Master's Dissertation
DOI
https://doi.org/10.11606/D.97.2016.tde-24072014-154227
Document
Author
Full name
Maria Gabriela Galvão Camarinha
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Lorena, 2014
Supervisor
Committee
Baptista, Carlos Antonio Reis Pereira (President)
Barboza, Miguel Justino Ribeiro
Torres, Marcelo Augusto Santos
Title in Portuguese
Avaliação do comportamento em fadiga do aço maraging 300 submetido a processo de soldagem a laser
Keywords in Portuguese
Aço Maraging
Fadiga
Soldagem a Laser
Abstract in Portuguese
Os aços maraging pertencem a uma classe de aços de ultra-alta-resistência que diferem da maioria dos aços pelo mecanismo de endurecimento. Enquanto nos aços convencionais o endurecimento é obtido por transformação martensítica, nos aços maraging o aumento das propriedades mecânicas é obtido pela precipitação de compostos intermetálicos em uma matriz martensítica de baixo teor de carbono, em temperaturas da ordem de 480°C. Para o presente trabalho, empregou-se um aço maraging 300 na forma de barras cilíndricas com diâmetro de 8mm e comprimento de 120mm, cedido na condição solubilizada pelo Departamento de Ciência e Tecnologia Aeroespacial (DCTA). Os corpos-de-prova foram soldados em cheio empregando-se um laser a fibra de 2kW e um dispositivo especialmente desenvolvido para solda orbital. As condições de envelhecimento foram inicialmente estudadas e a melhor combinação de resistência mecânica e ductilidade foi obtidas na condição de para 460°C por 3 horas, que foi então adotada para a caracterização do comportamento em fadiga. Os ensaios de fadiga foram realizados em uma máquina de flexão rotativa (R = -1), em níveis de tensão correspondentes à faixa de vida de 104 a 107 ciclos. Os corpos-de-prova soldados a laser foram submetidos a três condições de tratamento pós-soldagem: a) envelhecimento, b) solubilização + envelhecimento e c) homogeneização + solubilização + envelhecimento. Os resultados permitiram avaliar e comparar o efeito da solda a laser, seguida por tratamentos térmicos pós-soldagem, no comportamento em fadiga do aço maraging 300. Os tratamentos pós-soldagem não resultaram em diferença significativa na vida em fadiga do aço maraging 300, o fator determinante para a duração da vida em fadiga foi a quantidade de poros presente na superfície de fratura.
Title in English
Evaluation of the fatigue behavior of maraging 300 steel subjected to laser welding process
Keywords in English
Fatigue
Laser Beam Weld
Maraging Steel
Abstract in English
The maraging steels belong to a class of ultra-high-resistance steels that differ from most of steel for the hardening mechanism. While the conventional steel is obtained by hardening for martensitic transformation in maraging steel the increase of mechanical properties is obtained by the precipitation of intermetallic phases in a martensitic matrix of low carbon, at temperatures about 480°C. For the present study, we used a maraging 300 steel in form of cylindrical bars with a diameter of 8mm and length of 120mm, received as solution treated by the Department of Aerospace Science and Technology (DCTA). The test specimens were welded using a 2 kW fibre laser coupled to a special lathe in order to obtain an orbital weld line. The ageing contitions of the steel were initially investigated using base material samples. The best combination of hardness, tensile strength and ductility were achieved for 460°C for 3 hours , which was then chosen for the fatigue characterization..The fatigue tests were conducted in a rotating bending machine (R = -1). The stress levels were found for fatigue lives in the range of 104 to 107 cycles. The laser welded test pieces underwent three distinct post-weld heat treatments: a) ageing , b) solution + ageing and b) homogenization + solution + ageing .The results allowed assessing and comparing the effect of laser beam welding, followed by post-weld heat treatments, on the fatigue behavior of the maraging 300 steel. The post-weld heat treatments no results in significant difference in fatigue life of maraging 300 steel , the determinant factor for fatigue life was the amount of pores present in the fracture surface.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
EMD13006_O.pdf (6.18 Mbytes)
Publishing Date
2016-09-14
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.