Disertación de Maestría
DOI
10.11606/D.18.2018.tde-02032018-082043
Documento
Autor
Nombre completo
Ricardo Gomes Pereira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2013
Director
Tribunal
Casteletti, Luiz Carlos (Presidente)
Canale, Lauralice de Campos Franceschini
Picone, Carlos Alberto
Título en portugués
Caracterização de camadas produzidas por boretação e boretação-PVD nos aços AISI H13 e AISI D2
Palabras clave en portugués
AISI D2
AISI H13
Boretação
Micro desgaste abrasivo
PVD
Resumen en portugués
Neste trabalho foram produzidas camadas de boretos de elevadas durezas e resistências ao desgaste nos aços AISI H13 e AISI D2, por meio de tratamento termo-reativo em banho de bórax com adição de 10% de alumínio. Posteriormente foram realizados tratamentos pela técnica PVD sobre as camadas de boretos. As amostras foram caracterizadas por meio de microscopia óptica, microscopia eletrônica de varredura, ensaios de dureza e ensaios de micro desgaste abrasivo com esfera livre. Para ambos os materiais, os tempos de tratamento de boretação foram de 4 horas, seguido de resfriamento em óleo ou ao ar. As camadas produzidas por boretação no caso do aço AISI H13 apresentaram espessura média de 70 μm e para o aço AISI D2 espessura média de 100 μm. As durezas das camadas de boretos produzidas variaram de 1500 a 1700 HV. Os ensaios de micro desgaste abrasivos com esfera livre foram realizados com uso de solução abrasiva de carboneto de silício. Todas as camadas produzidas apresentaram resistências ao desgaste muito superiores as dos substratos. As amostras com tratamentos duplex boretação-PVD apresentaram os melhores desempenhos ao desgaste, seguidas pelo aço AISI D2 e AISI H13 boretados e por último os aços AISI D2 e AISI H13 temperados e revenidos.
Título en inglés
Characterization of layers produced by PVD-boriding and boriding on AISI H13 and AISI D2 steels
Palabras clave en inglés
Abrasive
AISI D2
AISI H13
Boronizing
Micro-wear
PVD
Resumen en inglés
Borides layers with high hardness and wear resistances were produced on AISI H13 and AISI D2 steels by thermo-reactive treatment in borax added with 10% of aluminum. Subsequently, treatments by the PVD technique were performed on the layers of borides. The samples were characterized using Optical Microscopy, Scanning Electron Microscopy, hardness testing and free-ball micro abrasive wear test. For both materials, the boriding treatment times were 4 hours long, followed by cooling in oil or air. In the case of AISI H13, the layers produced by boriding showed an average thickness of 70 μm while AISI D2 steel presented an average thickness of 100 μm. The hardness of the produced boride layers ranged from 1500 to 1700 HV. The micro abrasive wear tests were performed using abrasive solution of silicon carbide. All produced layers showed wear resistance much higher than the substrates. Samples with treatments duplex PVD-boriding presented the best wear performances, followed by AISI D2 and AISI H13 borated steels and finally, AISI D2 and AISI H13 steels quenched and tempered.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-03-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.