Tesis Doctoral
DOI
10.11606/T.18.2014.tde-16112015-161700
Documento
Autor
Nombre completo
Lucíola Lucena de Sousa
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2015
Director
Tribunal
Salomão, Rafael (Presidente)
Cabrelon, Marcelo Dezena
Fortulan, Carlos Alberto
Marcomini, Raphael Fortes
Morelli, Márcio Raymundo
Título en portugués
Desenvolvimento e caracterização de cerâmicas porosas moldáveis à base de alumina-mulita para uso como isolamento térmico em altas temperaturas
Palabras clave en portugués
Alumina
Cerâmicas porosas
Hidróxido de alumínio
Mulita
Sinterização
Resumen en portugués
Com o objetivo de reduzir o consumo energético, tem crescido o uso de cerâmicas porosas refratárias como isolantes térmicos para altas temperaturas. Entre as técnicas comumente empregadas na produção desses materiais, destaca-se aquela baseada na geração de poros por meio de transformação de fases. Esse método, que não libera voláteis tóxicos, apresenta uma importante limitação em relação ao uso prolongado em altas temperaturas: os compostos de transição formados após a desidroxilação tendem a acelerar a sinterização, reduzindo a porosidade. É bastante conhecido o fenômeno de que, durante a sinterização em temperaturas elevadas, peças de alumina com alta porosidade, sofrem a eliminação progressiva dos poros presentes. Por essa razão, compostos que dificultam a densificação das peças porosas têm sido adicionados para manter a porosidade originada pela decomposição do hidróxido de alumínio. O objetivo desse trabalho foi obter cerâmicas porosas moldáveis a partir de alumina, hidróxido de alumínio e diversas fontes de sílica (mulita eletrofundida, quartzo e microssílica), utilizando a técnica de decomposição de hidróxidos com o intuito de se formar mulita, composto capaz de diminuir a taxa de densificação em altas temperaturas e com aplicações na indústria petroquímica e do alumínio. As amostras foram sinterizadas entre 1100ºC e 1500ºC e os resultados mostraram que houve aumento da resistência mecânica com a elevação do teor de mulita eletrofundida, quartzo e microssílica incorporada ao sistema. Além disso, o sistema mulita eletrofundida para a composição 0,4-SMT apresentou uma PT = 53,58%, módulo elástico e resistência a compressão (E = 13,03 GPa e σR = 16,83 MPa). O sistema com a adição de quartzo, a amostra 0,2-SQZ, teve pequenas mudanças nos níveis de porosidade (PTG = 59,50%) e não apresentou um elevado aumento do módulo elástico e da resistência a compressão (E = 6,51 GPa e σR = 13,91 MPa) e o sistema contendo microssílica a composição 0,2-SMS apresentou os melhores resultados, tendo um ganho de propriedades mecânicas em temperaturas a 1100ºC e a 1500ºC manteve a porosidade (PTG = 56,23%), reduziu o tamanho médio de poros e apresentou também ótimas propriedades mecânicas (E= 15,39 GPa e σR = 36,79 MPa) proporcionando sua atuação como isolante térmico.
Título en inglés
Development and characterization of castable porous ceramics based on alumina-mullite for use as thermal insulation in high temperature
Palabras clave en inglés
Alumina
Aluminum hydroxide
Mullite
Porous ceramic
Sintering
Resumen en inglés
Refractory porous ceramics have largely been used as thermal insulators for high temperatures aiming to reduce energy consumption. The generation of pores through phase transformation (such as Al(OH)3 dehydroxilation) is one of the most interesting techniques employed to produce such materials. This method, which does not release toxic volatile, imposes an important limitation on the prolonged use at high temperatures. The transition compounds formed after the dehydroxylation tend to accelerate sintering and reduce porosity. It is well known that during sintering at high temperatures (above 1100ºC), parts of alumina with high porosity amounts undergo gradual pores' elimination. Therefore, compounds that hinder densification of porous pieces have been added to these compositions in order to maintain the porosity generated by the decomposition of aluminum hydroxide. This thesis addresses the production of castables porous ceramics from alumina, aluminum hydroxide and different sources of silica (electrofuse mullite, quartz and microsilica), employed for the in situ formation of mullite, a compound that reduces the rate of densification at high temperatures. The applications include petrochemical and aluminum industries. Samples were sintered between 1100ºC and 1500ºC and the results of the systems which contained electrofused mullite, quartz and microsilica showed less intense porosity levels reduction. The system with addition of electrofused mullite showed PTG = 53,58%,E = 13,03 GPa and σR = 16,83 MPa. The system containing quartz, presented a lower change of porosity (PTG = 59,50%) and the system containing microsilica provided the best results and an increment in the mechanical properties at temperatures between 1100°C and 1500°C. This last system also kept porosity (PTG = 56,23%), and reduced the average pore size. Its good mechanical properties (E = 15,39 GPa and σR = 36,79 MPa) proved it can be used as a thermal insulator.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Luciolatese.pdf (10.64 Mbytes)
Fecha de Publicación
2015-11-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.