Disertación de Maestría
DOI
10.11606/D.18.2007.tde-13032007-112426
Documento
Autor
Nombre completo
Jesner Sereni Ildefonso
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2007
Director
Tribunal
Fernandes Junior, Jose Leomar (Presidente)
Fabbri, Glauco Tulio Pessa
Oda, Sandra
Título en portugués
Análise da viabilidade técnica da utilização do copolímero etileno acetato de vinila (EVA) descartado pela indústria calçadista em misturas asfálticas (processo seco)
Palabras clave en portugués
Ensaios mecânicos
Envelhecimento
Etileno acetato de vinila
Método Bailey
Misturas asfálticas
Processo seco
Resumen en portugués
A presente dissertação teve por objetivo analisar o comportamento de misturas asfálticas modificadas, pelo processo seco, com o copolímero etileno acetato de vinila (EVA), resíduo sólido descartado pela indústria calçadista. Em razão das características do EVA, acredita-se que ele possa melhorar as características mecânicas de misturas asfálticas e a resistência ao desgaste. A maioria dos pesquisadores tem direcionado seus esforços em estudos de misturas asfálticas modificadas pelo processo úmido, porém, devido à natureza do resíduo analisado neste trabalho, optou-se pelo processo seco, que demanda menos energia por não necessitar de moagem do material. A pesquisa compreendeu o estudo de amostras de misturas asfálticas não envelhecidas e com envelhecimento de duas e quatro horas em estufa, com moldagem de corpos-de-prova para realização dos ensaios de resistência à tração por compressão diametral estática, módulo de resiliência por compressão diametral, fluência por compressão uniaxial estática e dinâmica, vida de fadiga e desgaste por abrasão (ensaio Cantabro). Os resultados mostram que a utilização deste resíduo aumentou a resistência das misturas à fadiga e ao desgaste de forma significativa, porém as misturas tornaram-se mais susceptíveis à deformação permanente. O tempo de envelhecimento de curto prazo se mostrou importante, pois aumentou a resistência das misturas à fadiga e à deformação permanente.
Título en inglés
Analysis of the technical feasibility of the use of the ethylene vinyl acetate copolymer (EVA) discarded for the footwear industry in asphalt mixtures (dry process)
Palabras clave en inglés
Aging
Asphalt mixtures
Bailey method
Dry process
Ethylene vinyl acetate
Mechanical tests
Resumen en inglés
The main purpose of the present master thesis was to analyze the behavior of modified hot-mix asphalt, through the dry process, with the copolymer ethylene vinyl acetate (EVA) discarded by the footwear industry. Since the EVA characteristics, it is believed that it can improve hot-mix asphalt mechanic characteristics and the wear and tear resistance. Most of the researchers have been addressing efforts in studies on modified hot-mix asphalt by the wet process, however, due to the nature of the solid residue analyzed in this work, the dry process will demand less energy for not needing of grinding. The research evolved the study of samples of asphalt mixtures not aged and with aging of two and four hours in oven, submitted to indirect tension test, resilient modulus, static and dynamic creep, fatigue life and loss due to abrasion (Cantabro test). The results show that the use of this residue increased the resistance of the mixtures to the fatigue and loss of mass due to abrasion, however the mixtures became more susceptible to the permanent deformation. The short-time aging was shown important, because it increased the resistance of the mixtures to the fatigue and the permanent deformation.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
diss_jsi.pdf (3.22 Mbytes)
Fecha de Publicación
2007-03-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2022. Todos los derechos reservados.