Disertación de Maestría
DOI
10.11606/D.18.2008.tde-19012011-103534
Documento
Autor
Nombre completo
Jen Po Wang
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2008
Director
Tribunal
Oliveira, Joao Fernando Gomes de (Presidente)
Jasinevicius, Renato Goulart
Machado, Alisson Rocha
Título en portugués
Avaliação da retificação com rebolo de CBN vitrificado aplicada em ligas de alto desempenho
Palabras clave en portugués
Difícil de ser retificado - DTG
Rebolo de CBN
Retificação em altas velocidades
Resumen en portugués
Superligas à base de níquel têm uma grande variedade de aplicações, por exemplo, turbinas a gás de aviões, câmaras de combustão, válvulas de motores, etc. As suas principais propriedades são alta resistência mecânica às temperaturas elevadas (> 500 graus Celsius), alta resistência à abrasão, alta resistência à fadiga e boa resistência à corrosão. Por isso, são considerados materiais difíceis de serem retificados (ou Difficult To Grind - DTG). Condições severas de retificação em superligas podem causar altas temperaturas de corte (podendo atingir 1000 graus Celsius) e altas tensões (pressão) na região de contato (podendo chegar a 3450 MPa), o que leva ao desenvolvimento rápido do desgaste do rebolo, dependendo das suas características e da severidade das condições de corte. A melhoria do processo de retificação pode ser atingida com a utilização de grãos superabrasivos mais duros, como o CBN. O CBN apresenta um alto desempenho na usinagem e sua aplicação tem como principais vantagens: a redução dos tempos de ciclo, melhor qualidade e aumento de produtividade. O desgaste da ferramenta de corte nos diversos processos de fabricação é de extrema importância no custo total da produção, portanto, na retificação de superligas, o desgaste do rebolo CBN deve ser mínimo devido ao seu alto custo. O presente trabalho avalia o desempenho de um rebolo de CBN vitrificado na retificação dos materiais Inconel 751, Silcrome 1 e 21-2N. Testes foram realizados variando-se apenas a velocidade de avanço para determinar a influência deste no desgaste do rebolo. Foi possível determinar assim, a relação entre o desgaste da ferramenta e a força tangencial em um grão, obtendo-se uma curva característica do rebolo.
Título en inglés
Evaluation of CBN grinding of high performance alloys
Palabras clave en inglés
CBN wheels
Difficult to Grind - DTG
High speed grinding - HSG
Resumen en inglés
Nickel-based superalloys have a great variety of applications, for example, aircraft gas turbines, combustion chambers, engines valves, etc. Their main properties are high strength at high temperatures (> 500 Celsius degrees), high resistance to the abrasion, high fatigue strength and good resistance to the corrosion. Therefore, they are considered difficult to grind (DTG) materials. Severe grinding conditions of superalloys can cause high cutting temperatures (able to reach 1000 Celsius degrees) and high tensions in the contact zone (able to reach 3450 MPa). This leads to the fast development of the wear of CBN wheels, depending on the tool characteristics and the severity of the cutting conditions. The improvement of the grinding process can be reached with the use of harder superabrasive grains, as the CBN. The CBN presents high performance in machining. The main advantages are: the reduction of the cycles times, better quality and increase of productivity. The wheel wear is extreme important in the total production cost, therefore, in the grinding of superalloys, the wear CBN wheels have to be minimum due to its high cost. The present work evaluates the performance of vitrified CBN wheels in the grinding process of Inconel 751, Silcrome 1 and 21-2N. Tests were carried out varying the feed-rate to establish its influence on the wheel wear. It was possible to determine the relation between tool wear and tangential force per grain, obtaining the wheel characteristic curve.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-02-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.