Tesis Doctoral
DOI
10.11606/T.18.2007.tde-19032007-100952
Documento
Autor
Nombre completo
Valdirene Maria Silva
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2007
Director
Tribunal
Liborio, Jefferson Benedicto Libardi (Presidente)
Baldo, João Baptista
Debs, Ana Lucia Homce de Cresce El
Giongo, Jose Samuel
Helene, Paulo Roberto do Lago
Título en portugués
Ação da carbonatação em vigas de concreto armado em serviço, construídas em escala natural e reduzida
Palabras clave en portugués
Carbonatação
Cobrimento
Concreto de alto desempenho
Concretos
Durabilidade
Fissura
Resumen en portugués
Este trabalho apresenta uma análise do comportamento da frente de carbonatação em vigas de concreto armado sob tensão, em escala natural e reduzida, com a máxima condição de subarmação. As vigas foram construídas com e sem adição da sílica da casca de arroz e sílica de ferro silício ou silício metálico. Para cada viga em escala natural (agregado graúdo com D máx. = 19 mm) foi moldada uma em escala reduzida com o mesmo traço de concreto para estabelecer os mesmos parâmetros de comparação. As vigas foram curadas durante 7 dias e posteriormente submetidas à flexão, com o carregamento aplicado nos terços (L/3 da viga). Realizou-se o pré-condicionamento para a estabilização da umidade interna das vigas que foram expostas durante 28 dias em um ambiente com concentração de 50% de dióxido de carbono, umidade relativa de 65 '+ OU -' 5% e temperatura ambiente. Foram determinados: resistências à compressão simples axial, resistência à tração por compressão diametral, módulos de elasticidade e profundidade da frente de carbonatação em corpos-de-prova cilíndricos. A profundidade da frente de carbonatação em corpos-de-prova foi determinada para diferentes concentrações de dióxido de carbono. Também foi verificada a carbonatação ao longo das vigas em escala natural e reduzida e nas posições das fissuras. Para a previsão da profundidade da frente de carbonatação nas vigas, foram ajustadas equações para a representação da carbonatação na região das fissuras. Os resultados obtidos mostraram a eficiência da espessura do cobrimento, a eficácia dos modelos físicos reduzidos para realizar estudos de carbonatação e a tendência da carbonatação em elementos estruturais na condição de serviço. A frente de carbonatação difere na posição das fissuras, evidenciando um comportamento diferente quando comparado com corpos-de-prova. A análise microestrutural ilustrou o comportamento da frente de carbonatação em vigas de concreto armado, complementando o estudo experimental. Com base nos resultados obtidos pode-se afirmar que a simples adoção de concretos de alto desempenho para construção de elementos estruturais não é suficiente nas peças que contenham fissuras e que sejam submetidas a atmosferas ambientais agressivas.
Título en inglés
Carbonation action in reinforced concrete beams under stress regime carried out on full and small scales
Palabras clave en inglés
Carbonation
Concretes
Cover
Crack
Durability
High performance concrete
Resumen en inglés
This work reports on the behavior of carbonation in reinforced concrete beams under stress regime on full and small scales having the lowest possible frame. The beams were made with and without adding silica from rice husk and silica fume (Fe-Si). For each beam on a full scale (coarse aggregate with D máx. = 19 mm) another beam on a small scale was made with the same mix of concrete to maintain the same comparison parameter. The beams were cured for 7 days and subsequently submitted to flexure by applying a two-point loading (L/3 of beam). Humidity stabilization to stabilize internal humidity of beams exposed for 28 days in an environment with a concentration of 50% carbon dioxide, 65 '+ OR -' 5% of relative humidity and room temperature was carried out. The following was determined: axial compression strength, tensile splitting strength, young's modulus and carbonation depth in cylindrical specimens. The carbonation depth was determined in specimens with unlike carbon dioxide concentration. Moreover, carbonation along beams on full and small scales and in cracks was observed. To estimate the carbonation depth of the beams, equations were adjusted to represent the carbonation in cracks. The results show the efficiency in the thickness of the cover, efficiency of small-scale models for studies concerning carbonation and behavior of carbonation in the serviceability of structural elements. The carbonation depth differs in the position of cracks, showing behavior which is unlike the one compared to specimens. The microstructure analyses show the behavior of carbonation depth in reinforced concrete beams complementing the experimental study. The results show that it is not sufficient to use high performance concretes in structural elements for elements with cracks and in aggressive atmospheres.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2007-04-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.