Doctoral Thesis
DOI
10.11606/T.18.2008.tde-12122008-143827
Document
Author
Full name
Sandra Maria de Lima
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2008
Supervisor
Committee
Libório, Jefferson Benedicto Libardi (President)
Barbosa, Mônica Pinto
Hanai, João Bento de
Helene, Paulo Roberto do Lago
Pinheiro, Libanio Miranda
Title in Portuguese
Concreto de alto desempenho aplicado a sistemas de processamento e armazenagem de alimentos em baixas temperaturas
Keywords in Portuguese
Alto desempenho
Armazenagem de alimentos
Baixas temperaturas
Concreto
Durabilidade
Gelo e degelo
Sistema de vazios
Abstract in Portuguese
O desenvolvimento de um concreto de alto desempenho aplicado a sistemas de processamento e armazenagem de alimentos em baixas temperaturas teve por objetivo atender às indústrias de alimentos no Brasil que se utilizam da tecnologia do frio em seu processo industrial. A hegemonia mundial do mercado de carnes é brasileira, sendo que nossas indústrias são responsáveis por 33% desse mercado. A ausência de estudos para aprimorar e tornar as plantas industriais mais duráveis e condizentes com a importância do setor foi determinante na delineação do tema desta tese. Desenvolveu-se um concreto de alto desempenho frente às possíveis situações em uma planta industrial: baixas temperaturas em ambientes secos e baixas temperaturas em ambientes sujeitos à umidade. A temperatura mínima a qual foram submetidos os concretos analisados foi de 35°C. O método de dosagem e as diretrizes calcadas no reforço da matriz da pasta de cimento e refinamento de poros mostraram-se como uma alternativa para vencer as agressividades causadas pelas baixas temperaturas ao concreto. Até então, estudos sugeriam um sistema de ar cujos vazios teriam diâmetros em torno de 250 µm espaçados com esta mesma distância entre eles e com conteúdo de 6±1% para a proteção de concretos expostos a baixas temperaturas. A produção de um concreto coeso, com teor de ar de 3,5%, poros com diâmetro médio de 0,02 µm e com área específica de 2,84m²/g, provaram ser duráveis quando expostos ao congelamento e a ciclos de gelo e degelo. O fator de durabilidade para esses concretos foi de 97%. Além da durabilidade, o projeto de dosagem contemplou o aspecto econômico, produzindo 1MPa com 7,8 kg de cimento por metro cúbico de concreto. Os resultados foram obtidos por meio de ensaios dinâmicos, microscopia eletrônica de varredura, porosimetria por intrusão de mercúrio, absorção de água por imersão, além dos ensaios mecânicos de resistência à compressão, à tração na flexão e módulo de elasticidade.
Title in English
High performance concrete applied to storage and processing system buildings at low temperatures
Keywords in English
Air void system
Concrete
Durability
Foodstuff storage
Freezing-thawing cycles
High performance
Low temperatures
Abstract in English
Brazil has rapidly emerged as one of the world's leading meat exporters, being responsible by 33% of this market. In face of that, a high performance concrete (HPC), that can be applied to storage and processing system buildings at low temperatures, has been developed with the aim of answering the needs of brazilian food manufacturers that use cooling technology during industrial process. The lack of studies to improve industrial plants and make them more durable was determinant to delineate this thesis subject. A high performance concrete was designed to resist to low temperatures at dry environments as well as at moist ones. Concrete was exposed to a target temperature of -35°C. The dosage method and the guidelines based on the strengthening of bulk cement and the porous refinement showed to be an alternative to overcome the aggressiveness caused by low temperatures to concrete. To this day, studies have suggested air voids systems to protect concrete from low temperature effects. According to them, the air voids should have about 250 µm of diameter, spaced from each other this same distance and with an air content of 6±1%. However, making a cohesive concrete, with 3,5% of air content and an average diameter porous of 0,02 µm with an specific surface of 2,84m²/g, resulted in a durable concrete, even when exposed to frost / thawing cycles. The durability factor of these concretes achieved 97%. Besides durability, the dosage design brought economical advantages, producing 1 MPa with 7,8 kg of cement per cubic meter of concrete. The results were obtained through dynamic tests, scanning electron microscopy, mercury intrusion porosimetry and water absorption by immersion. In addition, tests of compression, tension strength and elastic modulus were carried out.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2009-02-04
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.