Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.23.2016.tde-30092016-163902
Document
Auteur
Nom complet
Stephanie Soares Favero
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2016
Directeur
Jury
Cesar, Paulo Francisco (Président)
Genova, Luís Antonio
Sesma, Newton
 
Titre en portugais
Efeito do material no comportamento mecânico de laminados cerâmicos ultrafinos
Mots-clés en portugais
CAD-CAM
Cerâmicas odontológicas
Ciclagem mecânica
Dissilicato de lítio
Laminados ultrafinos
Porcelana
Resumé en portugais
Objetivos: (1) determinar a carga de fratura e o modo de falha de laminados cerâmicos ultrafinos processados via CAD-CAM em função da microestrutura do material (vitrocerâmica à base de dissilicato de lítio ou porcelana à base de leucita); (2) desenvolver metodologia de ciclagem mecânica para determinar o tempo de vida e o modo de falha de laminados cerâmicos ultrafinos processados via CADCAM. Materiais e métodos: dezesseis dentes humanos, incisivos centrais superiores, foram utilizados para confecção dos espécimes. Os dentes sofreram mínimo preparo, em esmalte, para adequada adaptação dos laminados cerâmicos ultrafinos. Os laminados de dissilicato de lítio e de porcelana foram confeccionados via CAD-CAM e cimentados com cimento resinoso sobre os dentes. Quatro espécimes de cada grupo foram levados à máquina de ensaios universal para determinação da carga de fratura dos laminados. Para o desenvolvimento de metodologia para determinação do tempo de vida dos laminados, uma série de testes piloto foi realizada, utilizando-se diferentes parâmetros como: tipo de antagonista (dentes naturais ou roletes metálicos), carga aplicada (20, 30 ou 40 N) e esquema de ciclo mastigatório (incisão ou deslizamento). Os padrões de falha dos laminados foram analisados em um estereomicroscópio, e os resultados obtidos no ensaio de carga de fratura foram analisados por ANOVA e teste de Tukey. Resultados: o valor médio obtido de carga de fratura para o dissilicato de lítio foi de 431,8 ± 217,9 N, enquanto que para a porcelana foi de 454,4 ± 72,1 N. Não houve diferença estatística entre os valores de carga de fratura encontrados, porém, o desvio padrão e o coeficiente de variação da vitrocerâmica foram muito superiores em relação aos da porcelana. Houve diferença no modo de falha dos materiais testados, sendo que a porcelana apresentou um maior número de falha por lascamento e o dissilicato de lítio apresentou maior quantidade de falha da estrutura dental. Na ciclagem mecânica, para cada condição testada, uma resposta diferente foi obtida. No tipo de ciclo incisão, os antagonistas (dente natural) fraturaram quando as cargas de 30 N e 40 N foram aplicadas. No tipo de ciclo deslizamento, o antagonista (dente natural) sofreu desgaste da borda incisal com carga de 30 N. Para o antagonista rolete metálico, quando a carga de 30 N foi aplicada ocorreu fratura do laminado, e quando aplicada a carga de 20 N, houve desgaste excessivo do rolete metálico. Conclusão: (1) o material utilizado não afetou a carga de fratura dos laminados cerâmicos ultrafinos quando o teste estático foi utilizado. Entretanto, o modo de falha foi significativamente diferente, sendo que a porcelana sofreu mais lascamentos do que o dissilicato de lítio; o qual, por sua vez, apresentou a maioria das falhas relacionadas à estrutura dental. (2) Não foi possível determinar uma combinação de parâmetros de ciclagem mecânica que permitisse a determinação dos parâmetros de fadiga para laminados cerâmicos ultrafinos, já que o número máximo de ciclos alcançados foi de 536.818 ciclos. Dessa forma, estudos futuros precisam ser realizados para que uma metodologia apropriada permita determinar parâmetros de fadiga clinicamente relevantes para laminados cerâmicos ultrafinos em dentes anteriores.
 
Titre en anglais
The effect of the material on the mechanical behaviour of the ultrathin ceramic laminates
Mots-clés en anglais
CAD-CAM, Lithium disilicate
Dental ceramics
Mechanical cycling
Porcelain
Ultrathin laminate
Resumé en anglais
Objectives: (1) to determine the fracture load and the failure mode of the ultra-thin ceramic laminates processed via CAD-CAM according to the microstructure of the material (lithium disilicate-based glass-ceramic or leucite-based porcelain); (2) to develop a fatigue methodology capable of determining the lifetime of ultra-thin ceramic laminates processed via CAD-CAM. Materials and methods: sixteen human maxillary central incisors were used to produce the specimens. The teeth required minimal preparation on the enamel for proper adaptation of the ultra-thin ceramic laminates. Ceramic laminates made of lithium disilicate and feldspathic porcelain with thicknesses between 0.3 mm to 0.5 mm were produced via CAD-CAM and cemented with resin cement. Four specimens of each group were taken to a universal testing machine to determine the fracture load of the laminates. For the development of a fatigue methodology, a series of pilot tests was performed using different parameters such as: type of antagonist (natural teeth or metal roller), applied load (20, 30 or 40 N), and type of masticatory cycle (incision or sliding). Failure modes were analysed using a stereomicroscope. Fracture load data were analysed by ANOVA and Tukey's test. Results: the mean fracture load obtained for the glass-ceramic was 431.8 ± 217.9 N, while that obtained for the porcelain was 454.4 ± 72.1 N. There was no statistical difference between the mean fracture load values; however, the standard deviation and the coefficient of the variation of the glass-ceramic were both higher than those obtained for the porcelain. There was also a difference in the failure modes for the two materials tested. The porcelain showed a higher number of factures due to chipping and the lithium disilicate showed a higher number of tooth structure failure. The fatigue experiment showed different results depending on the condition analysed. In the incision cycle, the antagonists (natural tooth) fractured when loads of 30 N and 40 N were applied. In the slide type of cycle, the antagonist (natural tooth) suffered wear on the incisal edge after applying 30 N of load. For the metal roller antagonist, when a 30 N load was applied, the ceramic laminate fractured, and when a 20 N load was applied, an excessive wear of the metal roller occurred. Conclusion: (1) The material used did not affect the fracture load of ultra-thin ceramic laminates when the static test was used. However, the failure mode was significantly different, as porcelain suffered more chipping than the lithium disilicate; which, in turn, showed most fails related to the tooth structure. (2) It was not possible to determine the combination of the mechanical cycling parameters that would allow the determination of fatigue parameters for ultra-thin ceramic laminates, since the maximum number of cycles reached was 536,818 cycles. In this way, future studies need to be carried out so that a clinically relevant methodology can be developed to determine the fatigue parameters of ultra-thin ceramic laminates in the anterior teeth.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-10-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs.
CeTI-SC/STI
© 2001-2024. Bibliothèque Numérique de Thèses et Mémoires de l'USP.