Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.23.2008.tde-17092008-101643
Document
Auteur
Nom complet
Mauricio Neves Gomes
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2008
Directeur
Jury
Francci, Carlos Eduardo (Président)
Cruz, Carlos Alberto dos Santos
Matos, Jivaldo do Rosario
 
Titre en portugais
Tratamento térmico pré e pós-cura de diferentes compósitos: análise térmica, reistência à flexão e grau de conversão
Mots-clés en portugais
Análise térmica diferencial calorimétrica
Resinas compostas
Resistência de materiais
Resumé en portugais
O objetivo deste estudo é realizar a caracterização térmica, resistência à flexão e o grau de conversão de um compósito nanoparticulado (Filtek Supreme XT: FT) e um microhíbrido (Esthet X: ET), cor A2, submetidos a diferentes tratamentos térmicos. Os grupos experimentais foram: G1: sem tratamento; G2: pré-aquecimento à 68°C com dispositivo Calset; G3: pós-aquecimento em forno MP-130, 10°C/min até 140°C e G4: pré e pós-aquecimento. Depois da fotoativação, foram realizadas análise termogravimétrica e calorimetria exploratória diferencial (DSC) para determinar a estabilidade térmica dos compósitos, temperatura de transição vítrea (Tg), pico de exotermia e calor liberado após fotoativação. O ensaio de resistência à flexão foi realizado 24h após armazenagem dos corpos de prova em água destilada a 37°C. A análise do grau de conversão foi realizada com espectrofotômetro FT-Raman. Análise de variância e teste de Tukey (p<0,05) demonstraram que os compósitos FT e ET têm 25,8% e 23,7% de matriz orgânica em peso respectivamente e estabilidade térmica até 200°C. O pico exotérmico do G2 (63,5°C) é maior do que G1 (60,9°C). Os grupos G3 e G4 não apresentaram pico exotérmico e calor liberado. A tg é de aproximadamente 160,5°C para o FT e de 161,4°C para o ET. A resistência à flexão (MPa) e grau de conversão(%) foram respectivamente: G1 (149,1; 60)=G2(152,5; 56,4) e G3 (170,5; 72,6)=G4 (178,2; 71,8) . O compósito ET apresenta maior grau de conversão que FT. À partir da caracterização térmica foi possível observar que o pré-aquecimento em condições não isotérmicas não promoveu maior conversão e resistência à flexão. O tratamento térmico deve ser realizado acima de 160°C.
 
Titre en anglais
Heat treatment pre and post cured of differents composites: thermal analysis, flexural strength and degree of conversion
Mots-clés en anglais
Composite resins
Differential Scanning Calorimetry Analysis
Materials Resistance
Resumé en anglais
The aim of this study was to perform the thermal characterization,flexural strength and degree of conversion of two composites, a nanofilled (Filtek Supreme XT: FT) and a microhybrid (Esthet X: ET), shade A2, submitted to different thermal treatments. Methods: The experimental groups were: G1: no treatment; G2: preheated at 68°C with Calset device; G3: post-heated in a MP-130 (EDG) oven, 10 °C/min up to reach 140°C for 20min and G4: pre and post-heated. After curing, thermogravimetric analysis and differential scanning calorimetry (DSC) were carried to determine thermal stability of the composites, glass transition temperature (Tg), exothermic peak and heat releasing after photoactivation. Three-point flexural test was performed after stored in water at 37oC for 24 hours. Degree of conversion was determined using a spectrophotometer FT-Raman. Analysis of variance and Tukey's test (P<0.05) showed that FT and ET composites have 25.8% and 23.7% of organic matrix in weight respectively and thermal stability at 200°C. The G2 group release more heat (9.9J/g) than G1 (7.3J/g). Exothermic peak of G2 group (63.5°C) is higher than G1 (60.9°C). G3 and G4 groups did not show exothermic peak and heat releasing. ET composite of G2 group presented the highest exothermic peak (65.2°C) of all groups. The Tg is nearly 160.5°C to FT and 161.4°C to ET. Flexural strength (MPa) and degree of conversion (%) were respectively: G1(149.1; 60) = G2(152.5; 56.4) and G3 (170.5; 72.6) = G4 (178,2; 71,8). ET composite presented higher conversion values than FT. Pre-heating at non-isothermal conditions does not promote higher conversion and flexural strength. Heat treatment after cure can be carried through 160°C.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
MauricioNevesGomes.pdf (565.47 Kbytes)
Date de Publication
2008-12-01
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs.
CeTI-SC/STI
© 2001-2024. Bibliothèque Numérique de Thèses et Mémoires de l'USP.