Master's Dissertation
DOI
10.11606/D.18.2010.tde-14012011-104648
Document
Author
Full name
Tobias Azevêdo da Costa Pereira
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2010
Supervisor
Committee
Liborio, Jefferson Benedicto Libardi (President)
Morelli, Marcio Raymundo
Thomaz, Ercio
Title in Portuguese
Concreto auto-adensável, de alta resistência, com baixo consumo de cimento Portland e com adições de fibras de lã de rocha ou poliamida
Keywords in Portuguese
Abrasão
Concreto auto-adensável
Concreto de alta resistência
Consumo de cimento
Lã de rocha
Poliamida
Temperatura
Abstract in Portuguese
O objetivo deste trabalho é apresentar uma metodologia que possibilita a obtenção de uma linha de concretos auto-adensáveis de alta resistência, econômicos e com reduzido impacto ambiental quando comparados com os concretos correntes. Para atingir estes resultados foram estabelecidos critérios de dosagem e de produção visando à sinergia entre os materiais constituintes do concreto. Foram pesquisados métodos de empacotamento dos agregados e adições minerais, estudada a interação entre o aditivo superplastificante e os materiais cimentícios e a incorporação de fibras de lã-de-rocha ou poliamida. Os concretos com matriz densa sob efeito de temperaturas elevadas tendem a sofrer lascamentos explosivos. Diante disso foi verificado o comportamento de corpos de prova e os resultados indicaram a importância da adição da fibra de poliamida nessa condição, onde o concreto resistiu a uma temperatura de 400ºC. Ensaios de resistência à abrasão indicaram que a fibra de lã-de-rocha melhora essa propriedade do concreto e, como esperado, essa adição não inibe o lascamento explosivo do concreto. Também foram determinadas as propriedades mecânicas dos concretos e concluiu-se que é possível o emprego de um concreto estrutural auto-adensável com consumo de cimento Portland da ordem de 325 kg/'M POT.3', fc7 = 53 MPa, fc28 = 71 MPa e Ec28 = 43 GPa. Devido à ação das adições minerais, estes concretos atingiram uma grande reserva de resistência à compressão após a idade de referência de 28 dias, obtendo-se 89 MPa aos 131 dias de idade. A densificação da pasta hidratada, a melhoria da zona de interface desta com os agregados, além da fissuração reduzida decorrente do baixo consumo de cimento e da adição de fibras indicam que este material tem desempenho superior ao prescrito pela NBR 6118 para as diversas classes de agressividade ambiental e de resistência.
Title in English
High strength self-consolidating concrete, with low content of cement Portland and addition of polyamide or rock wool fibers
Keywords in English
Abrasion
Cement content
High strength concrete
Polyamide
Rock wool
Self-consolidating concrete
Temperature
Abstract in English
The aim of this work is to show a methodology that allows to realize a set of high strength self-consolidating concrete, economic and with lower environmental impact when compared with current concretes. To get these results, criteria for production and mix design had been established aiming at to synergy between constituent materials of the concrete. Methods of particles packing (aggregates and mineral additions), the interaction between the superplasticizer and cementitious materials and the fiber incorporation were researched. The concretes with dense matrix under effect of high temperatures are susceptible to explosive spalling. In this situation, concretes were evaluated by testing cylindrical specimens and results evidenced the importance of the polyamide fiber when the concrete supported 400ºC. Tests of abrasion resistance indicated a good application for the wool-of-rock fiber, but this material not avoids explosive spalling. The mechanical properties of the concretes were determined and show that is possible to product a self consolidate concrete with low cement content (325 kg/'M POT.3'), fc7 = 53 MPa, fc28 = 71 MPa and Ec28 = 43 GPa. Due to action of the mineral additions, these concretes had a great reserve of compressive strength after the age of reference of 28 days and achieved 89 MPa at 131 days of age. The high density cement paste, the improvement of the matrix-aggregate interfacial zone and the reduced cracking due to the low cement content and the fibre addition indicate that these materials has superior performance to those prescribed for the NBR 6118 for diverse strength classes and aggressive environmental exposure.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2011-02-07
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.