Disertación de Maestría
DOI
https://doi.org/10.11606/D.97.2017.tde-20112017-165628
Documento
Autor
Nombre completo
Fabia Zampieri D'Antola de Mello
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2017
Director
Tribunal
Schneider, Sandra Giacomin (Presidente)
Afonso, Conrado Ramos Moreira
Rodrigues Junior, Durval
Vasconcellos, Luana Marotta Reis de
Título en portugués
Avaliação da biofuncionalidade dos implantes da liga Ti-35Nb-7Zr comparado aos implantes comerciais de Ti-Cp
Palabras clave en portugués
Análise Histológica
Biofuncionalidade
Citotoxicidade
Liga Ti-Nb-Zr
Torque de Remoção
Resumen en portugués
A Ti-35Nb-7Zr é uma liga Ti-ß desenvolvida pelo Grupo de Biomateriais da Escola de Engenharia de Lorena da Universidade de São Paulo, que demonstrou, em estudos anteriores, propriedades mecânicas favoráveis para ser usada como biomaterial, tais como, limite de resistência (~800 Mpa), resistência à corrosão e baixo módulo de elasticidade (33 GPa). Uma vez que o implante dentário traz melhores resultados no tocante à função mastigatória, fonação, conforto e estética, melhorando a qualidade de vida das pessoas, o presente estudo descreve a avaliação da biofuncionalidade dos implantes dentários da liga Ti-35Nb-7Zr comparados aos implantes comerciais de Ti-Cp da marca Titaniumfix. A biofuncionalidade foi avaliada por meio de testes in vitro e in vivo. A avaliação in vitro foi realizada com células mesenquimais indiferenciadas retiradas da medula óssea de fêmures de ratos, que foram cultivadas em meio de cultura osteogênico e posteriormente realizados os testes de citotoxicidade, quantificação de proteína total e avaliação da atividade da fosfatase alcalina. A avaliação in vivo compreendeu a realização de implantes de Ti-Cp Titaniumfix e da liga Ti-35Nb-7Zr em tíbias de coelhos para avaliação histológica, histomorfométrica por meio do cálculo da Fração da área óssea ocupada (BAFO) e aposição óssea, e de remoção ao torque com intuito de avaliar a osteointegração. Considerando os resultados obtidos nesta pesquisa, com relação aos testes in vitro, é possível concluir que a liga possui maior hidrofilicidade que o Ti-Cp; apresenta espraiamento celular similar ao Ti-Cp o que corrobora para o resultado de viabilidade celular classificando-a como não citotóxica. Nos testes de quantificação de proteína total e atividade da fosfatase alcalina a liga apresenta resultados similares ao Ti-Cp, favorecendo a ocorrência de diferenciação e proliferação das células osteoblásticas. Desta forma, pode-se concluir que a liga possui boa compatibilidade in vitro. Os resultados obtidos nas avaliações in vivo, por meio da fração de área óssea ocupada (BAFO), comprovam a semelhança entre a liga e o Ti-Cp pois tiveram o valor percentual de osso neoformado similar. A análise de fluorescência, após a administração dos marcadores tetraciclina e alizarina, mostra que a aposição óssea também foi semelhante entre a liga e o Ti-Cp nos períodos estudados. Com relação a força de interação avaliada pelo torque de remoção é possível afirmar que a liga apresenta osteointegração comparável aos implantes comerciais Ti-Cp. Esses resultados demonstraram que os implantes da liga Ti-35Nb-7Zr apresentaram biocompatibilidade e biofuncionalidade semelhantes ao dos implantes de Ti-Cp. Além de possuir um baixo módulo de elasticidade, a liga apresentou uma osteointegração bem similar ao Ti-Cp, reunindo características que demonstram seu potencial para ser usada como biomaterial intraósseo.
Título en inglés
Biofunctionality evaluation of a Ti-35Nb-7Zr implants compared to Ti-Cp implants
Palabras clave en inglés
Biofunctionality
Citotoxity
Histologic Evaluation
Removal Torque
Ti-Nb-Zr alloy
Resumen en inglés
Ti-35Nb-7Zr is a Ti-ß alloy developed by the Biomaterials Group of the Lorena School of Engineering of the University of São Paulo, which demonstrated, in previous studies, favorable mechanical properties to be used as biomaterial, such as resistance (~800 Mpa), corrosion resistance and low modulus of elasticity (33 GPa). Since the dental implant brings better results regarding masticatory function, phonation, comfort and aesthetics, improving the quality of life of the people, the present study describes the evaluation of the biofunctionality of the Ti-35Nb-7Zr ally dental implants compared to the Titaniumfix implants of Ti-Cp. The biofunctionality was evaluated by means of in vitro and in vivo tests. The in vitro evaluation was perfomed with undifferentiated mesenchymal cells removed from the bone marrow of rat femurs, which were cultured in osteogenic culture medium and subsequently perfomed cytotoxicity tests, total protein quantification and evaluation of alkaline phosphatase activity. The in vivo evaluation included the implantation of Ti-Cp Titaniumfix and Ti-35Nb-7Zr alloy implants in rabbit tibiae for histological, histomorphometric evaluation by calculating the Bone Area Fractional Occupied (BAFO) and bone apposition, and torque removal in order to evaluate the osseointegration. Considering the results obtained in this research, related to in vitro tests, it is possible to conclude that the alloy has a higher hydrophilicity than Ti-Cp; Show cellular spreading similar to Ti-Cp, which corroborates the result of cell viability classifying it as non-cytotoxic. In the tests of total protein quantification and alkaline phosphatase activity the alloy presents results similar to Ti-Cp, favoring the occurrence of differentiation and proliferation of osteoblastic cells. In this way, it can be concluded that the alloy has good compatiblity in vitro. The results obtained in the in vivo evaluations, through the BAFO, confirm the similarity between the alloy and Ti-Cp, since they had the percentage value similar to neoformed bone. Fluorescence analysis, after administration of the tetracycline and alisarin markers, show that bone apposition was also similar between the alloy and Ti-Cp in the periods studied. Regarding the interaction force evaluated by the removal torque, it is possible to affirm that the alloy show osseointegration comparable to commercial Ti-Cp implants. These results demonstrated that Ti-35Nb-7Zr alloy implants had similar biocompatibility and biofunctionality to Ti-Cp implants. In addition to having a low modulus of elasticity, the alloy presented an osseointegration very similar to Ti-Cp, bringing together characteristics that demonstrate its potential to be used as an intraosseous biomaterial.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD17001_C.pdf (11.13 Mbytes)
Fecha de Publicación
2017-11-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.