Thèse de Doctorat
DOI
10.11606/T.97.2013.tde-24032015-152637
Document
Auteur
Nom complet
Mariane Martim Sobrosa Passos de Abreu
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2013
Directeur
Jury
Shigue, Carlos Yujiro (Président)
Cioffi, Maria Odila Hilário
Oliveira, Pedro Carlos de
Saron, Clodoaldo
Thim, Gilmar Patrocínio
Titre en portugais
Preparação e caracterização de compósitos híbridos de talco e resina epóxi-anidrido
Mots-clés en portugais
Cinética
Propriedades mecânicas
Resina epóxi
Talco
Resumé en portugais
Neste trabalho foi realizado o estudo térmico, cinético e dielétrico durante a cura de um compósito constituído de uma matriz de resina epóxi-anidrido e de talco como carga modificadora das características dielétricas e mecânicas da matriz polimérica. Foram analisadas também as propriedades dinâmicas mecânicas e morfológicas dos compósitos completamente curados. O interesse na investigação das características térmicas, cinéticas e dielétricas visou encontrar correlação entre essas características e as propriedades dinâmicas mecânicas finais dos compósitos. Foram estudados os compósitos com diferentes concentrações de carga, variando de 0 a 10% m/m, utilizando as técnicas de calorimetria exploratória diferencial (DSC), de análise dielétrica (DEA), análise termomecânica dinâmica (DMTA) e análise por microscopia eletrônica de varredura (MEV). Os resultados da análise DSC foram analisados por método isotérmico (modelo de Sourour-Kamal modificado) e por método dinâmico (modelo isoconversional). Os resultados da análise da cura dos compósitos mostraram que a concentração da carga retarda o processo de cura, conforme observado pela análise dielétrica; a temperatura de transição vítrea do compósito curado apresentou valores mínimos nas concentrações de 7 e 10%, enquanto que a análise térmica dinâmica previu que a energia de ativação aumenta com o grau de conversão. Os resultados da análise termomecânica dinâmica mostraram o aumento no módulo de armazenamento a 25ºC de 2,1 GPa (0% talco) a 3,3 GPa (10% talco), indicando haver o efeito reforçador do talco sobre a matriz polimérica. As micrografias dos compósitos foram um excelente recurso para estudar suas morfologias e se correlacionam com os resultados cinéticos e mecânicos.
Titre en anglais
Preparation and characterization of talc and epoxy-anhydride resin hybrid composites
Mots-clés en anglais
Epoxy resin
Kinetic
Mechanical properties
Talc
Resumé en anglais
In this work we performed the thermal, kinetics, dielectrical and morphological studies on the curing of a hybrid composite material composed of epoxy-anhydride matrix and talc as modifier agent of the dielectrical and mechanical properties of the polymer matrix. It also was studied the dynamic mechanical properties of the full-cured composite materials. This investigation aimed to correlate the thermal, kinetics, and dielectrical characteristics of the curing material with their final mechanical properties. Composite materials with different talc concentrations were studied in the range from 0% up to 10% w/w, employing the Differential Scanning Calorimetry (DSC), the Dielectric Analysis (DEA), Dynamic Mechanical Thermal Analysis (DMTA) and Microscopy Electron Scanning (SEM) techniques. The DSC experimental results were analyzed through the isothermal method (Modified Sourour-Kamal model) and the dynamic method (Isoconversional model). The cure analysis results of the composite specimens showed the talc acting as a cure retardant as observed from DEA results; the glass transition temperature of the full-cured composite materials showed minimum values at talc concentrations of 7 and 10%, while the dynamic thermal analysis predicted the activation energy is increasing with the conversion degree. The DMTA results exhibited the storage modulus at 25ºC increases from 2.1 GPa for the matrix without talc up to 3.3 GPa at 10% talc concentration composite, thus indicating the reinforcement role of the talc on the polymer matrix. The composites micrographs were an excellent resource for study their morphologies and for correlation of kinetics and mechanical results.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMT13006_C.pdf (6.19 Mbytes)
Date de Publication
2015-03-24
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.