Mémoire de Maîtrise
DOI
10.11606/D.11.2014.tde-03102014-151142
Document
Auteur
Nom complet
Flavia Schmidt
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Piracicaba, 2014
Directeur
Jury
Silva Junior, Francides Gomes da (Président)
Bortoletto Junior, Geraldo
Moura, Luiz Fernando de
Titre en portugais
Polpação kraft de cavacos de espessura reduzida
Mots-clés en portugais
Espessura dos cavacos
Processo Kraft
Tempo reduzido de cozimento
Resumé en portugais
Este trabalho teve como objetivo analisar os cavacos de dimensões reduzidas inseridos em cozimentos que se utilizam de menores tempos e maiores temperaturas, de maneira a se obter as bases para o estabelecimento de um novo processo e/ou a otimização dos sistemas atualmente utilizados em escala industrial. Amostras de cavacos de referência (3,6 mm, obtidas pelo processo convencional de picagem) e de cavacos com espessura de 0,5 mm, 1 mm e 2 mm (obtidas por um gerador de partículas), do híbrido de Eucalyptus urophylla x Eucalyptus grandis com 7 anos foram analisadas quanto à densidade básica, composição química e morfologia das fibras. Após a caracterização, os materiais foram submetidos à polpação kraft pelo processo convencional e foram testados três níveis de fator H com quatro níveis de álcali ativo de maneira a se estabelecer uma equação que representasse o processo e pudesse ser utilizada em cozimentos futuros. Através das equações obtidas foi possível calcular os parâmetros de rendimento depurado, álcali ativo residual, álcali ativo consumido, teor de sólidos secos, fator H e álcali ativo em função de um número kappa 18. Os resultados mostram que a densidade básica, a composição química e a morfologia das fibras da madeira não foram afetadas pelo processo de picagem. No entanto, a densidade a granel foi afetada pela espessura dos cavacos, sendo de 0,037, 0,081, 0,110 e 0,141 g.cm-³ para os cavacos de 0,5 mm, 1 mm, 2 mm e 3,6 mm respectivamente. No processo de polpação, as espessuras se comportaram de maneira semelhante, no entanto, a espessura de 2 mm apresentou o melhor número kappa para o fator H de 451, o de maior interesse, com o mesmo rendimento que as demais espessuras. Na análise de regressão, a espessura de 2 mm apresentou melhor rendimento, menor teor de sólidos e menor fator H (de 461), compatível com o que se pretende utilizar em processos de polpação com tempo reduzido de cozimento.
Titre en anglais
Kraft pulping of thin chips
Mots-clés en anglais
Chip thickness
Kraft pulping
Short time pulping process
Resumé en anglais
The objective of this work was to evaluate the performance of thin chips inserted on a short time and higher temperatures in cooking process, to obtain the basis for the establishment of a new process and / or the optimization of the currently systems used on an industrial scale. Samples of the reference chips (3,6 mm obtained by the conventional process of chipping) and thin chips with 0,5 mm, 1 mm and 2 mm (obtained by a particle generator) of the Eucalyptus urophylla x Eucalyptus grandis hybrid with 7 years of age had their density, chemical composition and fibers morphology evaluated. After the characterization, the materials were submitted to conventional kraft pulping process and three levels of H factor with four levels of active alkali were tested to establish an equation to represent the process that can be used on future cookings. Yield, residual active alkali, consumed active alkali, dry solids, H factor and active alkali were calculated through equations, according to a kappa number 18. The results show that the basic density, chemical composition and morphology of the wood fibers were not affected by the chipping process. However, the bulk density of 0,037, 0,081, 0,110 and 0,141 g.cm-³ for the 0,5 mm, 1 mm, 2 mm and 3,6 mm chips, respectively, was affected by the chip thickness. On the pulping process, the different chips had the same behavior, however, 2 mm chips showed the best kappa number to H factor 451, with the same yield as the other thickness. On the regression analysis, the 2 mm chips showed better performance, lower solids content and lower H factor (461), consistent with a short time pulping process.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-10-08
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.