Disertación de Maestría
DOI
10.11606/D.18.2017.tde-09102017-161144
Documento
Autor
Nombre completo
Fabio Alas Martins
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1995
Director
Tribunal
Spinelli, Dirceu (Presidente)
Crnkovic, Ovidio Richard
Fernandes, Odilson Coimbra
Título en portugués
Fator limite de intensidade de tensão e fechamento de trinca por fadiga para a liga aeronáutica: 7050-T73651
Palabras clave en portugués
Alumínio
Fadiga
Fechamento de trinca
Liga aeronáutica
Limite de fadiga
Resumen en portugués
O desenvolvimento de trabalhos relacionados à compreensão do fenômeno de limiar de fadiga ou fator de intensidade de tensão limite (ΔK0), tem possibilitado a aplicação de medidas de segurança para evitar acidentes ou perdas. Estas medidas vão desde a avaliação e substituição de peças contendo falhas até o estabelecimento de prazos entre inspeções. O conhecimento mais aprofundado dos mecanismos que induzem ou promovem o fechamento de trinca por fadiga, auxilia na avaliação dos resultados obtidos para ΔK0 e permite o conhecimento mais preciso deste valor, introduzindo o parâmetro ΔK0,ef. Estudou-se o crescimento de trinca por fadiga para a liga aeronáutica 7050-T73651 com decaimento de ΔK para determinação de ΔK0. Foi considerado o efeito de fechamento de trinca para se verificar o valor de ΔK0,ef para a orientação de laminação LT. Foi verificada a eficiência das equações de Priddle e de Donahue para se prever o comportamento da curva da/dN versus ΔK em função dos parâmetros da equação de Paris e características do material.
Título en inglés
not available
Palabras clave en inglés
not available
Resumen en inglés
The recent development of works on the fatigue threshold phenomenon has provided powerful knowledge applicable to reliability practices such as the replacement of parts or the establishment of periods between inspections. A better understanding of the mechanisms leading to fatigue crack closure has permitted investigators to describe more accurately ΔK0 values, thus introducing a new ΔK0,eff parameter. In this work, fatigue crack growth was carried out on the aeronautics aluminum alloy 7050-T73651 with ΔK decreasing in order to determine ΔK0. Fatigue crack closure effects were considered as to verify the ΔK0,eff value for the LT direction. The ability of the equation of Priddle and that of Donahue to predict the behaviour of da/dN versus ΔK curves based on the parameters m and C from Paris equation and on the materials characteristics was verified.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-10-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.