Master's Dissertation
DOI
10.11606/D.23.2013.tde-17122013-154725
Document
Author
Full name
Milena Traversa Palazon
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Youssef, Michel Nicolau (President)
Hanashiro, Fernando Seishim
Turbino, Miriam Lacalle
Title in Portuguese
Avaliação da influência da técnica incremental na força coesiva de diferentes resinas compostas
Keywords in Portuguese
Compósitos
Contração de polimerização
Força coesiva
Silorano
Técnica incremental
Abstract in Portuguese
O objetivo desse estudo foi avaliar a influência da técnica incremental na força coesiva de diferentes resinas compostas. Foi confeccionado para este trabalho um dispositivo bipartido de Teflon que se encaixa em um magazine metálico para manter as metades em posição durante a preparação dos corpos de prova do compósito. A partir deste dispositivo de forma cônica, e dimensões: 4mm de base, 2mm de diâmetro na interface e 4mm de altura, foram obtidos 120 espécimes, divididos em 12 grupos ( n=10), 6 grupos sem o uso de adesivo e 6 grupos com o uso de adesivo. Foram utilizadas as resinas compostas: Filtek P90-3M ESPE, St.Paul,MN,USA e Filtek Z350 XT-3M ESPE, St. Paul, MN,USA , ambas na cor A3, inseridas no dispositivo bipartido de teflon segundo a técnica incremental adotada, técnica incremental obliqua, horizontal ou incremento único. A resina foi inserida com uma espátula metálica em incrementos horizontais ou em incrementos oblíquos, conforme a inclinação dada pelo instrumental utilizado, em incrementos de 2mm de espessura, ou ainda inserida de uma só vez, em porção única de 4mm de espessura e fotoativadas por 20 segundos, segundo indicação do fabricante. Os espécimes foram submetidos aos testes de tração para avaliar a força coesiva da resina composta e a influência da técnica incremental utilizada. Os dados obtidos foram analisados quanto à sua distribuição, à Análise de Variância (ANOVA) e ao Teste de Tukey HSD (p>0,05 %). Pode - se concluir que a técnica incremental utilizando incrementos oblíquos influencia negativamente na resistência coesiva. A Resina Filtek Z350XT possui maior resistência coesiva quando comparada à resina Filtek P90. A utilização de adesivo influencia negativamente na resistência coesiva.
Title in English
Influence of incremental technique on the cohesive strength of different dental resin composites: microtensile bond strenght analysis
Keywords in English
Cohesive strength
Composites
Incremental technique
Shrinkage
Silorane
Abstract in English
The aim of this study was to evaluate the influence of incremental technique on the cohesive strength of different dental resin composites. A total of 120 conical specimens of different resin composites, Filtek P90 and Filtek Z350 XT, both in color A3, were made in a bipartite teflon device with the following dimensions: 4 mm base diameter of 2mm and 8mm in height. The specimens were assigned into 12 groups (n = 10), 6 groups without the use of adhesive and 6 groups with the use of adhesive. The cavity was filled with a metal spatula in oblique or horizontal increments of 2mm thick or inserted at once in one portion 4mm thick and each increment was light-cured for 20 seconds following manufactures instructions. The specimens were subjected to microtensile tests to evaluate the cohesive strength of the resin composite and the influence of incremental technique used. Data were submitted to ANOVA and Tukey's HSD test (p<0,05%).Can be concluded that the incremental technique using increments oblique negatively influence the cohesive strength. The resin Filtek Z350XT has greater cohesive resistance when compared to Filtek P90. The use of adhesive negatively influence the cohesive resistance
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2014-02-11
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.