Master's Dissertation
DOI
10.11606/D.18.2016.tde-12032015-151858
Document
Author
Full name
Bruno Roberto Spirandeli
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2013
Supervisor
Committee
Casteletti, Luiz Carlos (President)
Arantes, Vera Lúcia
Farah, Alessandro Fraga
Title in Portuguese
Influência da adição de NbC e Al2O3+TiO2 nos desempenhos de revestimentos a base de Ni-Al produzidos por aspersão térmica
Keywords in Portuguese
Al2O3+TiO2
Aspersão térmica
Compósitos Ni-Al
Desgaste
NbC
Abstract in Portuguese
Aspersão térmica é um processo de produção de revestimentos metálicos, poliméricos, cerâmicos ou compósitos sobre superfícies previamente preparadas que objetiva na maioria das vezes a prevenção contra o desgaste e/ou corrosão e também a recuperação dimensional de superfícies desgastadas. Ligas de Ni-Al são extensivamente empregadas na aspersão térmica para reconstrução dimensional e como camada de ligação como materiais que não se ligam adequadamente à superfície a ser revestida. A baixa dureza e resistência ao desgaste (principalmente em aplicações de reconstrução dimensional) desta liga poderiam ser contornadas pela adição de partículas ou compostos de altas durezas na matéria prima em pó antes da aspersão. Neste trabalho avaliou-se a influência da adição de NbC e do composto cerâmico Al2O3+TiO2 no desempenho ao desgaste de revestimentos de Ni-Al, bem como verificou-se as alterações microestruturais, químicas, e mecânicas decorrentes. Para tanto se adicionou 25%p de NbC ou 25%p do composto Al2O3+TiO2 à liga base de Ni-Al, formando-se dois materiais compósitos: Ni-Al + NbC e Ni-Al + (Al2O3+TiO2). Utilizou-se microscópio eletrônico de varredura com EDS para caracterizar as matérias primas e os revestimentos produzidos, assim como determinar o mecanismo de desgaste nos ensaios de micro-abrasão tipo "esfera-livre" e "esfera-fixa". Mediram-se as durezas superficiais e as microdurezas das fases por meio dos ensaios Rockwell Superficial e microdureza Vickers. Avaliou-se a resistência ao desgaste por meio de ensaios de micro-abrasão nas modalidades "esfera-livre" e "esfera-fixa". As adições dos materiais citados na liga a base de níquel alteraram características microestruturais importantes, como aumento do percentual de óxidos, bem como a composição química e distribuição dos elementos nas camadas formadas; ocorreram também aumentos significativos das durezas e nas resistências ao desgaste dos revestimentos.
Title in English
Influence of addition of Al2O3+TiO2 and NbC coatings on the performance of the Ni-Al base produced by thermal spraying
Keywords in English
Al2O3+TiO2
Composites Ni-Al
NbC
Thermo spray
Wear
Abstract in English
Thermo Spray is a metallic, polymeric, ceramic and composite coating process applied over a previously prepared surface usually seeking to improve wear and/or corrosion resistance. It is also used to repair worn surfaces restoring the original dimensions. Ni-Al alloys are used as a primer coating to promote the adhesion between surface and incompatible coatings and also extensively in the reconstruction of worn surfaces. The low hardness and wear resistance (when used in reconstruction applications) of this alloy could be improved by the addition of hard particles/composites to the powdered raw material prior to the spray operation. In this work the influence of NbC and Al2O3+TiO2 additions to Ni-Al alloys were evaluated concerning wear performance and the resulting changes in microstructure, chemical and mechanical behavior. The experimental procedure included the preparation of samples of the Ni-Al base alloy with additions of 25wt% of NbC or 25wt% of Al2O3+TiO2, what resulted in two different sprayed composite materials: Ni-Al + NbC e Ni-Al + (Al2O3+TiO2). SEM with EDS microprobe was used to characterize the raw materials, the sprayed coating samples and the type of wear mechanism occurring in the wear tests of the type "free sphere" and "fixed sphere" micro abrasion that were used to evaluate the wear resistance of the samples. Surface hardness and micro hardness of the different phases in the coatings were evaluated using Rockwell and Vickers micro hardness testing machines respectively. The addition of the hard phases promoted important changes in the Ni-Al base alloy, decreasing the porosity level and increasing the percentage of oxides. Hardness were significantly increased as well as the wear resistance of the coatings.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Dissertacao.pdf (8.16 Mbytes)
Publishing Date
2016-08-24
 
WARNING: Learn what derived works are clicking here.