Doctoral Thesis
DOI
10.11606/T.23.2010.tde-03072010-100616
Document
Author
Full name
Flavia Gonçalves
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2010
Supervisor
Committee
Braga, Roberto Ruggiero (President)
Pfeifer, Carmem Silvia Costa
Piva, Evandro
Valandro, Luiz Felipe
Witzel, Marcelo Ferreira
Title in Portuguese
Influência do conteúdo inorgânico e da composição da matriz resinosa no desenvolvimento de tensões de polimerização em compósitos experimentais
Keywords in Portuguese
Conteúdo inorgânico
Matriz orgânica
Propriedades mecânicas
Resinas Compostas
Tensão de polimerização
Abstract in Portuguese
Objetivo: avaliar a relação de dependência da tensão de polimerização (TP), grau de conversão (GC), taxa máxima de reação de polimerização (Rpmax), contração volumétrica (CV), módulo de elasticidade (E) e tangente de delta (tan) com o conteúdo inorgânico e proporção de BisGMA:TEGDMA e verificar as possíveis relações de dependência entre a TP e as demais variáveis-resposta. Material e métodos: Foram preparadas vinte formulações, com concentrações de carga de 40, 50, 60 ou 70 % em peso de vidro de bário e proporções molares de BisGMA:TEGDMA de 3:7, 4:6, 5:5, 6:4 ou 7:3. TP (n=7) foi determinada pela inserção do compósito entre bastões de acrílico fixados às garras de uma máquina universal de ensaios e dividindo-se a máxima força de contração registrada pela secção transversal dos bastões. GC e Rpmax foram determinados por espectroscopia no infra-vermelho próximo (n=5). CV foi mensurada em dilatômetro de mercúrio (n=3). E foi obtido através do teste de flexão em três pontos (n=10). Tan foi determinada por nanoidentação dinâmica (n=3). Foram realizadas análises de regressão para avaliar a influência da fração inorgânica e da proporção monomérica nas variáveis estudadas e para avaliar o efeito das variáveis-resposta na determinação da TP. Resultados: Todas as variáveis se mostraram dependentes da concentração inorgânica e conteúdo monomérico. TP, GC e Rpmax foram mais influenciados pela matriz, enquanto que CV, E e tan apresentaram maior efeito da concentração de carga. TP mostrou-se dependente dos fatores CV e GC. Conclusões: a formulação de compósitos com baixa TP deve observar criteriosamente a fração inorgânica e o conteúdo monomérico, sendo o principal desafio encontrar formulações com baixa CV, uma vez que os demais fatores demonstraram não ter influência significativa e o GC do material não deve ser sacrificado com o propósito de reduzir a TP.
Title in English
Influence of inorganic content and resin matrix composition on polymerization stress development
Keywords in English
Inorganic content
Mechanical properties
Organic matrix
Polymerization stress
Resin composites
Abstract in English
Objective: To evaluate the dependence relationship of polymerization stress (PS), degree of conversion (DC), maximum polymerization rate (Rpmax), volumetric shrinkage (VS), elastic modulus (E) and loss tangent (tan) with the inorganic content and BisGMA:TEGDMA ratio and verify possible relationship among PS and the others variables. Materials and Methods: twenty resin composites were studied, having barium glass concentration of 40, 50, 60 or 70 wt% and BisGMA:TEGDMA molar ratio of 3:7, 4:6, 5:5, 6:4 or 7:3. PS (n=7) was determined inserting the composite between acrylic rods fixed to clamps of an universal test machine and dividing the maximum load recorded by the rods cross-sectional area. DC and Rpmax were determined by near infrared spectroscopy in real time (n=5). VS was measured by mercury dilatometer (n=3). E was obtained by three-point bending test (n=10). Tan was determined by dynamic nanoindentation (n=3). Regression analyses were performed to evaluate the relationship of inorganic content and monomeric ratio on studied variables and to evaluate the effect of the variables on the polymerization stress development. Results: All variables showed dependence on inorganic concentration and monomeric content. PS, DC and Rpmax were more affected by resin matrix whereas VS, E and Tan were more strongly influenced by filler fraction. PS was dependent on both volumetric shrinkage and degree of conversion. Conclusions: in order to obtain composites formulations which provide low polymerization, the inorganic concentration and monomeric contend have to be carefully observed. The main challenge is to design formulations with low VS since the others factors apparently do not have significance and PS should not come at the expense of DC.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
FlaviaGoncalves.pdf (4.08 Mbytes)
Publishing Date
2010-07-13
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.