Thèse de Doctorat
DOI
10.11606/T.18.2007.tde-19032007-100952
Document
Auteur
Nom complet
Valdirene Maria Silva
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2007
Directeur
Jury
Liborio, Jefferson Benedicto Libardi (Président)
Baldo, João Baptista
Debs, Ana Lucia Homce de Cresce El
Giongo, Jose Samuel
Helene, Paulo Roberto do Lago
Titre en portugais
Ação da carbonatação em vigas de concreto armado em serviço, construídas em escala natural e reduzida
Mots-clés en portugais
Carbonatação
Cobrimento
Concreto de alto desempenho
Concretos
Durabilidade
Fissura
Resumé en portugais
Este trabalho apresenta uma análise do comportamento da frente de carbonatação em vigas de concreto armado sob tensão, em escala natural e reduzida, com a máxima condição de subarmação. As vigas foram construídas com e sem adição da sílica da casca de arroz e sílica de ferro silício ou silício metálico. Para cada viga em escala natural (agregado graúdo com D máx. = 19 mm) foi moldada uma em escala reduzida com o mesmo traço de concreto para estabelecer os mesmos parâmetros de comparação. As vigas foram curadas durante 7 dias e posteriormente submetidas à flexão, com o carregamento aplicado nos terços (L/3 da viga). Realizou-se o pré-condicionamento para a estabilização da umidade interna das vigas que foram expostas durante 28 dias em um ambiente com concentração de 50% de dióxido de carbono, umidade relativa de 65 '+ OU -' 5% e temperatura ambiente. Foram determinados: resistências à compressão simples axial, resistência à tração por compressão diametral, módulos de elasticidade e profundidade da frente de carbonatação em corpos-de-prova cilíndricos. A profundidade da frente de carbonatação em corpos-de-prova foi determinada para diferentes concentrações de dióxido de carbono. Também foi verificada a carbonatação ao longo das vigas em escala natural e reduzida e nas posições das fissuras. Para a previsão da profundidade da frente de carbonatação nas vigas, foram ajustadas equações para a representação da carbonatação na região das fissuras. Os resultados obtidos mostraram a eficiência da espessura do cobrimento, a eficácia dos modelos físicos reduzidos para realizar estudos de carbonatação e a tendência da carbonatação em elementos estruturais na condição de serviço. A frente de carbonatação difere na posição das fissuras, evidenciando um comportamento diferente quando comparado com corpos-de-prova. A análise microestrutural ilustrou o comportamento da frente de carbonatação em vigas de concreto armado, complementando o estudo experimental. Com base nos resultados obtidos pode-se afirmar que a simples adoção de concretos de alto desempenho para construção de elementos estruturais não é suficiente nas peças que contenham fissuras e que sejam submetidas a atmosferas ambientais agressivas.
Titre en anglais
Carbonation action in reinforced concrete beams under stress regime carried out on full and small scales
Mots-clés en anglais
Carbonation
Concretes
Cover
Crack
Durability
High performance concrete
Resumé en anglais
This work reports on the behavior of carbonation in reinforced concrete beams under stress regime on full and small scales having the lowest possible frame. The beams were made with and without adding silica from rice husk and silica fume (Fe-Si). For each beam on a full scale (coarse aggregate with D máx. = 19 mm) another beam on a small scale was made with the same mix of concrete to maintain the same comparison parameter. The beams were cured for 7 days and subsequently submitted to flexure by applying a two-point loading (L/3 of beam). Humidity stabilization to stabilize internal humidity of beams exposed for 28 days in an environment with a concentration of 50% carbon dioxide, 65 '+ OR -' 5% of relative humidity and room temperature was carried out. The following was determined: axial compression strength, tensile splitting strength, young's modulus and carbonation depth in cylindrical specimens. The carbonation depth was determined in specimens with unlike carbon dioxide concentration. Moreover, carbonation along beams on full and small scales and in cracks was observed. To estimate the carbonation depth of the beams, equations were adjusted to represent the carbonation in cracks. The results show the efficiency in the thickness of the cover, efficiency of small-scale models for studies concerning carbonation and behavior of carbonation in the serviceability of structural elements. The carbonation depth differs in the position of cracks, showing behavior which is unlike the one compared to specimens. The microstructure analyses show the behavior of carbonation depth in reinforced concrete beams complementing the experimental study. The results show that it is not sufficient to use high performance concretes in structural elements for elements with cracks and in aggressive atmospheres.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2007-04-16
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.