Tesis Doctoral
DOI
10.11606/T.18.2017.tde-15092017-083621
Documento
Autor
Nombre completo
Bárbara Branquinho Duarte
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2017
Director
Tribunal
Lahr, Francisco Antonio Rocco (Presidente)
Bertolini, Marília da Silva
Chahud, Eduardo
Govone, José Silvio
Teixeira, Ronaldo Soares
Título en portugués
Influência de componentes químicos em propriedades mecânicas da madeira
Palabras clave en portugués
Celulose
Cinzas
Extrativos
Hemicelulose
Lignina
Porosidade
Propriedades físico-mecânicas
Resumen en portugués
A madeira é muito empregada em diferentes campos, dentre os principais tem-se a construção civil, visto que a relação entre resistência mecânica e densidade, para a madeira, é das mais altas no caso dos materiais empregados na construção civil. Neste sentido, o Brasil se encontra em posição favorável, pois já dispõe diversas áreas certificadas para extração de madeiras, no âmbito da Floresta Amazônica. A fim de obter as melhores respostas na utilização desse material, necessita-se de sua completa caracterização. Entretanto, com a anisotropia e a heterogeneidade da madeira, muitas propriedades devem ser determinadas, o que exige equipamentos específicos, técnicos especializados e, por conseguinte, o tempo despendido é considerável. Neste contexto, é urgente a definição de procedimentos que tornem mais expedita e igualmente confiável a caracterização. No presente estudo foi avaliada, de forma inédita, a possibilidade de propriedades físico-mecânicas da madeira se relacionar com parâmetros como porosidade, densidade aparente e componentes químicos (celulose, hemicelulose, lignina, extrativos e cinzas). Foram caracterizadas dez espécies tropicais de madeira, por meio dos ensaios descritos no Anexo B da Norma ABNT NBR 7190/1997. Os componentes químicos foram determinados pelo método Klason modificado, a partir da norma TAPPI T-222 om-02, e a porosidade pela intrusão de mercúrio. A partir dos resultados, foram aplicados modelos de regressão multivariadas, dos quais se obtiveram equações para estimar cada propriedade a partir das diversas variáveis fixas (densidade aparente, porosidade e componentes químicos). Nas relações encontradas verificaram-se ótimos resultados como, por exemplo, a equação que estima a resistência à compressão paralela às fibras (fc0) levou a R² 99,69%. Deste modo, a hipótese inicial se confirmou, o que possibilita a estimativa confiável das propriedades estudadas com os parâmetros citados.
Título en inglés
Influence of chemical components on mechanical properties of wood
Palabras clave en inglés
Ash
Cellulose
Extractives
Hemicellulose
Lignin
Physical-mechanical properties
Porosity
Resumen en inglés
Wood is a very used material in different fields, among them civil construction can be highlighted, since the relation between mechanical strength and density for wood is the highest in the case of building materials. In this sense, Brazil is in a favorable position, as it already has several areas certified for timber extraction, within the Amazon Forest. In order to obtain the best responses in the use of this material, its complete characterization is required. However, due to wood anisotropy and heterogeneity, many properties must be determined, which requires specific equipment sets, technical expertise and therefore time spent is considerable. In this context, it is urgent to devise procedures that make more expeditious and equally reliable the wood characterization. In the present study, it was considered the possibility of wood physical-mechanical properties can be estimated in an unprecedented way, based on parameters such as porosity, chemical components (cellulose, hemicellulose, lignin, extractives and ash) and density. Ten tropical wood species were characterized by tests described in Annex B of ABNT NBR 7190/1997. Chemical components were determined by the modified Klason method, from TAPPI standard T-222 om-02 and the porosity by the intrusion of mercury. To the results, multivariate regression models were applied and equations were obtained to estimate each property from the several fixed variables (apparent density, porosity and chemical components). Very great results were reached from these relationships, for example, the equation that estimates strength in compression parallel to the grain (fc0) led to R² 99.69%. Thus, the initial hypothesis was confirmed, which allows the reliable estimation of the studied properties with the mentioned parameters.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-09-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.