Tesis Doctoral
DOI
10.11606/T.18.2014.tde-24102014-010405
Documento
Autor
Nombre completo
Fábio Augusto de Souza Ferreira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2014
Director
Tribunal
Rodrigues Filho, Ubirajara Pereira (Presidente)
Chinaglia, Dante Luis
Eckert, Hellmut
Ionashiro, Massao
Jafelicci Junior, Miguel
Título en portugués
Desenvolvimento de materiais híbridos baseados em poliimida
Palabras clave en portugués
HPW
Materiais dielétricos
Materiais híbridos
ORMOSIL
Poliimida
Revestimento anticorrosivo
Resumen en portugués
Nesse trabalho são discutidos os resultados a respeito de materiais híbridos baseados na poliimida, PI, obtida por reações de policondensação entre a diamina 4,4'-Oxidianilina (ODA) e o dianidrido 4,4'-Oxidiftálico (ODPA), seguida de imidização térmica. O estudo foca na influência do tempo de tratamento (1, 15 e 60 min) e na temperatura de decomposição térmica (500°C) sobre as propriedades da PI. Os experimentos foram realizados sob fluxo de Argônio e os materiais obtidos apresentam características intermediárias entre PI e materiais carbonáceos. Dados de Nanoindentação (NI) revelaram aumento de até 50% de dureza para os filmes tratados por 60 min. ODPA e ODA serviu ainda de base para a preparação do revestimento híbrido contendo ORMOSIL gerado in situ por catálise ácida via processo sol-gel a partir do (3-aminopropil)trietóxissilano (APTES) e Tetraetil Ortossilicato (TEOS). O revestimento obtido é homogêneo e tem boa interação com o substrato (aço inoxidável 316L). A polarização potenciodinâmica revelou uma proteção elevada tanto em solução de NaCl 3,5% em massa quanto em H2SO4 0,5 mol L-1, em relação ao aço sem revestimento, com densidade de corrente da ordem de 10-9 A cm-2, na faixa de -700 a 500 mV vs Ag/AgCl. Por fim, filmes híbridos baseados em ODPA, ODA, APTES e TEOS, adicionados de Ácido Fosfotungstico (HPW) foram preparados e avaliados por Espectroscopia na região do Infravermelho com Transformada de Fourier e Ressonância Magnética Nuclear de Silício e Fósforo (29Si e 31P MAS NMR) que confirmaram a formação da PI e da rede ORMOSIL, bem como revelam que a estrutura do HPW permaneceu intacta após o processo de síntese. Mapeamentos realizados por Micro-fluorescência de Raios X assistida por Luz Síncrotron (μ-XRF) mostram uma boa dispersão da fase inorgânica (ORMOSIL e HPW) na orgânica (POO), e todos os materiais são termicamente estáveis até aproximadamente 500°C, de acordo com as curvas obtidas por Termogravimetria (TGA). Outras técnicas de caracterização também foram usadas para uma investigação mais detalhada dos materiais.
Título en inglés
Development of hybrid materials based on polyimide
Palabras clave en inglés
Anticorrosive coating
Dielectric materials
HPW
Hybrid materials
ORMOSIL
Polyimide
Resumen en inglés
In this thesis are presented the results and considerations related to several hybrid materials derived from the polyimide, PI, obtained by polycondensation reactions between 4,4'-Oxydianiline (ODA) and 4,4'-Oxydiphthalic (ODA), followed by thermal imidization. The study focuses on the effect of thermal treatment time (1, 15 and 60 min) and the temperature of beginning of thermal decomposition (773 K) on the properties of PI. The experiments were performed under Argon flow, and the materials presented intermingled properties of PI and carbonaceous materials. The hardness, evaluated by Nanoindentation (NI), reached an increase of 50% for POO films treated for 60 min. POO was also used for the preparation of the hybrid coating containing ORMOSIL obtained in situ by acid catalysis via sol-gel process from (3-aminopropyl)triethoxysilane (APTES) and Tetraethyl Orthosilicate (TEOS). The coating is homogeneous and present a good interaction with the substrate (316L stainless steel). Data of potendynamic polarization revealed a high protection both under NaCl 3.5 wt% and H2SO4 0.5 mol L-1 solutions related to the neat substrate, with current density of order 10-9 A cm-2, in range potential of -700 to 500 mV vs Ag/AgCl. Finally, hybrid films were prepared based on ODPA, ODA, APTES and TEOS, in addition to Phosphotungstic Acid (HPW). The characteristics of all materials were evaluated by Fourier Transform Infrared Spectroscopy in Middle and Near Infrared region (FTMIR and FTNIR), and Magic Angle Spinning-Nuclear Magnetic Resonance of Silicon 29 and Phosphorus 31 (29Si and 31P MAS NMR) which confirmed the ORMOSIL network formation, as well as revealed that the HPW structure remained intact after the synthesis process. Mapping performed by Assisted Synchrotron Light X-ray Micro Fluorescence (μ-XRF) the good dispersion of the inorganic phase (ORMOSIL and HPW) in the organic phase (POO). All materials are thermally stable up to 773 K, according to Thermogravimetric Analysis (TGA). Other techniques of characterization were also used to further investigation of the materials.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-11-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.