Thèse de Doctorat
DOI
10.11606/T.18.2016.tde-15022016-091455
Document
Auteur
Nom complet
Maria Gorett dos Santos Marques
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2015
Directeur
Jury
Calil Junior, Carlito (Président)
Bose Filho, Waldek Wladimir
Lahr, Francisco Antonio Rocco
Savastano Junior, Holmer
Vasconcelos, Raimundo Pereira de
Titre en portugais
Estudo das propriedades físicas e mecânicas e da durabilidade de compósitos cimentícios reforçados com fibra amazônica
Mots-clés en portugais
Arumã
Fibra vegetal
Laminado cimentício
Material compósito
Resumé en portugais
O presente estudo tem como objetivo principal desenvolver um compósito cimentício reforçado com fibras de arumã. O intuito é agregar valor a uma planta típica da região Amazônica, denominada arumã, pertencente à espécie do gênero Ischnosiphon arouma (aubl) Korn e originária da família Maranthaceae, de tal modo que possa ser obtido um Novo Material. Na primeira etapa do estudo foi realizada a caracterização da fibra vegetal de arumã e de todos os componentes da matriz cimentícia, a qual compreendeu ensaios químicos, físicos e mecânicos para a investigação e avaliação de suas propriedades. Na etapa seguinte, adotou-se o procedimento de trabalhar as características físicas e mecânicas das fibras junto à matriz cimentícia, compreendendo um estudo da modificação superficial da fibra por meio de tratamentos químicos à base de soluções de hidróxido de sódio ou utilizando processos com água quente e hornificação. Na terceira etapa, foram produzidas placas reforçadas com fibras sem e com tratamento, as quais, parte delas foram submetidas à cura por 28 dias e as restantes ao ensaio de envelhecimento acelerado. Os resultados obtidos na caracterização das fibras de arumã indicam o seu potencial uso como elemento de reforço para compósitos cimentícios. Por outro lado, os compósitos produzidos com telas de fibra de arumã sem e com tratamento (hornificação e alcalino), apresentaram comportamento pouco dúctil e com baixa resistência, como consequência da degradação das fibras na matriz cimentícia. Isso foi confirmado por meio de ensaios de envelhecimento acelerado com ciclos de molhagem e secagem.
Titre en anglais
Study of physical and mechanical properties and durability of the cementation composites reinforced with amazon fiber
Mots-clés en anglais
Arumã
Composite material
Laminate cement
Vegetable fiber
Resumé en anglais
This present study aims to develop a cementation composite reinforced with arumã fiber. The aim is to aggregate value to a typical plant of the Amazon region, called arumã, belonging to species of the genus Ischnosiphon arouma (Aubl) Korn and originally from Maranthaceae family, so that, it can be obtained a New Material. In the first stage of the study was performed the characterization the vegetable fiber arumã and all components of the cementicious matrix, which comprised chemical, physical and mechanical tests for research and evaluation of their properties. In the next stage, it was adopted the procedure of working the physical and mechanical characteristics of the fibers with the cementitious matrix comprising a study of the surface of the fiber modification by chemical treatments using sodium hydroxide solution or employing procedures with hot water and hornification. In the third step, the reinforced plates were produced without and with treatment, which, part of were subjected to cure for 28 days and the remaining subjected to the accelerated aging test. The results obtained in the characterization of arumã fibers indicate its potential use as a reinforcement element for cementicious composites. On the other hand, the composites produced with arumã fiber fabrics without and with a treatment (hornification and alkaline) showed slightly ductile behavior and low strength as a result of degradation of fibers in the cementitious matrix. This was confirmed through accelerated aging tests with wetting and drying cycles.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-02-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.