Mémoire de Maîtrise
DOI
Document
Auteur
Nom complet
Ugo Leandro Belini
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Piracicaba, 2007
Directeur
Jury
Tomazello Filho, Mario (Président)
Bortoletto Junior, Geraldo
Oliveira, José Tarcisio da Silva
Titre en portugais
Caracterização e alterações na estrutura anatômica da madeira do Eucalyptus grandis em três condições de desfibramento e efeito nas propriedades tecnológicas de painéis MDF
Mots-clés en portugais
Anatomia vegetal
Chapa de fibra
Desfibramento
Eucalipto
Madeira
Resumé en portugais
Constata-se, atualmente, uma grande demanda de crescimento na produção de painéis MDF de madeira de eucalipto em relação à do pinus, comumente utilizada na indústria. Pelo exposto, o presente trabalho teve como objetivo caracterizar os componentes morfológicos da madeira de cavacos de Eucalyptus grandis, “in natura” e submetidas a três condições diferentes de desfibramento (tempo, pressão e energia), sendo denominadas de condição intermediária, de menor e de maior intensidade de refino (A, B e C, respectivamente). As características tecnológicas das chapas MDF obtidas para as três condições de desfibramento foram, da mesma forma, analisadas segundo a norma NBR 15316. No desenvolvimento do trabalho foram coletados para as três condições de desfibramento, em toda a cadeia produtiva do painel MDF: cavacos de madeira, material lenhoso desfibrado e painéis MDF final em escala industrial e laboratorial. Os cavacos de madeira foram caracterizados com respeito a sua estrutura microscópica; o material lenhoso desfibrado nas 3 condições foi avaliado através do seu fracionamento em peneiras seguindo-se a classificação morfológica e a caracterização microscópica dos componentes celulares de cada fração. Os resultados mostraram que os cavacos de madeira coletados no silo da unidade fabril apresentaram-se homogêneos nas 3 pré-condições avaliadas e não exerceram qualquer influência nos tratamentos. A condição de desfibramento mais branda induziu a formação de feixes de fibra e manutenção de vasos e parênquima com as fibras apresentando maior comprimento médio. A condição de desfibramento mais drástica induziu o rompimento da parede das fibras, com polpa apresentando fibras de menor comprimento e com baixa freqüência de vasos e de parênquima. As características de coloração foram observadas, sendo que a massa de fibras mais escura foi decorrente da alta pressão, maior tempo e mais energia de refinação aplicada. Os painéis MDF obtidos na condição mais branda apresentaram maior resistência ao arranque de parafuso, ao contrário dos painéis MDF confeccionados com polpa da condição de desfibramento mais drástica mostrando menores propriedades mecânicas de resistência à tração perpendicular e superficial e maiores valores de inchamento e de absorção. Os resultados do trabalho evidenciam a importância das variáveis de produção relacionadas com os tratamentos da madeira e do material fibroso nas propriedades tecnológicas dos painéis MDF de eucalipto.
Titre en anglais
Characterization and anatomical structure alterations of Eucalyptus grandis wood in three refining conditions and effect in technological properties of MDF panels
Mots-clés en anglais
Eucalyptus grandis
MDF panel
Medium density fiberboard
Wood anatomy
Wood refining
Resumé en anglais
Currently is evidenced a great demand of growth in eucalypts MDF panels production in relation with pinus, commonly used in the industry. The present study had the objective to characterize the morphologic components of Eucalyptus grandis wood chips “in natura” submitted in three different refining conditions (time, pressure and energy), named intermediate, smaller and biggest intensity of refining (A, B and C, respectively). The technological characteristics of MDF panels from three refining conditions were analyzed according standard NBR 15316. During this development were collected for three refining conditions, in all the productive chain of the MDF panels: wood chips, wooden dissociated material and panels MDF in industrial and laboratorial scale. The wood chips structure were microscopically characterized; the dissociated wood cells suspended in water of 3 refining conditions were evaluated through its separation in sieves and each fraction of woody material was morphologically classified and microscopically described. The results showed that the wood chips collected in industry storage compartment were homogeneous in the 3 refining preconditions and not influenced the MDF panel's treatments. The softness refining condition induced the shives formation and maintenance of vessels, parenchyma and the longest fibers. The more drastic refining condition induced the fiber cell walls broking, with wood pulp presenting shortest fibers and lower vessels and parenchyma frequency. The coloration characteristics were observed, and the fiber pulp was darker as result of the high pressure, greater time and more refinement energy applied. The MDF panels elaborated by softness refining condition presented greater resistance to screw pull in contrast of panels confectioned with hardness refining condition showing lesser mechanical properties of perpendicular and superficial tensile strength and bigger values of swelling and absorption. The results showed the importance of the variable related production with the wood and pulp wood treatments in technological properties of eucalypts MDF panels.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
UgoBelini.pdf (1.56 Mbytes)
Date de Publication
2007-06-11
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2022. Tous droits réservés.