Disertación de Maestría
DOI
10.11606/D.23.2009.tde-28042009-094222
Documento
Autor
Nombre completo
Frederico Seidi Hori
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Carvalho, Rubens Corte Real de (Presidente)
Aranha, Ana Cecilia Corrêa
Santos, Flávio Augusto Merichello dos
Título en portugués
Adesivos experimentais com diferentes parâmetros de solubilidade: teste de microcisalhamento após 1, 7 e 90 dias
Palabras clave en portugués
Adesão
Microcisalhamento
Parâmetros de solubilidade
Resumen en portugués
Adesivos modernos são misturas complexas de monômeros resinosos hidrofílicos e hidrofóbicos dissolvidos em combinações de água/solvente. A inclusão de monômeros altamente hidrofílicos nos sistemas adesivos está transformando-os em membranas permeáveis que são altamente susceptíveis aos efeitos de degradação da água. Desenvolver formulações adesivas que promovem uma melhor penetração de componentes hidrofóbicos dentro da matriz dentinária é de grande importância. O método mais válido para se avaliar o processo de degradação in vitro é a armazenagem dos espécimes em água. Neste estudo avaliamos através do microcisalhamento com delimitação da área adesiva de 0,8 mm, a resistência adesiva de 3 adesivos experimentais com diferentes graus de hidrofilia. Os fatores de variação foram 2: o tipo de adesivo experimental utilizado, em 4 níveis ( Bis-GMA, Bis-EMA/ Bis-GMA, PBH, Single Bond) e o período de armazenamento, em 3 níveis (1 dia, 7 dias, 90 dias), totalizando 12 níveis de variação. Foram confeccionadas 120 superfícies de dentina de 30 terceiros molares extraídos, totalizando um n= 10. O modelo estatístico escolhido foi o teste paramétrico de ANOVA de dois fatores independentes. Os adesivos experimentais apresentaram valores na faixa de 11.31 a 12.96 MPa, sendo que o PBH apresentou os menores valores de resistência adesiva, Bis-GMA os maiores e Bis-EMA/Bis-GMA valores intermediários, enquanto que o grupo Controle está dentro de uma faixa média de 24 MPa. Através da MEV, observamos que os adesivos experimentais não formaram camada híbrida, embora tenha ocorrido a penetração nos túbulos dentinários e a formação de tags de resina. Provavelmente, a menor hidrofilicidade dos adesivos não permitiu a penetração dos adesivos na matriz de colágeno úmida para provocar uma hibridização levando a resistências adesivas bem menores que o adesivo controle. Com o presente estudo, concluímos que adesivos dentinários com componentes monoméricos hidrofóbicos, embora formem tags de resina, se tornam incapazes de penetrar nas fibras colágenas e formar camada híbrida e consequentemente têm baixa resistência adesiva e que também tende a decair com o tempo.
Título en inglés
Experimental adhesives with different hydrophilicity: microshear test in 1, 7 and 90 days
Palabras clave en inglés
Adhesion
Microshear
Solubility parameters
Resumen en inglés
The most recent adhesives systems have fewer steps required for bonding to simplify use and hopefully reduce technique sensitivity. A trend in adhesive dentistry is providing simpler and faster adhesives. Single bottle adhesives are complex mixtures of hydrophilic and hydrophobic resin monomers dissolved in water/solvent combinations. In this study we evaluate by microshear test 3 experimental adhesives with different degree of hydrophilicity after 1, 7 and 90 days.The variation factors were 2: the type of the adhesive used, at 4 levels (Bis-GMA, Bis-EMA/Bis-GMA, PBH, Single Bond) and the period of storage, in 3 levels (1 day, 7 days, 90 days), totalizing 12 levels of variation. The etch-and-rinse experimental adhesive systems were formulated by FGM, Joinville, SC, BR. The experimental units were confectioned on 120 dentine surfaces of 30 third extracted molar, totalizing n= 10. The specimens were stored in water distilled and divided in 4 groups of 10 specimens in accordance with the type of used monomer, being that each tooth origin 4 specimens. The delimitation of the adhesive area was used, made with adhesive ribbon double face with 1 circular perforation lined up of 0,8 mm of diameter made with a rubber sheet perforator in each specimen, being used for each one tygon tubing with light of 0,8 mm. The fractures were classified as adhesive, coesive in dentine, coesive in resin and mixing. Using the parametric test of variance analyses (ANOVA) of two independent factors, we observed that the experimental adhesives showed values in the range of 11.31 a 12.96 MPa, as the PBH showed the lowest values of resistance, Bis-GMA the highest and Bis-EMA/Bis-GMA intermediary values, and the control group in the range of 24 MPa. Dentin adhesives with hydrophobic monomeric components can form resin tags, but they are disable to penetrate colagen fibers and form hybrid layers and consequently have low bond resistance that falls with time.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-11-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.