Disertación de Maestría
DOI
10.11606/D.18.2015.tde-22092015-105627
Documento
Autor
Nombre completo
Sabrina Nicoleti Carvalho dos Santos
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2015
Director
Tribunal
Gonçalves, Débora (Presidente)
Gonçalves, Raquel
Lahr, Francisco Antonio Rocco
Título en portugués
Análise estrutural e de superfície de madeiras submetidas a tratamento térmico e degradadas pelo fungo Pycnoporus sanguineus
Palabras clave en portugués
Análise dinâmico-mecânica
Ângulo de contato
Madeira
Raios X
Tratamento térmico
Resumen en portugués
Neste trabalho, analisou-se como o tratamento térmico e a degradação pelo fungo de podridão branca influenciaram as propriedades dos componentes das amostras de madeira das espécies Araucaria sp., Pinus sp., Erisma sp. e Hymenaea sp.. Essas amostras foram cortadas em diferentes planos de corte e submetidas inicialmente a um teor de umidade de equilíbrio de 12%. As caracterizações das amostras foram realizadas empregando a técnica de ângulo de contato, medidas de perda de massa (somente para amostras degradadas pelo fungo), a análise dinâmico-mecânica (DMA) e difração de raios X. Para as amostras degradadas pelo fungo, o valor de perda de massa foi maior para a espécie Pinus sp. e menor para Hymenaea sp.. Os difratogramas de raios X apontaram que o corte transversal apresentou um caráter mais amorfo em relação ao corte longitudinal. As medidas de ângulo de contato mostraram que com o aumento da temperatura de tratamento térmico a superfície se tornou mais hidrofóbica. O mesmo comportamento foi verificado para amostras submetidas à degradação pelo fungo. De forma que, tanto o tratamento térmico quanto a degradação pelo fungo, ocasionaram um aumento de grupos não-polares presentes na superfície. Já nas medidas de DMA foi observado que o módulo de armazenamento (E') diminuiu com o aumento da temperatura. E o grau de mobilidade das cadeias poliméricas foi analisado por meio das temperaturas de transições vítreas das hemiceluloses e lignina (Tg), bem como, as relaxações secundárias através do fator de perda (tan δ). Esses resultados possibilitam uma maior elucidação sobre como o tratamento térmico e a degradação fúngica afetam diferentes tipos de amostras de várias espécies de madeira, essas informações são relevantes para a utilização e preservação dessas madeiras.
Título en inglés
Structural analysis and surface of wood heat-treated and degraded by the fungus Pycnoporus sanguineus
Palabras clave en inglés
Contact angle
Dynamic-mechanical analysis
Heat treatment
Wood
X-ray
Resumen en inglés
The present dissertation addresses the analysis of the influence of heat treatment and degradation by white rot fungus on the properties of the components of wood species Araucaria sp., Pinus sp., Erisma sp. and Hymenaea sp. Samples were cut at different cutting plans and initially subjected to a 12% equilibrium moisture content. They were then characterized by a contact angle technique, weight loss measurements (for samples degraded by the fungus), dynamic mechanical analysis (DMA) and X-ray diffraction. The mass loss values of samples degraded by the fungus were higher for Pinus sp. and lower for Hymenaea sp. The X-ray diffraction showed the transversal cut had an amorphous character in relation to the longitudinal cut. According to the contact angle measurements, showed that with increasing heat treatment temperature over the surface became hydrophobic. The same behavior was observed for samples submitted to degradation by fungus. In order, that both heat treatment and degradation by the fungus, caused an increase of non-polar groups on the surface. The DMA measurements showed the storage modulus (E') decreases with increasing temperature. The degree of mobility of the polymer chains was analyzed through glass transition temperatures of hemicelluloses and lignin (Tg) and the secondary relaxations were assessed through the loss factor (tan δ). The results enabled greater elucidation on how the heat treatment and fungal degradation affect different types of samples of various wood species. Such information is relevant for the use and preservation of woods.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-09-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.