Tesis Doctoral
DOI
10.11606/T.18.2013.tde-03122013-223454
Documento
Autor
Nombre completo
Paulo Cesar Moselli
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2013
Director
Tribunal
Oliveira, Marcelo Falcão de (Presidente)
Bolfarini, Claudemiro
Casteletti, Luiz Carlos
Kobayashi, Yukio
Pinto, Haroldo Cavalcanti
Título en portugués
Desenvolvimento de dispositivo, adaptado à tocha SATG, para a realização de revestimento duro, utilizando ligas, em forma de pó
Palabras clave en portugués
PAT-P

Resistência ao desgaste
Revestimento duro
SATG
Stellite 6
Resumen en portugués
Este trabalho inova a aplicação de revestimentos duros usando o processo de soldagem SATG (Soldagem ao Arco Tungstênio com Atmosfera Gasosa) utilizando ligas, em forma de pó, incorporadas diretamente à poça de solda. Devido à boa resistência ao desgaste, utilizou-se a liga Stellite 6, no substrato SAE 1020. Dados de microdureza Vickers, taxa de deposição, diluição, análise micrográfica e desgaste foram comparados com resultados do PAT-P (Plasma por Arco Transferido-Pó) e permitiram avaliar a técnica proposta. Os resultados mostraram um revestimento pelo processo SATG-pó livre de poros, sem oxidação na superfície e diluição superior, ao processo PAT-P. Porém, o consumo de gás foi menor, devido à redução da vazão do gás de arraste e da não utilização de gás plasma. A análise microestrutural evidenciou uma microestrutura similar, para ambos os processos, mas o processo PAT-P apresentou uma microestrutura mais refinada. Obteve-se, pelo processo SATG-pó semi-automático, microdurezas entre 400 e 500 HV e uma taxa de diluição de 5%, próximas aos valores do processo PAT-P. Quanto ao desgaste, observaram-se valores também bem próximos para os três processos.
Título en inglés
Development of an adapted device for GTAW torchs to perform hardfacing by applying powdered alloys
Palabras clave en inglés
GTAW
Hardfacing
Powder
PTA-P
Stellite 6
Wear resistance
Resumen en inglés
This work innovates the application of hardfacing by using the welding process GTAW (Gas Tungsten Arc Welding) using alloys in the powder form and directly embedded in the weld pool. Due to the good wear resistance it was used Stellite 6 alloy for hardfacing the substrate SAE 1020. Vickers hardness data, deposition rate, dilution, micrographic analysis and wear results were compared with the PTA-P (Plasma Transferred Arc-Powder) in order to evaluate the proposed technique. The results showed a coating produced by the process GTAW-powder free of pores, without surface oxidation and higher dilution in comparison with the PTA-P process. However, gas consumption was lower due to reduced flow of the carrier gas and as it was not used as plasma gas. Microstructural analysis showed a similar microstructure for both processes, but the PTA-P process presented a more refined microstructure. It was obtained, by the semi-automatic GTAW-powder process, micro hardness between 400 and 500HV and rate dilution of 5%, values close to the PTA-P process. As for the wear it was observed values very close too, for the three process.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-01-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.