Mémoire de Maîtrise
DOI
10.11606/D.100.2014.tde-06072015-212521
Document
Auteur
Nom complet
Andressa da Nobrega Almeida
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2014
Directeur
Jury
Costa, Sirlene Maria da (Président)
Canettieri, Eliana Vieira
Kanamaru, Antonio Takao
Titre en portugais
Estudo da aplicação de um polímero em superfícies têxteis e desenvolvimento de novas texturas
Mots-clés en portugais
Borracha de silicone
Novas Texturas
Substratos têxteis
Resumé en portugais
O objetivo do presente trabalho foi pesquisar sobre a adequação e viabilização do processo de aplicação de um polímero, comercialmente conhecido como borracha de silicone, com o intuito de criar um novo conceito estético, a partir da vontade de produzir uma nova textura ou nova concepção de estrutura para substratos têxteis aplicados na alta costura. Primeiramente, investigou-se qual a melhor forma de adequação desta borracha e como ela se comporta em diferentes superfícies têxteis. Foram realizados ensaios para avaliar as condições de preparo da borracha de silicone, quanto ao volume de catalisador a ser utilizado de (0,75, 2,5 e 5 mL), temperatura (125oC a 180 oC) e tempo de secagem (30 a 90mim). Os materiais produzidos foram submetidos a testes de secagens a diferentes condições de temperatura para a realização dos trabalhos de moldagem. Além dos processos de secagem, foram realizados ensaios de laboratório como Calorimetria Exploratória Diferencial (DSC), Termogravimetria (TG), Espectroscopia de Absorção na Região do Infravermelho (FTIR) e citotoxicidade e Microscopia Eletrônica de Varredura (MEV) e Espectroscopia de Energia Dispersivo (EDS), a fim de caracterizar e conhecer as características dos materiais produzidos em termos físicos,químicos e biológicos,e ter estes estudos como aliados do processo criativo. Novos ensaios foram realizados ensaios com renda de poliamida, poliéster e algodão com aplicação da borracha e pigmentos preto,azul e amarelo. Os resultados mostraram que a melhor quantidade de catalisador foi entre 3 a 5 mL. A temperatura de secagem 150oC. Por meio da analise de Espectroscopia de Energia Dispersiva (EDS) foi verificado que a diferença da amostra com os controles foi a presença de silício. Foram desenvolvidas seis pecas, dois vestidos, duas saias, um acessório de cabelo e um sapato. Foram trabalhadas algumas possibilidades de utilização da borracha de silicone em materiais têxteis, os resultados foram promissores
Titre en anglais
Study of application of a polymer fabric surfaces and development of new textures
Mots-clés en anglais
New textures
Rubber of silicone
Substrates textiles
Resumé en anglais
The present work has its aim to investigate on the adaptation and to make it possible the process of application of a polymer, commercially known as a silicone rubber, in the context of creating a new aesthetic concept and the will to bring to textiles a new texture or new conception of structure to substrates. Firstly we investigated how best to adapt this rubber and how it behaves in different textile surfaces. Assays were performed to evaluate the conditions of preparation of the silicone rubber, the volume of the catalyst to be used (0.75, 2.5 and 5 ml), temperature (125°C to 180°C) and drying time (30 to 90 mim). The materials produced were subjected to drying tests at different temperature conditions for carrying out the molding work. Above the drying process, laboratory tests were conducted as Scanning Electron Microscopy-SEM and Analysis by Energy Dispersive Spectroscopy (EDS) in order to characterize and understand the characteristics of the materials on physical, chemical and biological terms, and these studies have as allies of the creative process. New tests were performed tests with income of polyamide, polyester and cotton with application of rubber and black pigments, blue and yellow. The results showed that the optimal amount of catalyst was from 3 to 5 ml. The drying temperature of 150°C. Through spectral analysis Energy Dispersive (EDS) it was found that the difference of the sample with the controls was the presence of silicon. Six pieces were developed, two dresses, two skirts, a hair accessory and a shoe. It was reached possibilities making use of silicone rubber textile materials, the results were promising
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
andressa.pdf (2.53 Mbytes)
Date de Publication
2015-09-22
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.