Master's Dissertation
DOI
https://doi.org/10.11606/D.97.2015.tde-05082015-160801
Document
Author
Full name
Davison Ramos de Almeida Junior
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Lorena, 2015
Supervisor
Committee
Sandim, Hugo Ricardo Zschommler (President)
Eleno, Luiz Tadeu Fernandes
Fonseca, Gláucio Soares da
Rios, Paulo Rangel
Title in Portuguese
Crescimento de grão num fio de ferro comercialmente puro trefilado a frio
Keywords in Portuguese
Crescimento anormal de grão
Ferro comercialmente puro
Molhamento no estado sólido
Recristalização secundária
Trefilação a frio
Abstract in Portuguese
Este trabalho tem como objetivo caracterizar as mudanças microestruturais durante o recozimento isotérmico de um fio de ferro trefilado a frio e de pureza comercial com ênfase no crescimento de grão. Os recozimentos foram realizados no intervalo de 823-1173 K por diversos tempos. As informações estatísticas do tamanho de grão foram obtidas por meio do método dos interceptos lineares. O mapeamento das orientações foi obtido por meio de difração de elétrons retroespalhados (EBSD). O material apresenta uma microestrutura ferrítica e totalmente recristalizada a partir de 873 K. Foram encontrados indícios de crescimento normal de grão a partir de 1023 K, porém este crescimento não evoluiu consideravelmente ao longo do tempo de tratamento. Os resultados obtidos a partir do método dos interceptos lineares demonstram que a distribuição de tamanho de grão segue uma curva próxima à log-normal. Nas amostras recozidas a partir de 1123 K, verificou-se a ocorrência de crescimento anormal de grão. O crescimento anormal de alguns grãos inicia-se na região central do fio, estendendo-se até uma região próxima à superfície do fio. Algumas modificações na dimensão da amostra e na atmosfera de recozimento foram realizadas a fim de se estudar a interação destas variáveis no desenvolvimento dos grãos anormais. Foram identificados indícios morfológicos de que o mecanismo para ocorrência de crescimento anormal foi o molhamento de contornos no estado sólido (solid-state wetting) que depois foram confirmados pelas análises de micro e mesotexturas. A análise de microtextura também revela que o material apresenta duas componentes preferenciais, as fibras <001> || DT e <111> || DT, onde DT é a direção axial de trefilação. A primeira orientação é a mais intensa, sendo que seu fortalecimento parece ser impulsionado pelo crescimento anormal de grão. A segunda é menos intensa e parece estar relacionada com as orientações dos grãos oriundos da recristalização primária. Aspectos teóricos e analíticos sobre o crescimento de grão são apresentados e associados aos resultados experimentais e à literatura.
Title in English
Grain growth in commercially-pure cold-drawn wires of iron
Keywords in English
Abnormal grain growth
Cold-drawing
Commercially-pure iron
Secondary recrystallization
Solid-state wetting
Abstract in English
This Dissertation aims follow the microstructural changes occurring during isothermal annealing of commercially-pure cold-drawn iron wire, with emphasys on grain growth phenomena. The grain size data were obtained by means of the linear intercept method. The orientations scanning were done by means of electron backscatter diffraction patterns (EBSD). Isothermal annealing was performed within the temperature range 823 - 1173 K for several times. The material displays full recrystallization at temperatures above 873 K. Normal grain growth was observed above 1023 K, although this growth did not evolve through longer annealing times. The results of the linear intercept method show the grain size distribution has a log-normal shape. For samples annealed above 1123 K, abnormal grain growth occurs. The first signs of secondary recrystallization appear close to the center of the wire, growing towards the surface. Changes in the wire diameter and annealing atmosphere were performed to assess the effect of these variables on abnormal grain growth. Results point out that abnormal grain growth is driven by solid-state wetting. These morphological observations were also confirmed by micro and mesotexture analyses. The microtexture also shows the presence of two major fiber texture components <001> || WD and <111> || WD, were WD is the axial wire-drawn direction. The first one is the most intense and its strengthening seems to be related with abnormal grain growth. The second one is weaker and it seems to be most related with small primary recrystallized grains. Theoretical and analytical features about grain growth are presented and discussed in light of literature and experimental results.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
EMD15006_C.pdf (8.17 Mbytes)
Publishing Date
2015-08-05
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2024. All rights reserved.