Disertación de Maestría
DOI
https://doi.org/10.11606/D.18.2020.tde-13082020-142934
Documento
Autor
Nombre completo
Luiz Gonzaga Martins Júnior
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2020
Director
Tribunal
Oliveira, Marcelo Falcão de (Presidente)
Coury, Francisco Gil
Zepon, Guilherme
Título en portugués
Fases de alta entropia com menor densidade combinando metais refratários com Al e Ti
Palabras clave en portugués
ligas de alta entropia
ligas metálicas
refratários
Resumen en portugués
Ligas de alta entropia têm apresentado um grande potencial de aplicação em diversos setores da indústria. Dentre estes, o setor aeroindustrial em especial tem sido um grande motivador para produção de ligas de alta entropia refratárias que superam as ligas convencionais em condições de alta temperatura. No entanto, apesar de ser um campo que tem se expandido rapidamente, ainda existem muitas possibilidades de composições química, para novas ligas não exploradas. Neste contexto, o presente trabalho propôs-se a identificar possíveis fases de alta entropia formadas em sistemas de ligas refratárias que apresentam potencial para formulação de ligas de menor densidade combinando metais refratários (Nb, Zr, Hf, Mo e Cr) com Al e Ti. A produção das ligas foi realizada por meio de fusão por arco elétrico. A difração de raios X (DRX) foi utilizada para determinação das estruturas cristalinas em busca do sistemas cristalinos CCC em conjunto com dados de espectroscopia por dispersão de energia (EDS), usados para encontrar composições químicas que resultassem em uma entropia configuracional maior que 1,5R (sendo R a constante universal dos gases). Como resultado, cinco fases, das quais quatro ainda não reportadas na literatura, atenderam os critérios de classificação para fases CCC de alta entropia. As novas fases descobertas servem como base para a formulação de novas ligas e comprovam a efetividade da metodologia empregada em sua busca.
Título en inglés
High entropy alloys production
Palabras clave en inglés
high entropy alloys
metallic alloys
refractory
Resumen en inglés
High entropy alloys have been presenting a great potential for many industrial applications. Among these, aerospace industry has been a great motivator for refractory high entropy alloys production that overcome conventional alloys in high temperature applications. Although this research field has been presenting an accelerated expansion, there is a great number of unexplored chemical composition possibilities. The purpose of this work was to identify potential high entropy phases forming from refractory metals (Nb, Zr, Hf, Mo, Cr) with lower density by combining them with Al and Ti. The alloys were manufactured by arc melting. X-ray diffraction (XRD) was used to identify the crystalline structures for searching bcc systems. Energy dispersive spectroscopy (EDS) was used to identify the phases whose the chemical compositions results in a configurational entropy of, at least, 1.5R (R is the universal gas constant). As result, five bcc phases meet such criteria. Among these, four haven't yet been reported in the literature. These new phases can be used as a refence for the production of new refractory high entropy alloys with lower density.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2021-06-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.