Mémoire de Maîtrise
DOI
10.11606/D.23.2018.tde-15022018-101701
Document
Auteur
Nom complet
Amanda Cavalcante Pereira
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2017
Directeur
Jury
Rodrigues Filho, Leonardo Eloy (Président)
Boaro, Letícia Cristina Cidreira
Moraes, André Guaraci de Vito de
Turbino, Miriam Lacalle
Titre en portugais
Influência da profundidade e de um processo de envelhecimento acelerado em propriedades de resinas bulk fill
Mots-clés en portugais
Dureza
Envelhecimento
Módulo de Elasticidade
Resinas Compostas
Resumé en portugais
O presente estudo teve como objetivo avaliar o desempenho de quatro resinas bulk fill (Filtek Bulk Fill (FBF), Opus Bulk Fill (OBF), Sonicfill (SF) e Tetric N-Ceram Bulk Fill (TNBF)) e uma resina convencional (Charisma Diamond (CD)) quanto às seguintes propriedades: resistência à flexão (RF), módulo de elasticidade (ME) e dureza Knoop (KHN) em função da profundidade e após a realização de um envelhecimento acelerado. Corpos de prova em formato de barra foram confeccionados simultaneamente em diferentes profundidades (1, 2, 3, 4 e 5 mm) para realização dos testes de resistência à flexão (n=10), módulo de elasticidade (n=10) e dureza Knoop (n=3). Os testes foram realizados em dois momentos, previamente e após a realização de um envelhecimento acelerado, que consistiu na realização de uma termociclagem com banhos alternados em água a 5 e 55ºC, com 1 min de imersão em cada, por 2000 ciclos. Os resultados para o teste de RF e ME mostraram que os valores para estas duas propriedades diminuíram em função da profundidade e após a realização da termociclagem para todas as resinas estudadas. Apenas a resina TNBF não apresentou diferença estatística para valores de ME após o envelhecimento acelerado. Quanto à dureza, os valores também diminuíram em função da profundidade, porém aumentaram após a realização do envelhecimento acelerado. Apenas a resina SF não apresentou diferença estatística entre os valores de dureza antes e após o envelhecimento. A resina convencional CD após a ciclagem térmica foi a única que apresentou relação base/topo (2 mm) acima de 80%. Nenhuma das resinas do tipo bulk fill apresentou uma relação base/topo acima de 80% para a dureza quando avaliadas na espessura máxima recomendada. Com base nos resultados obtidos, pode-se afirmar que, quando fotoativadas na espessura máxima recomendada, apenas a resina convencional CD apresentou resultados condizentes com a homogeneidade esperada em todas as condições deste estudo. Entretanto, para as resinas do tipo bulk fill, pode-se observar que as propriedades estudadas, de modo geral, sofreram uma diminuição significativa em função da profundidade. Para o envelhecimento, a dureza, diferentemente dos outros parâmetros, mostrou uma tendência de aumento.
Titre en anglais
Influence of depth and an accelerated aging process on bulk fill resin properties
Mots-clés en anglais
Aging
Composite Resin
Elastic Modulus
Hardness
Resumé en anglais
The purpose of this study was to evaluate the performance of four bulk fill resins (Filtek Bulk Fill (FBF), Opus Bulk Fill (OBF), Sonicfill (SF) and Tetric N-Ceram Bulk Fill (TNBF)) and a conventional resin (Charisma Diamond (CD)) for the following properties: flexural strength (FS), flexural modulus (FM) and Knoop hardness (KHN) as a function of depth and after accelerated aging. Specimens were made simultaneously with different depths (1, 2, 3, 4 and 5 mm) for flexural strength tests (n = 10), flexural modulus (n = 10) and Knoop hardness (n = 3). The tests were carried out in two moments, before and after the accelerated aging process, which consisted of thermocycling with alternating baths in water at 5 and 55ºC, with 1 min immersion in each, for 2000 cycles. The results for the FS and FM tests showed that the values for these two properties decreased as a function of depth and after the thermocycling for all the studied resins. Only TNBF resin showed no statistical significant differences in FM values after accelerated aging. For the hardness test, values also decreased as a function of depth, but increased after accelerated aging. SF resin was the only one that showed no statistical significant differences between hardness values before and after aging. CD, after thermal cycling, was the exclusive resin to show a bottom/top ratio above 80%. None of the bulk fill resins had a bottom/top ratio above 80% for hardness when evaluated at the maximum recommended thickness. Based on the results obtained, it can be stated that, when photoactivated at the maximum recommended thickness, only the conventional resin CD presented results consistent with the expected homogeneity in all the conditions of this study. However, for bulk fill resins, it can be observed that the studied properties, in general, suffered a significant decrease as a function of depth. For aging, the hardness, unlike the other parameters, showed a tendency to increase.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2018-02-16
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.