Thèse de Doctorat
DOI
10.11606/T.18.2013.tde-03122013-223454
Document
Auteur
Nom complet
Paulo Cesar Moselli
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2013
Directeur
Jury
Oliveira, Marcelo Falcão de (Président)
Bolfarini, Claudemiro
Casteletti, Luiz Carlos
Kobayashi, Yukio
Pinto, Haroldo Cavalcanti
Titre en portugais
Desenvolvimento de dispositivo, adaptado à tocha SATG, para a realização de revestimento duro, utilizando ligas, em forma de pó
Mots-clés en portugais
PAT-P

Resistência ao desgaste
Revestimento duro
SATG
Stellite 6
Resumé en portugais
Este trabalho inova a aplicação de revestimentos duros usando o processo de soldagem SATG (Soldagem ao Arco Tungstênio com Atmosfera Gasosa) utilizando ligas, em forma de pó, incorporadas diretamente à poça de solda. Devido à boa resistência ao desgaste, utilizou-se a liga Stellite 6, no substrato SAE 1020. Dados de microdureza Vickers, taxa de deposição, diluição, análise micrográfica e desgaste foram comparados com resultados do PAT-P (Plasma por Arco Transferido-Pó) e permitiram avaliar a técnica proposta. Os resultados mostraram um revestimento pelo processo SATG-pó livre de poros, sem oxidação na superfície e diluição superior, ao processo PAT-P. Porém, o consumo de gás foi menor, devido à redução da vazão do gás de arraste e da não utilização de gás plasma. A análise microestrutural evidenciou uma microestrutura similar, para ambos os processos, mas o processo PAT-P apresentou uma microestrutura mais refinada. Obteve-se, pelo processo SATG-pó semi-automático, microdurezas entre 400 e 500 HV e uma taxa de diluição de 5%, próximas aos valores do processo PAT-P. Quanto ao desgaste, observaram-se valores também bem próximos para os três processos.
Titre en anglais
Development of an adapted device for GTAW torchs to perform hardfacing by applying powdered alloys
Mots-clés en anglais
GTAW
Hardfacing
Powder
PTA-P
Stellite 6
Wear resistance
Resumé en anglais
This work innovates the application of hardfacing by using the welding process GTAW (Gas Tungsten Arc Welding) using alloys in the powder form and directly embedded in the weld pool. Due to the good wear resistance it was used Stellite 6 alloy for hardfacing the substrate SAE 1020. Vickers hardness data, deposition rate, dilution, micrographic analysis and wear results were compared with the PTA-P (Plasma Transferred Arc-Powder) in order to evaluate the proposed technique. The results showed a coating produced by the process GTAW-powder free of pores, without surface oxidation and higher dilution in comparison with the PTA-P process. However, gas consumption was lower due to reduced flow of the carrier gas and as it was not used as plasma gas. Microstructural analysis showed a similar microstructure for both processes, but the PTA-P process presented a more refined microstructure. It was obtained, by the semi-automatic GTAW-powder process, micro hardness between 400 and 500HV and rate dilution of 5%, values close to the PTA-P process. As for the wear it was observed values very close too, for the three process.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-01-06
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.