Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.18.2020.tde-04022020-144127
Document
Auteur
Nom complet
Renan Freire de Carvalho Lopes Rocha
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2019
Directeur
Jury
Oliveira, Marcelo Falcão de (Président)
Coury, Francisco Gil
Marcomini, José Benedito
Titre en portugais
Efeito da micro-adição de Y na liga Zr52,5Cu17,9Ni14,6Al10Ti5 (VIT105)
Mots-clés en portugais
Microligante
Oxigênio
Vidros metálicos
Zr52,5Cu17,9Ni14,6Al10Ti5 (VIT105)
Resumé en portugais
A microestrutura amorfa obtida em ligas metálicas resfriadas rapidamente garante propriedades interessantes se comparadas às ligas convencionais cristalinas. Ligas amorfas baseadas em zircônio são muito sensíveis às contaminações por oxigênio, impedindo sua vitrificação. Este trabalho estudou o efeito do ítrio como elemento micro ligante. O ítrio foi adicionado em teores estequiométrico em relação aos níveis de oxigênio presentes na liga Zr52,5Cu17,9Ni14,6Al10Ti5 (VIT105). As amostras foram produzidas por fusão a arco sob atmosfera controlada de argônio, em molde de cobre resfriado à água e dimensões de 5 e 6 mm de diâmetro. Os teores de oxigênio foram estabelecidos em 600, 800, 1300, 2000 e 3000 ppm, em peso. A tendência de formação vítrea (TFV) foi comparada entre amostras com e sem adição de ítrio como micro ligante. Os teores de oxigênio foram monitorados pelo método de fusão em gás inerte. A fração de fase amorfa foi quantificada por análise de imagens de microscopia óptica. Difração de raios-X foi utilizada para identificação de fases cristalinas e verificação de fase amorfa. Microscopia eletrônica de varredura, com espectroscopia por dispersão de energia, possibilitaram a observação das fases formadas e sua identificação. O ítrio se mostrou muito eficaz em aumentar a TFV da liga, mesmo tendo sido adicionado em pequenas quantidades (< 1% at.). O elemento microligante foi capaz de capturar o oxigênio da liga permitindo maior obtenção de fração de fase amorfa em todos os níveis de oxigênio. O oxigênio ligado ao ítrio forma seu óxido estável, Y2O3, e este, por sua vez, não interfere na formação do vidro. A abordagem utilizada foi muito eficaz, indicando ser uma alternativa viável para o aumento da tendência à formação de vidro em ligas baseadas em Zr, sem a necessidade de altos níveis de pureza (< 200 ppm) da matéria prima em relação ao oxigênio.
Titre en anglais
Effect of minor Y addition in Zr52,5Cu17,9Ni14,6Al10Ti5 (VIT105) amorphous alloy
Mots-clés en anglais
Metallic glass
Micro alloying
Oxygen
Zr52,5Cu17,9Ni14,6Al10Ti5 (VIT105)
Resumé en anglais
Amorphous microstructure obtained in metallic alloys rapidly quenched ensure interesting properties when compared to conventional alloys. Amorphous alloys based on zirconium are very sensitive to oxygen contamination, avoiding their vitrification. This dissertation studied the effect of yttrium as micro alloying element. Yttrium was added based on stoichiometric content regarding the amount of oxygen present in Zr52,5Cu17,9Ni14,6Al10Ti5 (VIT105) alloy. The samples were produced by arc fusion under controlled argon atmosphere. Casting in a copper mold cooled by water with a diameters of 5 and 6 mm. The oxygen contents were set in 600, 800, 1300, 2000, 3000 ppm, by mass. The glass forming ability (GFA) was compered among the samples with and without the addition of yttrium as micro alloying. The contents of oxygen were monitored by inert gas fusion method. Amorphous phase fraction was quantified by image analysis with optical micrographs. X-ray diffraction was used to verify the presence of crystalline and amorphous phases. Scanning electron microscopy and energydispersive X-ray spectroscopy enabled the observation of the phases formed and their identification. Yttrium was effective in enhancing the alloy GFA, even in small content (< 1%). The micro alloying element could scavenge the oxygen present in the alloys making possible obtaining large amount of amorphous phase in all oxygen levels. Oxygen bonds with yttrium forming its stable oxide, Y2O3, this oxide doesn't interfere in the glass formation. The approach was very effective raising the GFA of Zr-based alloys, without the need of high levels of purity (< 600 ppm) in the raw materials regarding the oxygen contents.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2020-02-17
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.