Master's Dissertation
DOI
10.11606/D.23.2013.tde-13122013-161327
Document
Author
Full name
Thayse da Costa Guimarães
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Braga, Roberto Ruggiero (President)
Boaro, Letícia Cristina Cidreira
Miranda Junior, Walter Gomes
Title in Portuguese
Desenvolvimento de tensões de polimerização determinado através do método da propagação de trincas
Keywords in Portuguese
Grau de conversão
Módulo flexural
Resina Composta
Tensão de polimerização
Abstract in Portuguese
O objetivo do presente estudo foi avaliar o desenvolvimento das tensões de polimerização de um compósito resinoso restaurador ao longo das primeiras 24 horas após a fotoativação, segundo dois métodos de análise da propagação de trincas. A influência do armazenamento em água sobre a magnitude das tensões também foi avaliada. O grau de conversão (GC) e o módulo de elasticidade (E) do compósito foram determinados nos diferentes tempos de observação. As hipóteses nulas do trabalho foram: 1) tensão de polimerização, GC e E não variam de forma significativa ao longo do período de observação; 2) os dois métodos de análise de propagação de trincas fornecem resultados semelhantes; 3) os valores de tensão não são influenciados pelo meio de armazenamento. Foram confeccionados discos de vidro de soda-cal com 2 mm de espessura, diâmetro externo de 12 mm, com perfuração central de 4 mm de diâmetro. Os discos foram aleatorizados em três grupos. Em um deles, os discos foram restaurados (Charisma Diamond, Heraeus Kulzer) e, após os tempos de 10 min, 1, 2, 4, 8 ou 24 horas (n=10), os espécimes receberam quatro indentações Vickers, (9,8N por 20s) a 500m da margem da cavidade. O segundo grupo passou pelo mesmo processo, porém os discos ficaram armazenados em água antes de serem indentados. Em seguida, o comprimento das trincas e a diagonal da indentação foram mensurados em microscópio óptico. A tensão residual no vidro foi calculada de acordo com a norma 4-01 (The Society of Materials Science, JSMS, Japão). No terceiro grupo, os discos foram indentados e armazenados em dissecador por 24h antes de serem restaurados. As trincas foram medidas antes e após a restauração, nos mesmos tempos descritos acima, e a tensão calculada de acordo com a fórmula descrita por Yamamoto et al. (Dent Mater, 2009). O GC foi determinado por espectroscopia no infra-vermelho próximo (n=3). O E foi obtido através do teste de dobramento em três pontos (n=10). Os dados foram submetidos a ANOVA/Tukey (=0,05) e análise de regressão. A tensão de polimerização, assim como o GC e o E tiveram seus valores aumentados ao longo do tempo. O GC aumentou 28% entre 10 minutos e 24 horas, para o E houve um aumento de 1,7 GPa para 6,3 GPa entre 10 minutos e 24 horas. A tensão de polimerização aumentou 40% entre 10min e 24h para a norma 4-01 e 51% para o método do Yamamoto et al. O meio de armazenamento foi estatisticamente significativo até o tempo de 4 horas. Portanto, a primeira hipótese foi rejeitada. A segunda e a terceira hipótese podem ser apenas parcialmente rejeitadas.
Title in English
Development also polymerization stress determined by crack analysis methods
Keywords in English
Composite resin
Degree of conversion
Modulus of elasticity
Polymerization stress
Abstract in English
The objective of this study was to evaluate composite resin restoration polymerization stress development over the first 24 hours after polymerization, according to two methods of analysis of crack propagation. The influence of water storage on the magnitude of the stresses was also evaluated. The degree of conversion (DC) and modulus of elasticity (E) of the composite were determined at various time points. The null hypotheses of this study were: 1) The polymerization stress, DC and E do not change significant throughout the observation period, 2) the two methods of analysis of crack propagation provide similar results, 3) the stress values are not influenced by storage medium. Disks were made of soda-lime glass with 2 mm thickness, 12 mm in outside diameter with central bore of 4 mm in diameter. The perforations were treated with hydrofluoric acid and silane. The discs were randomized into three groups. In one of them, the discs were restored (Charisma Diamond, Heraeus Kulzer), and, the times after 10 min, 1, 2, 4, 8 or 24 hours (n = 10), the specimens received four Vickers indentations (9.8 N for 20 s) at 500m cavity margin. The second group went through the same process, but the discs were stored in water prior to being indented. Then, the length diagonal of the indentation and crack was measured in an optical microscope. The residual stress in the glass was calculated according to standard 4-01 (The Society of Materials Science, JSMS, Japan). The third group of discs were treated similarly, indented and stored in a desiccator for 24 hours before being restored. The cracks were measured before and after the restoration following the same time, and the stress calculated according to the formula described by Yamamoto et al. (Dent Mater, 2009). The DC was determined by near-infrared spectroscopy (n = 3). The E was obtained through the bend test conducted at three-points. Data were subjected by ANOVA / Tukey test ( = 0.05) and regression analysis. The polymerization stress, as well as DC and E values were increased over time. GC increased 28% between 10 minutes and 24 hours, and for an increase of 1.7 GPa to 6.3 GPa between 10 minutes and 24 hours. The polymerization stress increased 40% between 10 min and 24 hours to the standard 4.1 and 51% for the method of Yamamoto et al. The storage medium was statistically significant at the time of 4 hours. Thus, the first hypothesis was rejected. The second and third hypothesis may only be partially rejected.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2014-02-11
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2022. All rights reserved.