Thèse de Doctorat
DOI
https://doi.org/10.11606/T.23.2008.tde-08042009-153710
Document
Auteur
Nom complet
Nívea Regina de Godoy Fróes Salgado
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2008
Directeur
Jury
Francci, Carlos Eduardo (Président)
Braga, Roberto Ruggiero
Giannini, Marcelo
Pfeifer, Carmem Silvia Costa
Soares, Carlos José
Titre en portugais
Influência do pré-aquecimento e de diferentes regimes de fotoativação na adaptação marginal, grau de conversão e propriedades mecânicas de um compósito nanoparticulado
Mots-clés en portugais
Adaptação marginal
Grau de conversão
Propriedades mecânicas
Resinas compostas
Resumé en portugais
Proposição: O objetivo deste estudo foi verificar a influência do pré-aquecimento e de regimes de fotoativação (dois contínuos e um em dois passos com baixa irradiância inicial) sobre a adaptação marginal de restaurações, grau de conversão (GC), resistência à flexão (RF) e microdureza Knoop (KHN) de um compósito. Material e Métodos: O nanocompósito Filtek Z350 foi submetido às seguintes condições experimentais: com ou sem pré-aquecimento a 68ºC através do dispositivo Calset; e fotoativado através de um dos três regimes a seguir: 600mW/cm2 por 20s ou 40s (12 ou 24J/cm2 respectivamente) ou 200mW/cm2 por 20s + intervalo de 1 minuto + 500mW/cm2 por 40s (24J/cm2). O teste de adaptação marginal foi realizado através de microscopia eletrônica de varredura, com a mensuração de gaps em réplicas de cavidades Classe V (n=10) em aumento de 200X. A interface adesiva foi dividida em sete segmentos para o cálculo de freqüência de gaps. GC foi obtido através de espectroscopia em FT-Raman nas faces irradiada e oposta de espécimes (n=3) mantidos durante 24h em ambiente escuro a 37°C. RF do compósito foi medida por ensaio de dobramento em três pontos em espécimes (n=10) armazenados em água destilada por 24h. KHN foi mensurada inicialmente (n=6) após 24h de estocagem a seco. Foi realizada armazenagem em etanol 100%, seguida de segunda medida para o cálculo da redução percentual de KHN. Os resultados foram analisados através de análise de variância e teste de Tukey (=0,05) para os testes de GC, RF e KHN e com os testes de Friedman, Wilcoxon e Kruskal-Wallis para a adaptação marginal. Resultados: As paredes axiais das restaurações apresentaram maior freqüência de gaps quando comparadas às laterais. O pré-aquecimento do compósito reduziu a freqüência de gaps. Os regimes de fotoativação demonstraram freqüência de gaps semelhantes entre si. No teste de GC apenas o fator face foi estatisticamente significativo (p<0,05), com maiores valores médios para as faces irradiadas. O regime de ativação em dois passos causou redução (p<0,01) dos valores médios de RF. No teste de KHN após 24h tanto os fatores principais como a interação apresentaram-se estatisticamente significativos (p<0,05 para modo de fotoativação, p<0,001 para pré-aquecimento e p<0,05 para a interação). Os grupos pré-aquecidos demonstraram em geral menores médias de KHN do que aqueles sem aquecimento. Comparando-se os grupos sem pré-aquecimento, não houve diferença em função do modo de fotoativação. Entre os grupos pré-aquecidos, houve diminuição de KHN para 600mW/cm2 por 20s. Na KHN após etanol apenas o fator pré-aquecimento foi significativo (p<0,001), com as menores médias apresentadas pelos grupos pré-aquecidos. A redução percentual da KHN após armazenamento em etanol ocorreu de forma uniforme para todos os grupos. Conclusões: O pré-aquecimento do compósito estudado promoveu melhor vedamento da interface adesiva sem, no entanto, afetar seu grau de conversão e resistência à flexão. O regime de fotoativação com baixa irradiância inicial reduziu a resistência à flexão do compósito, apesar de produzir grau de conversão similar ao de formas contínuas. O pré-aquecimento pode reduzir a microdureza da superfície irradiada de um compósito.
Titre en anglais
Influence of preheating and different photoactivation modes on marginal adaptation, degree of conversion and mechanical properties of a nanofiller composite
Mots-clés en anglais
Degree of conversion
Marginal adaptation
Mechanical properties
Resin composites
Resumé en anglais
Proposition: The objective of this study was to verify the influence of preheating and photoactivation modes (two continuous and one in two steps with a low initial irradiance) on restoration marginal adaptation, degree of conversion (DC), flexural strength (FS) and Knoop microhardness (KHN) of a composite. Material and Methods: The nanocomposite Filtek Z350 was evaluated under the following experimental conditions: pre-heated up to 68ºC with the use of Calset device or without preheating; and photoactivated through one of the three regimens: 600mW/cm2 for 20s or 40s (12 and 24J/cm2 respectively) and one in two steps (200mW/cm2 for 20s + 1 minute delay + 500mW/cm2 for 40s (24J/cm2). Marginal adaptation test was performed by scanning electron microscopy, measuring gaps in Class V replica (n=10) under 200X magnification. The adhesive interface was segmented in seven parts for gaps frequency calculus. DC was obtained by FT-Raman spectroscopy in irradiated and non-irradiated surfaces (n=3) of samples stored in dark for 24h at 37C . FS was evaluated in a three-bending test in samples (n=10) after 24h storage in distilled water. KHN was measured (n=6) initially after 24h dark and dry storage. After that, samples were stored in 100% ethanol and KHN percentual reduction calculated. Results were analysed by ANOVA and Tukey's test (=0.05) DC, FS and KHN and with Friedman, Wilcoxon and Kruskal-Wallis tests for marginal adaptation. Results: Axial walls of the restorations showed higher gaps frequency than lateral walls. Composite preheating leaded to a lower gaps frequency. Photoactivation modes demonstrated similar gap frequency. In DC test only the main factor surface was significant (p<0.05), with higher mean values for irradiated surfaces. The two steps regimen reduced (p<0.01) mean FS values. About KHN after 24h, both main factors and their interaction were significant (p<0.05 for photoactivation mode, p<0.001 for pre-heating use and p<0.05 for interaction). Generally pre-heated groups showed lower KHN means than non-preheated. Comparing non-preheated groups there was not a statistical difference regardless the photoactivation mode. In preheated groups, KHN mean for 600mW/cm2 during 20s was lower than means for other irradiation regimens. In KHN after ethanol, the main factor pre-heating was significant (p<0.001). Preheated groups showed lower means than non-preheated. KHN percentual reduction after ethanol storage occured in a uniform way for all groups. Conclusions: Preheating of the nanocomposite in study promoted a better adhesive interface sealing without compromising the degree of conversion and flexural strength. The photoactivation method that uses a low initial irradiance reduced composite flexural strength in spite of the similar degree of conversion was reached, comparing to continuous modes. Pre-heating can reduce irradiated surface microhardness.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
NiveaFroesSalgado.pdf (954.97 Kbytes)
Date de Publication
2009-06-08
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.