído com TEGDMA, Bis-GMA propoxilado (CH3Bis-GMA) e Bis-GMA propoxilado fluorinado (CF3Bis-GMA). Comonômeros, copolímeros e compósitos experimentais foram preparados combinando Bis-GMA com TEGDMA, CH3Bis-GMA, CF3Bis-GMA e, aldeído (24 e/ou 32 mol%) e diquetona (24 e/ou 32 mol%). No caso dos compósitos, partículas híbridas silanizadas (bário aluminosilicato; 60 peso%) foram adicionadas aos comonômeros. Para a fotopolimerização, adicionou-se canforoquinona (0,2 peso%) e N,N-dimetil-p-toluidina (0,2 peso%). Os comonômeros e copolímeros experimentais tiveram as seguintes propriedades avaliadas: viscosidade, contração de polimerização, grau de conversão, ângulo de contato (em esmalte, dentina e vidro), temperatura de transição vítrea (DSC e equação de Fox), microdureza, alteração de rugosidade superficial e desgaste por abrasão. Os compósitos experimentais, tiveram avaliadas as seguintes propriedades: resistência flexural, módulo de elasticidade, tração diametral, módulo de resiliência, microdureza, alteração de rugosidade superficial e desgaste por abrasão. Os sistemas Bis-GMA/TEGDMA e Bis-GMA/CH3Bis-GMA tiveram suas propriedades significantemente alteradas pela incorporação de aditivos (propanal ou diquetona). Os aditivos (propanal/diquetona) não influenciaram de forma significante as propriedades do sistema Bis-GMA/CF3Bis-GMA. O efeito dos aditivos nas propriedades dos materiais analisados relaciona-se à sua abilidade em aumentar o grau de conversão de alguns sistemas resinosos
Título en inglés
Influence of additives on the properties of comonomers, copolymers and composites based on Bis-GMA, diluted with TEGDMA or the synthesized Bis-GMA analogs (CH3Bis-GMA and CF3Bis-GMA)
Palabras clave en inglés
Additives
Bis-GMA analogs
Diluent monomers
Mechanical properties
Resin composites
Resumen en inglés
The purpose of this study was to evaluate the effect of two additives, propionaldehyde (aldehyde) and 2,3-butanedione (diketone), on the properties of Bis-GMA based comonomer, copolymer and composites when diluted with TEGDMA, propoxylated Bis- GMA (CH3Bis-GMA) and propoxylated fluorinated Bis-GMA (CF3Bis-GMA). Experimental comonomer/copolymer/composites were prepared combining Bis-GMA and TEGDMA, CH3Bis-GMA, CF3Bis-GMA, with aldehyde (24 and/or 32 mol%) and diketone (24 and/or 32 mol%). For composites, hybrid treated filler (barium aluminosilicate glass; 60 wt%) was added to monomer mixtures. Photopolymerization was effected by using camphorquinone (0.2 wt%) and N,N-dimethyl-p-toluidine (0.2 wt%). Experimental comonomer/copolymers viscosity, polymerization shrinkage, degree of conversion, contact angle (enamel, dentin and glass surfaces), glass transition temperature (DSC and Fox equation), microhardness, surface roughness changes and wear were evaluated. Experimental composites, flexural strength, modulus of elasticity, diametral tensile strength, modulus of resilience, microhardness, surface roughness changes and wear were also assessed. Bis-GMA/TEGDMA and Bis- GMA/CH3Bis-GMA systems had properties significantly influenced by incorporation of additives (either propanal or diketone). Additives (propanal/diketone) did not significantly influence on Bis-GMA/CF3Bis-GMA system properties. The effect of additives on the evaluated material properties is mainly attributed to their ability in improving some resin systems degree of conversion
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AnuradhaPrakki.pdf (16.11 Mbytes)
Fecha de Publicación
2007-10-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.