Tesis Doctoral
DOI
https://doi.org/10.11606/T.18.2017.tde-20042017-110657
Documento
Autor
Nombre completo
Winston Junior Zumaeta Moncayo
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2017
Director
Tribunal
Pinheiro, Libânio Miranda (Presidente)
Catoia, Bruna
Leite Júnior, Geraldo Silveira
Moreno Junior, Armando Lopes
Munaiar Neto, Jorge
Título en portugués
Comportamento residual do concreto leve com pérolas de EPS após situação de incêndio
Palabras clave en portugués
ABAQUS 14
Análise numérica
Concreto com EPS
Concreto leve
Concreto pré-moldado
Ensaios
Fibras de aço
Situação de incêndio
Resumen en portugués
O estudo do comportamento de estruturas em situação de incêndio tem se tornado cada vez mais importante devido às graves consequências de incêndios que têm ocorrido no Brasil e em outros países. Por esse motivo, este trabalho tem como objetivo estudar o comportamento residual do concreto com pérolas de EPS sob altas temperaturas, pois se pretende utilizar esse concreto em painéis e em lajes pré-moldadas para a construção de edifícios de pequeno e de médio porte, por ele ser um concreto muito leve, com massa específica em torno de 1170 kg/m3, um pouco menos da metade da relativa ao concreto convencional. Para este estudo, foram utilizados corpos de prova cilíndricos e prismáticos, seguindo recomendações nacionais e internacionais. As análises foram realizadas para 200ºC, 400ºC e 600ºC, e foram avaliadas: massa específica, resistência à compressão, módulo de elasticidade estático, módulo de elasticidade dinâmico, resistência à tração por compressão diametral, resistência à tração na flexão e fator de tenacidade. Para esses dois últimos, foram utilizadas fibras de aço nas seguintes taxas: 0,3%, 0,6% e 0,9%. Os resultados foram comparados com os de concreto com EPS em temperatura ambiente e com os de concreto convencional, que já tem alguns resultados disponíveis na literatura técnica. Também foi realizada uma análise térmica numérica, utilizando o software ABAQUS 14, para calibrar duas propriedades: calor específico e condutividade térmica. Para isso, foram utilizados resultados obtidos na análise experimental. Os resultados numéricos e experimentais foram coerentes com os esperados. Os experimentais apresentaram redução de valor à medida que a temperatura aumentava, e comportamento pior em comparação ao concreto convencional. A adição de fibras aumentou a resistência à tração na flexão e também a tenacidade, tanto em temperatura ambiente quanto em temperaturas elevadas.
Título en inglés
Residual behavior of lightweight concrete with EPS beads after fire
Palabras clave en inglés
ABAQUS 14
Concrete with EPS
Fire situation
Lightweight concrete
Numerical analysis
Precast concrete
Steel fibers
Tests
Resumen en inglés
The study of the structures behavior in fire has become increasingly important due to the serious consequences of fires that have occurred in Brazil and in other countries. Therefore, this work aims to study the residual behavior of concrete with EPS beads under high temperatures, because it is intended to use it in panels and precast slabs for the construction of small and medium-sized buildings, for it is a very light concrete, with a density around 1170 kg/m3, slightly less than half that of conventional concrete. For this study, cylindrical and prismatic specimens were used, following national and international standards. The analyses were carried out to 200°C, 400°C and 600°C, and were evaluated: density, compression strength, static modulus of elasticity, dynamic modulus of elasticity, splitting tensile strength, flexural tensile strength, and toughness factor. For the latter two, steel fibers were used at the following rates: 0.3%, 0.6% and 0.9%. The results were compared with those of concrete with EPS at room temperature, and with conventional concrete which already has some results available in the technical literature. A numerical thermal analysis was also performed, using ABAQUS 14 software, to calibrate two properties: specific heat and thermal conductivity. For this, results obtained in the experimental analysis were used. The numerical and experimental results were consistent with those expected. The experimental results showed reduction of value as temperature increased, and worst behavior in comparison to ordinary concrete. The addition of fibers increased tensile strength in bending and also the toughness, both at room temperature and at elevated temperatures.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-05-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.