Thèse de Doctorat
DOI
https://doi.org/10.11606/T.97.2010.tde-26092012-172415
Document
Auteur
Nom complet
Eliana Cursino
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2010
Directeur
Jury
Rodrigues Junior, Durval (Président)
Santos, Claudinei dos
Carvalho, Claudio Luiz
Neves, Marcelo Azevedo
Ribeiro, Sebastiao
Titre en portugais
Obtenção e caracterização de supercondutores de Bi2212 texturizados com introdução de centros artificiais de aprisionamento
Mots-clés en portugais
Centros artificiais de aprisionamento
Difratometria de raios X
Microscopia eletrônica de transmissão
Microscopia eletrônica de varredura
Supercondutividade
Resumé en portugais
O presente trabalho analisou as condições de texturização de amostras de Ag/Bi2212 (Bi2Sr2CaCu2O8+δ) na forma de pastilhas e de fitas, verificando-se a influência do tratamento térmico, atmosfera, adição de prata e adição de zircônia ou zirconato de cálcio. As adições de zircônia ou de zirconato de cálcio, com partículas de dimensões submicrométricas ou nanométricas (abaixo de 200nm), foram analisadas como possíveis geradores de centros de aprisionamento de fluxo magnético, assim como foi feita a análise de seus comportamentos nas propriedades intrínsecas da matriz supercondutora. A influência da atmosfera de tratamento térmico foi analisada de modo a alterar a concentração de oxigênio na fase supercondutora visando melhores resultados de temperatura crítica, sem depreciação das densidades de corrente crítica e dos campos de irreversibilidade, Birr. Foram analisadas as influências dos parâmetros de tratamento térmico, tais como temperatura máxima de reação, tempo nesta temperatura máxima, taxa de resfriamento do estado líquido ao estado sólido, e temperatura e tempo de recozimento após solidificação. Verificou-se a influência do resfriamento do forno sobre a texturização e a temperatura crítica. Quanto à dopagem com prata, foi verificada sua influência na texturização e interação com a zircônia. Foram realizadas caracterizações supercondutoras e microestruturais das amostras.
Titre en anglais
Production and characterization of textured Bi2212 superconductors with introduction of artificial pinning centers.
Mots-clés en anglais
Artificial pinning centers
Scanning electron microscopy
Superconductivity
Transmission electron microscopy
X-ray diffractometry
Resumé en anglais
The present work analyzed the texturing conditions of Ag/Bi2212 samples (Bi2Sr2CaCu2O8+δ) in the form of bulks and of tapes, verifying the influence of heat treatment, atmosphere, silver addition and addition of zirconia or calcium zirconate. The additions of zirconia or calcium zirconate, with particles of submicron or nanometric (below 200nm) dimensions, were analyzed as possible generators of magnetic flux pinning centers, as well as it was analyzed their behaviors on the intrinsic properties of the superconducting matrix. The influence of the heat treatment atmosphere was analyzed in order to change the oxygen concentration in the superconducting phase aiming better results of critical temperature, without depreciation of the critical current densities and of the irreversibility fields, Birr. The influences of the heat treatment parameters were analyzed, such as the reaction maximum temperature, soaking time at this maximum temperature, cooling rate from the liquid to the solid states, and annealing temperature and time after solidification. It was verified the influence of the furnace cooling rate on the texturing and critical temperatures. Concerning to the silver addition, it was verified its influence on the texturing and its interaction with the zirconia. Superconducting and microstructural characterizations of the samples were performed.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMT10003.pdf (9.09 Mbytes)
Date de Publication
2012-09-26
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.