Tesis Doctoral
DOI
10.11606/T.23.2010.tde-22122010-114112
Documento
Autor
Nombre completo
Breno Mont'Alverne Haddade Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Rodrigues Filho, Leonardo Eloy (Presidente)
Alves, Claudia Maria Coêlho
Miranda Junior, Walter Gomes
Mondelli, Jose
Souza, Sérgio Moraes de
Título en portugués
Efeito do tratamento térmico sobre a sorção e solubilidade, tenacidade à fratura e grau de conversão de compósitos restauradores diretos
Palabras clave en portugués
Compósitos
Grau de Conversão
Sorção e Solubilidade
Tenacidade à Fratura
Tratamento Térmico
Resumen en portugués
O tratamento térmico em compósitos restauradores diretos foi realizado a fim de verificar a influência sobre algumas propriedades, tais como a sorção, solubilidade, tenacidade à fratura e grau de conversão. Foram utilizados três compósitos: um nanoparticulado, um microhíbrido e um microparticulado. Duas fontes de luz (Halógena e LED) e dois períodos (48h e 28dias) de armazenagem, com exceção da solubilidade. O tratamento térmico foi realizado em estufa convencional (170o C por 5min), sendo metade dos corpos de prova (cps) tratados e a outra, apenas fotoativada.Para sorção e solubilidade, foram confeccionados 60 cps de acordo com os fatores analisados (n=5) em uma matriz metálica circular de dimensões 15 mm x1 mm. Para o cálculo da sorção e solubilidade, os cps foram pesados em uma Balança Analítica,inicialmente após a confecção do cp, 1hora, 24h, 48h, 7d, 14, 21 e 28d, a fim de estabelecer Massa Inicial (Mi) Massa absorvida (Ma) e Massa dessecada (Md). Para a tenacidade à fratura, foram confeccionados 240 cps de acordo com os fatores analisados (n=10) em uma matriz metálica de dimensões internas 25 mm x 5mm x 2,8 mm. O método utilizado foi o Single Edge Notch-Beam(SENB), com um entalhe de 2,3 mm posicionado no centro da matriz. Os cps eram levados à máquina universal para o ensaio de flexão e, após a ruptura, as superfícies de fratura eram analisadas no estereomicroscópio, para, em seguida, obter as imagens e calcular as dimensões do cps para inserir naequação da tenacidade à fratura.Já para o grau de conversão foram confeccionados 36 cps em uma matriz de acetato circular de 15 mm x 1 mm, posicionados entre duas lâminas microscópicas (n=3). O cálculo do grau de conversão foi determinado por espectroscopia no infravermelho (FTIR).Em geral, os estudos apresentaram uma influência significante do tratamento térmico, Dos resultados para a sorção o compósito, em geral, diminuiu,comparado aos grupos somente fotoativados em ambos os períodos. Entre as interações analisadas (Fonte de Luz X Período) foi significante para todos os grupos. Para a solubilidade a interação (Fonte de luz X Tratamento térmico foi significante para todos os grupos. Quanto à tenacidade à fratura, apenas o fator tratamento foi significante para os compósitos nanoparticulado e microhíbrido. Já para os microparticulados, houve influência dos fatores principais e dasinterações(Fonte de Luz X Período) e Fonte de Luz X Tratamento Térmico). De maneira geral, houve um aumento dos valores de tenacidade para todos os grupos. Já para o grau de conversão, houve um aumento significativo com relação ao tratamento e os períodos analisados dos compósitos. O tratamento térmico, em geral, influenciou positivamente as propriedades estudadas. Sendo assim, a opção de realizar o tratamento térmico nos compósitos de acordo com as propriedades e fatores analisados, torna a técnica passível de ser recomendada.
Título en inglés
Effect of post-curing heat cured treatment in sorption and solubility, fracture toughness and degree of conversion of direct composites
Palabras clave en inglés
Composites
Degree of Conversion
Fracture Toughness
Post-curing heat treatment
Sorption and solubility
Resumen en inglés
The post-curing heat treatment in direct composite treatment was done to verify the influence on some properties like sorption, solubility, fracture toughness and the degree of conversion. During the referred study it was used three composites: nanoparticle, a microhybrid and a microfill. Two sources of light (Halogen and LED) and two periods (48 hours and 28 days) for each one, but not to solubility. The postcuringwas done in dry heat sterilizer of 170º C for five minutes for, half of the test samples (TS) were treated and the other half were only photoactivated. It was made 60 TS to sorption and solubility according to the analyzed factors (n=5) in a 15mm x 1mm round metal matrix. To calculate sorption and solubility the TS were weighted in a analytical balance, right after the beginning of the production in 1 hour, 24 hours, 7days, 14 days, 21 days and 28 days respectively in order to establish the initial absorbed mass (Mi), the absorbed mass (Ma) and the desiccated mass (Md ). It was produced 240 TS to the fracture toughness according to factors (n=10) in a 25mm x 5mm x 2,8mm in metallic matrix. The Single Edge Notch-Beam (SENB), was the used method during this study with a notch of 2,3mm placed in the center of the matrix. The TS were taken to a universal machine to flexural test so after the rupture referred surface fractures were analyzed in a stereomicroscope and then it was possible to get the images to calculate the size of the TS to insert the calculus of the fracture toughness. To degree conversion were made 36 TS in a 15mm x 1mm circular acetate matrix placed between two microscopes slides (n=3). The degree conversion was determined a infrared spectroscopy (FTIR). In general the study showed a significant influence in relation post-curing heat treatment. In both periods the sorption of the composites have decreased in general comparison to the photoactivated only. The interactions(light source versus period) was significant for all groups. To solubility the interaction (light source versus post-curing heat treatment) was significant for all groups. In reference to fracture toughnessonly post curing heat treatment factor was significant to the nanoparticle and microhybrid composites. In other hand the microfill composite were influenced by the main factors and by the interactions (light source X periods) and (llght source X heat cured). In general there was an increase of the fracture toughness value in all groups. In relation to the degree conversion there was an increase significant of the composite during heat cured and analyzed periods. The post-curing heat treatment influenced all the studied properties of the direct composite in a positive way. Therefore the option of doing the heat cured treatment in the composites according to the properties and the analyzed factor is technically possible to be done.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-04-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.