• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Thèse de Doctorat
DOI
10.11606/T.25.2002.tde-10012005-102846
Document
Auteur
Nom complet
Oscar Barreiros de Carvalho Júnior
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2002
Directeur
Jury
Freitas, Cesar Antunes de (Président)
Bonachela, Wellington Cardoso
Cruz, Carlos Alberto dos Santos
Francisconi, Paulo Afonso Silveira
Nunes, Osvaldo Benoni da Cunha
Titre en portugais
Avaliação 'in vitro' da dureza superficial, da contração de polimerização e da rugosidade de 29 resinas compostas
Mots-clés en portugais
polimerização
propriedades físico-químicas
resinas compostas
Resumé en portugais
Foram analisadas in vitro a dureza superficial, a contração de polimerização e a rugosidade de 29 resinas compostas. Foram confeccionados 3 corpos-de-prova para cada material, com fotopolimerização por 80 segundos; após mais 5 minutos, determinou-se a dureza superficial Rockwell 30T; os espécimes foram então armazenados em água desionizada, a 37ºC, durante 168 horas, quando nova leitura da dureza foi realizada. Para avaliação da contração de polimerização, foram confeccionados 5 corpos-deprova para cada material; cada resina era inserida em uma matriz metálica, com uma cavidade em forma de “meia cana”, cujas paredes das extremidades planas eram paralelas entre si, com fotopolimerização por 40 segundos; após 10 minutos, removia-se a amostra da matriz, cujo comprimento era medido para se estabelecer a contração inicial ocorrida; os espécimes eram então armazenados em estufa a 37ºC, durante 168 horas (1 semana), quando nova medida era tomada, para se determinar a contração final da resina. Os mesmos corpos-de-prova usados nos testes de dureza, após desgaste com lixas de papel até a de n.º 1.500, foram analisados num rugosímetro. Estatisticamente, todas as resinas mostraram aumento da dureza e da contração de polimerização, da medição imediata para a com 168 horas. Em termos globais, as que apresentaram os melhores resultados, analisando-se as três características simultaneamente, foram a Z-100 e a P-60, enquanto as com o pior desempenho foram a Solitaire e a Helioprogress.
Resumé en anglais
In vitro surface hardness, polimerization shrinkage and roughness of 29 composite resins were stablished. For each material, it were made 3 specimens, photocured by 80 seconds; 5 minutes later, Rockwell 30T surface hardness was determined; the specimens were then imersed in deionized water, at 37ºC by 168 hours, when a new evaluation of hardness was effectued. In evaluating polymerization shrinkage, 5 specimens were made for each material; each resin was inserted in a metallic matrix, in which there was a cavitiy with the shape of a hemi-cilinder, whose flat surfaces were paralel between itself, com photopolimerization for 40 seconds; 10 minutes later, the lenght was measured to determine the inicial shrinkage; specimes were then stored in a stove, at 37ºC for 168 hours, when a new length measuring was effectued to determine the final shrinkage. The same specimens used for hardness were abraded with sand paper (till 1,500 mesh) and evaluated for roughness with a rugosimeter. All resins showed an increase in hardness and in polymerization shrinkage, since the inicial evaluation to that effectued 168 hours later. In a global way, by a simultaneous analysis of the 3 characteristics, the best results were presented by Z-100 and P-60; Solitaire and Helioprogress had the worst performance.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2005-01-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.