Disertación de Maestría
DOI
10.11606/D.18.2014.tde-29012015-215637
Documento
Autor
Nombre completo
Marcelo Rizzo Piton
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2014
Director
Tribunal
Mastelaro, Valmor Roberto (Presidente)
Lisboa Filho, Paulo Noronha
Silva, Elson Longo da
Título en portugués
Síntese e caracterização do composto SrTi1-xMnxO3 nanoestruturado
Palabras clave en portugués
Fotoluminescência
Manganês
Precursores poliméricos
SrTiO3
XANES
Resumen en portugués
Amostras nanoestruturadas do sistema SrTi1-xMnxO3 (STM) com x = 0%, 0.5%, 1%, 2.5%, 5% e 10% na forma de pó foram sintetizadas através do método dos precursores poliméricos. As propriedades térmicas, estruturais e ópticas das amostras STM calcinadas em diferentes temperaturas foram analisadas a temperatura ambiente através de técnicas de análise térmica, difração de raios-x, espectroscopia de absorção de raios-x e fotoluminescência. Os resultados obtidos através das técnicas de analise térmica mostraram que o íon manganês causa um efeito retardante, aumentando a temperatura onde ocorre o início da cristalização. Os resultados de DRX mostraram que no limite de solubilidade estudado, o íon manganês foi incorporado em solução sólida no sítio B na rede do SrTiO3 (ST), assumindo estados de oxidação entre +3,4 e +3,7, indicando que ocorre a criação de defeitos para compensação de cargas, mantendo a neutralidade elétrica do material. A análise dos espectros de fotoluminescência das amostras STM amorfas mostrou que o aumento da quantidade de manganês até 1% leva a um aumento da intensidade fotoluminescência em relação a amostra SrTiO3. Entretanto, a adição de manganês acima desta quantidade leva a uma diminuição pronunciada da intensidade fotoluminescente. Nas amostras amorfas não foi observada uma variação significativa da ordem local ao redor dos átomos de titânio bem como no estado de oxidação dos átomos de manganês à medida que a quantidade de manganês aumenta. Desta forma, a variação da intensidade fotoluminescente não pôde ser atribuída a estes fatores. O aumento da temperatura de calcinação leva a uma diminuição significativa da intensidade fotoluminescente. Uma análise dos espectros XANES medidos na borda K do titânio destas amostras mostrou que ocorre uma maior ordenação dos átomos de Ti nos octaedros de oxigênio [TiO6] a medida que a temperatura de calcinação aumenta, ou seja, à medida que aumenta o grau de cristalinidade das amostras.
Título en inglés
Synthesis and characterization of nanostructured SrTi1-xMnxO3 compound
Palabras clave en inglés
Manganese
Photoluminescence
Polymeric precursor method
SrTiO3
XANES
Resumen en inglés
Nanostructured SrTi1-xMnxO3 (STM) powder samples with x = 0%, 0.5%, 1%, 2.5%, 5% and 10% were synthesized by the polymeric precursors method. The thermal, structural and optical properties of STM samples heat-treated at different temperatures were analyzed by thermal analysis, X-ray diffraction, X-ray absorption spectroscopy and photoluminescence techniques. The thermal analysis results have shown that manganese ion causes a retarding effect, increasing the onset of the crystallization temperature. The XRD results showed that manganese ion is incorporated in a solid solution in the B site of the SrTiO3 (ST) network for the range of solubility studied, with oxidation states between +3.4 and +3.7, indicating the creation of charge compensation defects, keeping the materials electrical neutrality. The analysis of the photoluminescence (PL) spectra of the STM amorphous samples showed that the PL intensity increases when the amount of manganese is up to 1%. However, higher manganese concentrations leads to a pronounced decrease of the photoluminescence intensity. The amorphous samples showed no significant change of the local order around the titanium atoms, observed as well as in the oxidation state of the manganese atoms as the amount of manganese increases. Thus, the variation of the photoluminescence intensity cannot be explained by these factors. Increasing the calcination temperature leads to a significant decrease of the photoluminescence intensity. An analysis of the XANES spectra measured at the titanium K edge of these samples showed that as the calcination temperature increases, i. e., as it increases the degree of crystallinity, the ordering of the Ti atoms in the oxygen octahedra TiO6 of the samples increases.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-02-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.