Thèse de Doctorat
DOI
10.11606/T.23.2010.tde-03072010-100616
Document
Auteur
Nom complet
Flavia Gonçalves
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2010
Directeur
Jury
Braga, Roberto Ruggiero (Président)
Pfeifer, Carmem Silvia Costa
Piva, Evandro
Valandro, Luiz Felipe
Witzel, Marcelo Ferreira
Titre en portugais
Influência do conteúdo inorgânico e da composição da matriz resinosa no desenvolvimento de tensões de polimerização em compósitos experimentais
Mots-clés en portugais
Conteúdo inorgânico
Matriz orgânica
Propriedades mecânicas
Resinas Compostas
Tensão de polimerização
Resumé en portugais
Objetivo: avaliar a relação de dependência da tensão de polimerização (TP), grau de conversão (GC), taxa máxima de reação de polimerização (Rpmax), contração volumétrica (CV), módulo de elasticidade (E) e tangente de delta (tan) com o conteúdo inorgânico e proporção de BisGMA:TEGDMA e verificar as possíveis relações de dependência entre a TP e as demais variáveis-resposta. Material e métodos: Foram preparadas vinte formulações, com concentrações de carga de 40, 50, 60 ou 70 % em peso de vidro de bário e proporções molares de BisGMA:TEGDMA de 3:7, 4:6, 5:5, 6:4 ou 7:3. TP (n=7) foi determinada pela inserção do compósito entre bastões de acrílico fixados às garras de uma máquina universal de ensaios e dividindo-se a máxima força de contração registrada pela secção transversal dos bastões. GC e Rpmax foram determinados por espectroscopia no infra-vermelho próximo (n=5). CV foi mensurada em dilatômetro de mercúrio (n=3). E foi obtido através do teste de flexão em três pontos (n=10). Tan foi determinada por nanoidentação dinâmica (n=3). Foram realizadas análises de regressão para avaliar a influência da fração inorgânica e da proporção monomérica nas variáveis estudadas e para avaliar o efeito das variáveis-resposta na determinação da TP. Resultados: Todas as variáveis se mostraram dependentes da concentração inorgânica e conteúdo monomérico. TP, GC e Rpmax foram mais influenciados pela matriz, enquanto que CV, E e tan apresentaram maior efeito da concentração de carga. TP mostrou-se dependente dos fatores CV e GC. Conclusões: a formulação de compósitos com baixa TP deve observar criteriosamente a fração inorgânica e o conteúdo monomérico, sendo o principal desafio encontrar formulações com baixa CV, uma vez que os demais fatores demonstraram não ter influência significativa e o GC do material não deve ser sacrificado com o propósito de reduzir a TP.
Titre en anglais
Influence of inorganic content and resin matrix composition on polymerization stress development
Mots-clés en anglais
Inorganic content
Mechanical properties
Organic matrix
Polymerization stress
Resin composites
Resumé en anglais
Objective: To evaluate the dependence relationship of polymerization stress (PS), degree of conversion (DC), maximum polymerization rate (Rpmax), volumetric shrinkage (VS), elastic modulus (E) and loss tangent (tan) with the inorganic content and BisGMA:TEGDMA ratio and verify possible relationship among PS and the others variables. Materials and Methods: twenty resin composites were studied, having barium glass concentration of 40, 50, 60 or 70 wt% and BisGMA:TEGDMA molar ratio of 3:7, 4:6, 5:5, 6:4 or 7:3. PS (n=7) was determined inserting the composite between acrylic rods fixed to clamps of an universal test machine and dividing the maximum load recorded by the rods cross-sectional area. DC and Rpmax were determined by near infrared spectroscopy in real time (n=5). VS was measured by mercury dilatometer (n=3). E was obtained by three-point bending test (n=10). Tan was determined by dynamic nanoindentation (n=3). Regression analyses were performed to evaluate the relationship of inorganic content and monomeric ratio on studied variables and to evaluate the effect of the variables on the polymerization stress development. Results: All variables showed dependence on inorganic concentration and monomeric content. PS, DC and Rpmax were more affected by resin matrix whereas VS, E and Tan were more strongly influenced by filler fraction. PS was dependent on both volumetric shrinkage and degree of conversion. Conclusions: in order to obtain composites formulations which provide low polymerization, the inorganic concentration and monomeric contend have to be carefully observed. The main challenge is to design formulations with low VS since the others factors apparently do not have significance and PS should not come at the expense of DC.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
FlaviaGoncalves.pdf (4.08 Mbytes)
Date de Publication
2010-07-13
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.