Tesis Doctoral
DOI
10.11606/T.23.2010.tde-18082010-124119
Documento
Autor
Nombre completo
Caroline Lumi Miyazaki
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Rodrigues Filho, Leonardo Eloy (Presidente)
Matos, Jivaldo do Rosario
Miranda Junior, Walter Gomes
Rodrigues, Flávia Pires
Santana, Ivone Lima
Título en portugués
Caracterização térmica, grau de conversão, resistência à flexão e dureza de compósitos comerciais tratados termicamente
Palabras clave en portugués
Análise Térmica
Dureza Knoop
Grau de Conversão
Resinas Compostas
Resistência à Flexão
Resumen en portugués
Visando otimizar as propriedades químicas e mecânicas de compósitos de uso direto aplicados na forma indireta, associados a tratamentos térmicos experimentais (TT), torna-se necessária uma caracterização térmica que permita a determinação de uma temperatura de TT segura (abaixo da temperatura de início de perda de massa). Assim, a primeira etapa deste estudo consistiu em caracterizar termicamente dez compósitos comerciais (Z100, Filtek Z250, Z350 e Supreme XT- 3M ESPE, Esthet-X e TPH Spectrum Dentsply, Charisma Heraeus Kulzer, Tetric Ceram Ivoclar Vivadent, Herculite XRV e Point 4 - Kerr), fotoativados pelo método contínuo (C) e pulse-delay (PD) (20 J.cm-2), por termogravimetria (TG) (n=1) e calorimetria exploratória diferencial (DSC) (n=3). Foram escolhidas duas temperaturas de TT: 100 e 170°C, aplicadas por 10 min, 24h após a fotoativação. A partir disto, avaliaram-se: 1) o grau de conversão (GC), por espectroscopia FT-Raman (n=3); 2) a resistência à flexão em três pontos (RF) (n=10); e 3) a dureza Knoop (KHN) para as faces topo e base (n=3) de quatro destes compósitos (Filtek Z250 e Supreme XT, Esthet-X e Point 4), após diferentes condições: imediatamente, 1h, 6h e 24h após a fotoativação e 24h após fotoativação seguida de TT a 100 ou 170°C. Os dados obtidos foram submetidos à análise de variância e ao teste de Tukey (nível de significância de 5%). Quanto ao GC (%), houve significância estatística para o fator material (p=0,000): Point 4 (68,42) > Z250 (63,05) = Esthet-X (61,69) > Supreme (54,27); condição (p=0,000): TT170 (73,20) = TT100 (73,58) > 24h (62,60) = 6h (60,18) > 1h (55,10) = imediato (53,66); e ativação (p=0,006): C (62,97) > PD (60,75). Também foram significantes as interações material × condição (p=0,007) e material × condição × ativação (p=0,013). Para a RF (MPa), foram encontradas significâncias estatísticas para os fatores material (p=0,000): Z250 (165,48) > Supreme (153,96) > Point 4 (131,30) = Esthet-X (128,06); e condição (p=0,000): TT170 (194,56) > TT100 (182,91) > 24h (150,88) > 6h (131,79) > 1h (111,77) > imediato (96,30); assim como para as interações: ativação × condição (p=0,000), material × condição (p=0,000) e material × ativação × condição (p=0,000). Para a dureza, foram encontradas significâncias estatísticas para os fatores: materialativação (p=0,000): Supreme C (82,46) > Supreme PD (80,29) = Z250 C (77,46) > Z250 PD (74,30) > Esthet-X C (69,17) > Esthet-X PD (65,67) > Point 4 C (57,21) = Point 4 PD (56,71); condição (p=0,000): TT170 (81,35) > TT100 (73,72) > 24h (70,36) > 6h (67,92) > 1h (64,99) > imediato (64,12) e face (p=0,000): topo (71,40) > base (69,40); assim como para as interações: material-ativação × face (p=0,011), material-ativação × condição (p=0,000) e face × condição (p=0,000). A partir dos resultados obtidos, pôde-se concluir que os TTs experimentais propostos foram capazes de aumentar as propriedades estudadas, sendo, de maneira geral, os resultados obtidos com 170°C melhores do que os com 100°C, e ambos melhores do que as demais condições.
Título en inglés
Thermal characterization, degree of conversion, flexural strength and Knoop hardness of heat treated commercial composites
Palabras clave en inglés
Composite Resins
Degree of Conversion
Flexural Strength
Knoop Hardness
Thermal Analysis
Resumen en inglés
Aiming to optimize chemical and mechanical properties of direct composites applied in an indirect way, with an association to experimental heat treatments (TT), it is necessary a thermal characterization, in a way to determine a safe temperature for the TT (below the significant mass loss temperature). Thus, the first step of this study was to perform the thermal characterization of ten commercial composites (Z100, Filtek Z250, Z350 and Supreme XT 3M-ESPE, Esthet-X and TPH Spectrum Dentsply, Charisma Heraeus Kulzer, Tetric Ceram Ivoclar Vivadent, Herculite XRV and Point 4 - Kerr) photoactivated by continuous (C) and pulse-delay (PD) methods (20 J.cm-2), by thermogravimetry (TG) (n=1) and differential scanning calorimetry (DSC) (n=3). After that, two temperatures were chosen for the TT: 100 and 170°C, which were applied for 10 min, 24h after photoactivation. Thus, some properties were evaluated for four composites (Filtek Z250 and Supreme XT, Esthet- X and Point 4): 1) degree of conversion (GC) by FT-Raman spectroscopy (n=3); 2) three-point bending test (RF) (n=10); and 3) Knoop hardness (KHN) for top and bottom surfaces (n=3). The conditions were: immediately, 1h, 6h and 24h after photoactivation and 24h after photoactivation followed by TT at 100 or 170°C. Data were analyzed by ANOVA and Tukeys test (level of significance of 5%). In relation to GC (%), there were statistical significance for the factors material (p=0.000): Point 4 (68.42) > Z250 (63.05) = Esthet-X (61.69) > Supreme (54.27); condition (p=0.000): TT170 (73.20) = TT100 (73.58) > 24h (62.60) = 6h (60.18) > 1h (55.10) = immediately (53.66); and activation (p=0.006): C (62.97) > PD (60.75); and for the interactions: material × condition (p=0.007) and material × condition × activation (p=0.013). For RF (MPa), statistical significance were found for the factors material (p=0.000): Z250 (165.48) > Supreme (153.96) > Point 4 (131.30) = Esthet-X (128.06); and condition (p=0.000): TT170 (194.56) > TT100 (182.91) > 24h (150.88) > 6h (131.79) > 1h (111.77) > immediately (96.30); and also for the interactions: activation × condition (p=0.000), material × condition (p=0.000) and material × activation × condition (p=0.000). For KHN, statistical significance were found for the factors material-activation (p=0.000): Supreme C (82.46) > Supreme PD (80.29) = Z250 C (77.46) > Z250 PD (74.30) > Esthet-X C (69.17) > Esthet-X PD (65.67) > Point 4 C (57.21) = Point 4 PD (56.71); condition (p=0.000): TT170 (81.35) > TT100 (73.72) > 24h (70.36) > 6h (67.92) > 1h (64.99) > immediately (64.12), and face (p=0.000): top (71.40) > bottom (69.40); as for the interactions: material-activation × face (p=0.011), material-activation × condition (p=0.000) and face × condition (p=0.000). By the results, it could be concluded that both proposed experimental TTs were capable of increasing the studied properties, with, in a general way, 170°C generating better mechanical properties than 100°C, and both better than the other conditions.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-08-24
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.