Disertación de Maestría
DOI
10.11606/D.18.2017.tde-20102017-101959
Documento
Autor
Nombre completo
Danielle Camargo Gimenes
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2017
Director
Tribunal
Chinelatto, Marcelo Aparecido (Presidente)
Ambrósio, José Donato
Bettini, Sílvia Helena Prado
Título en portugués
Avaliação de comportamento térmico, morfológico e mecânico de blendas de PLA/PCL compatibilizadas por copolímero em bloco de baixa massa molar
Palabras clave en portugués
Blendas poliméricas
Compatibilização não-reativa
Copolímero em bloco
Pol(ε-icaprolactona)
Poli(ácido láctico)
Resumen en portugués
O poli(ácido láctico) (PLA) é um polímero biodegradável, biocompatível e bioabsorvível proveniente de fontes renováveis. Constitui uma excelente alternativa sustentável para substituição dos polímeros provenientes de petróleo, atualmente dominantes no mercado industrial. Apesar das vantagens, o PLA tem baixa tenacidade e reduzida elongação na ruptura a temperatura ambiente, o que torna a sua utilização limitada em usos que necessitem de alta deformação plástica em níveis de exigência mecânicos elevados. Misturas mecânicas de PLA com polímeros altamente flexíveis, como é o caso da poli(ε-caprolactona) (PCL), podem resultar em novos materiais com propriedades mecânicas adequadas para diferentes aplicações. Blendas PLA/PCL são completamente imiscíveis, sendo seu comportamento mecânico altamente dependente da interação interfacial entre os componentes da blenda. Portanto, o objetivo desse trabalho é avaliar o efeito compatibilizante de um copolímero em bloco de baixa massa molar (2000 g mol-1) derivado de ε-caprolactona e policarbonato (C2) e, disponível comercialmente em blendas imiscíveis PLA/PCL. Blendas binárias e ternárias foram preparadas por mistura mecânica no estado fundido via processo de extrusão em rosca simples. O teor de PLA nas blendas foi de 75, 50 e 25% (em massa) e a concentração do copolímero de 0, 1, 3, 5 e 7% (em massa). O comportamento térmico, morfológico e mecânico das blendas compatibilizadas e não compatibilizadas foi avaliado por Calorimetria Exploratória Diferencial (DSC), Análise Termodinâmico-Mecânica (DMTA), Microscopia Eletrônica de Varredura (MEV) e ensaios de tração, flexão e impacto Izod. Os resultados de DSC e DMTA indicaram que o copolímero provocou pequena redução na temperatura de transição vítrea (Tg) do PLA, sugerindo que o C2 é solúvel no PLA. Entretanto, nas micrografias das superfícies de fraturas do PLA foi nítida a presença de pequenas micelas formadas pelo copolímero em bloco, indicando que há um limite de solubilidade do compatibilizante na fase de PLA. Os resultados obtidos em tração mostraram que com o aumento do teor de compatibilizante, a tensão no escoamento, a tensão na ruptura e o módulo elástico das blendas sofrem alterações. A propriedade de tenacidade, avaliada no ensaio de impacto Izod, mostrou que as blendas tiveram um ganho na resistência quando comparadas com o PLA puro. Os resultados mostraram que o copolímero em bloco derivado de ε-caprolactona e policarbonato alifático pode atuar como compatibilizante para blendas PLA/PCL
Título en inglés
Behavioral assessment of thermal behavior, morphological and mechanical behavior of biodegradeble blends PLA/PCL blends compatibilized by low molar mass block copolymer
Palabras clave en inglés
Block copolymer
Non-reactive compatibilization
Poly(ε-caprolactone)
Poly(lactic acid)
Polymeric blends
Resumen en inglés
Poly(lactic acid) (PLA) is a biodegradable, biocompatible and bioabsorbable polymer from renewable sources. It is an excellent sustainable alternative for replacing petroleum polymers, currently dominant in the industrial market. Despite the advantages, PLA has low toughness and reduced elongation at room temperature, which makes its use limited in uses that require high plastic deformation under high mechanical stress levels. Mechanical mixtures of PLA with highly flexible polymers, such as poly(ε-caprolactone) (PCL), may result in new materials with mechanical properties suitable for different applications. PLA/PCL blends are completely immiscible, and their mechanical behavior is highly dependent on the interfacial interaction between the components of the blend. Therefore, the objective of this work is to evaluate the compatibilizing effect of a low molar mass block copolymer (2000 g mol-1) derived from ε-caprolactone and polycarbonate (C2) and commercially available in PLA/PCL immiscible blends. Binary and ternary blends were prepared by mechanical mixing in the melted state via single-screw extrusion process. The content of PLA in the blends was 75, 50 and 25% (% by mass) and the copolymer concentration was 0, 1, 3, 5 and 7% (% by mass). The thermal, mechanical and morphological behavior of compatibilized and non-compatibilized blends was evaluated by differential scanning calorimetry (DSC), thermodynamic-mechanical analysis (DMTA), scanning electron microscopy (SEM), tensile test, flexion test, and Izod impact. The results of DSC and DMTA indicated that the copolymer caused a small reduction in the glass transition temperature (Tg) of PLA, suggesting that C2 is soluble in PLA. However, in the micrographies of the fracture surfaces of the PLA the presence of small micelles formed by the block copolymer is clear, indicating that there is a limit of solubility of the compatibilizer in the PLA phase. The results obtained in a tensile test showed that with the increase of the compatibilizing content, the tension in the flow, the tension at rupture and the elastic modulus of the blends undergo changes. The tenacity property, evaluated in the Izod impact test, showed that the blends had a gain in resistance when compared to pure PLA. The results showed that block copolymer derived from ε-caprolactone and aliphatic polycarbonate can act as a compatibilizer for PLA/PCL blends.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-10-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.