Thèse de Doctorat
DOI
https://doi.org/10.11606/T.97.2019.tde-12072019-114000
Document
Auteur
Nom complet
José Mauro Moraes Junior
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2018
Directeur
Jury
Nunes, Carlos Angelo (Président)
Baptista, Carlos Antonio Reis Pereira
Bortolozo, Ausdinir Danilo
Hein, Luis Rogério de Oliveira
Suzuki, Paulo Atsushi
Titre en portugais
Processamento e caracterizações de ligas Al-Ti-V-Zr-Nb e Al-Ti-V-Cr-Nb (ligas com elementos multiprincipais) para aplicação aeroespacial
Mots-clés en portugais
Aplicação aeroespacial
Liga refratária
Ligas com elementos multiprincipais
Ligas de alta entropia
Resumé en portugais
Foram estudadas MPEAs com diferentes composições químicas, das famílias Al-Ti-V-Zr-Nb e Al-Ti-V-Cr-Nb, visando desenvolver uma liga com propriedades interessantes para aplicação aeroespacial. As ligas foram produzidas em um forno a arco laboratorial, sob atmosfera de argônio. As primeiras ligas caracterizadas foram da composição equimolar de ambas famílias, mas não apresentaram microestrutura com solução sólida monofásica depois do tratamento térmico de homogeneização (1200°C/24h). Após ajustes na composição química duas ligas foram consideradas promissoras na caracterização microestrutural, após homogeneização, BZr7 e BCr8. Para avaliar a estabilidade microestrutural ambas foram expostas a alta temperatura por longo período de tempo (700ºC/168h), e ambas apresentaram pequena fração de segunda fase após esta exposição térmica. A dureza da BZr7 e da BCr8, após exposição térmica, foi de 3,46 e 4,91 GPa, respectivamente. Ambas foram laminadas a 1000 °C, encapsuladas em tubo de aço inoxidável austenítico para evitar oxidação, mas apenas a BZr7 apresentou conformabilidade, sendo a BCr8 não utilizada nos testes subsequentes. A BZr7 exposta termicamente apresentou, na temperatura ambiente, tensão limite de escoamento, em compressão, de 1250 MPa. A tensão limite de escoamento se manteve alta em temperaturas elevadas, sendo 1080, 720 e 690 MPa nas temperaturas de 600, 700 e 800 °C, respectivamente. A massa específica é de 6,34 g/cm3, que originou tensões de escoamento específicas de 197,2 kPa.m3/kg na temperatura ambiente, e 170,3, 113,6 e 108,8 kPa.m3/kg nas temperaturas de 600, 700 e 800 °C, respectivamente, resultados bem melhores que das três ligas convencionais usadas como referência neste trabalho, Ti6Al4V, Tiβ21s e Inconel 625. Além de boa resistência em compressão a liga apresentou boa ductilidade na temperatura ambiente (ε = 38%). Apenas a MPEA refratária AlNbTiVZr0,5, publicada por Stepanov et al. (2015d) e Yurchenko et al. (2017), apresentou combinação simultânea de alta resistência e boa ductilidade acima da liga BZr7 na temperatura ambiente. Apesar dos bons resultados de propriedades mecânicas, a liga apresentou baixa resistência à oxidação, tornando necessário revestimento para aplicações a elevadas temperaturas.
Titre en anglais
Processing and characterization of Al-Ti-V-Zr-Nb and Al-Ti-V-Cr-Nb alloys (multi-principal elements alloys) for aerospace application
Mots-clés en anglais
Aerospace application
High entropy alloy
Multi-principal elements alloys
Refractory alloy
Resumé en anglais
MPEAs with different chemical compositions, based in Al-Ti-V-Zr-Nb and Al-Ti-V-Cr-Nb families, were explored, aiming to develop an alloy with interesting properties for aerospace application. The alloys were produced in a laboratory arc furnace, with argon atmosphere. The equimolar composition of both families were the first characterized alloys, but did not exhibit single-phase solid solution microstructure after homogenization heat treatment (1200 °C/24h). After adjustments in the chemical composition two alloys were considered promising in the microstructural characterization after homogenization, BZr7 and BCr8. To evaluate the microstructural stability both alloys were exposed to high temperature for long period of time (700ºC/168h), and both presented small fraction of second phase after this exposure heat treatment. The microhardness of BZr7 and BCr8 alloys, after thermal exposure, was 3.46 and 4.91 GPa, respectively. Both were rolled at 1000 ° C, after encapsulation in austenitic stainless steel tube to avoid oxidation, but only BZr7 showed formability, than BCr8 was not considered for subsequent tests. The BZr7 alloy, after thermal exposure, exhibited 1250 MPa of yield stress at ambient temperature. The yield stress remained high at elevated temperatures, being 1080, 720 and 690 MPa at temperatures of 600, 700 and 800 ° C, respectively. BZr7 density is 6.34 g/cm3, resulting in a specific yield stress of 197.2 kPa.m3/kg, at room temperature, and 170.3, 113.6 and 108.8 kPa.m3/kg at temperatures 600, 700 and 800 °C, respectively, better results than the three conventional alloys tested in this work, Ti6Al4V, Tiβ21s and Inconel 625. In addition to good compressive yield stress, the alloy showed good ductility at room temperature (ε = 38%). Only the refractory MPEA AlNbTiVZr0.5, published by Stepanov et al. (2015d) and Yurchenko et al. (2017), showed a simultaneous combination of high yield stress and good ductility, above the BZr7 alloy, at room temperature. Despite the good results of mechanical properties, the BZr7 alloy showed low oxidation resistance, so coating is required for high temperature applications.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMT18001_ON.pdf (5.44 Mbytes)
EMT18001_RN.pdf (230.63 Kbytes)
Date de Publication
2019-07-12
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.