Tesis Doctoral
DOI
https://doi.org/10.11606/T.18.2017.tde-09102017-142618
Documento
Autor
Nombre completo
Alberto Ibanez Ruiz
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1996
Director
Tribunal
Rollo, João Manuel Domingos de Almeida (Presidente)
Beatrice, Carlos Roberto Sobreira
Canale, Lauralice de Campos Franceschini
Gomes, Samuel Irati Novaes
Gregolin, José Ângelo Rodrigues
 
Título en portugués
A presença do nióbio em um ferro fundido branco de cromo-molibdênio: traçado da curva transformação-tempo-temperatura
Palabras clave en portugués
Curvas TTT
Dilatometria
Ferro fundido branco de alto cromo
Nióbio
Temperabilidade
Transformações de fase
Resumen en portugués
Avaliou-se experimentalmente o ferro fundido branco de alto-cromo-molibdênio ao qual foi adicionado nióbio, a respeito de sua temperabilidade. Dilatometricamente traçou-se a curva TTT desse material, bem como a de um ferro fundido branco de alto cromo para efeito comparativo. Constatou-se por essa comparação e pelos resultados da literatura a alta temperabilidade obtida pela liga experimental. A partir da temperatura de austenitização utilizada, podem-se usar taxas de resfriamento de até 0,12°C/s sem transformação de fase, enquanto que na liga comparativa essa taxa aumenta para 5,8°C/s. Foram realizadas análises de desgaste abrasivo, de dureza e microdureza, de difração por raios-X , de fase magnética e de microanálise como forma de caracterizar as transformações de fase observadas por dilatometria. As variações estruturais decorrentes dos tratamentos térmicos realizados nas duas ligas foram acompanhados por microscopia ótica. É indicativo pelo presente trabalho que tal material além de suas características inerentes de resistência à abrasão e à corrosão oferece maior flexibilidade nos projetos que envolvam paredes espessas.
 
Título en inglés
not available
Palabras clave en inglés
Dilatometry
Hardenability
High chromium white cast iron
Niobium
Phase transformation
TTT curves
Resumen en inglés
In this work we studied the hardenability of high chromium- molibdenum white cast iron with niobium. By dilatometry we obtained the TTT curve of this material as well as the high chromium white cast iron for comparison. This comparison and available results in literature confirm the high temperability of experimental material. We can use slow rate cooling 0,12°C/s or higher without phase transformation, while in the comparative alloy this rate is around 5,8°C/s or higher from specific used austenitic abrasive temperature. We also realized analysis of abrasive wear, hardness and microhardness, raios-X difraction, magnetic phase and microanalyse for verifing the phase transformation as observed by dilatometry. The structure variation as function of termic treatment in both alloys is monitored by optical microscope. The present work indicate that the material under study can offer more flexibility for projects with thick materials apart from intrinsic characteristics of abrasive wear and corrosion.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Tese_Ruiz_AlbertoI.pdf (42.74 Mbytes)
Fecha de Publicación
2017-10-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores.
CeTI-SC/STI
© 2001-2024. Biblioteca Digital de Tesis y Disertaciones de la USP.